Open hole and post-impact compression fatigue of stitched and unstitched carbon/epoxy composites

The performance is studied of a stitched uniweave fabric composite and that of a toughened tape composite. The effects of stitching on compression fatigue life are addressed. Post impact compression fatigue and open hole fatigue tests were run on an AS4/3501-6 uniweave with stitching and a toughened IM7/8551-7 tape without stitching. Stitching was found to increase the thickness and consequently the weight of the composite material. The two materials were compared on an equal carbon content basis as well as on an equal weight basis. The excess thickness in the stitched uniweave composite was responsible for the lower fatigue life, on an equal carbon basis, compared to the toughened resin tape composite. Comparison of fatigue lives on an equal carbon content basis indicated that puncture or crimp type damage from stitching has very little effect on compression failure. Post impact fatigue test showed that although the damage area in the stitched uniweave composite was twice that of the toughened tape composite, the fatigue lives of the stitched composite were significantly longer than those of the toughened composite. Thus, it appears that the increase in thickness from stitching is much more of a penalty than crimped fibers or puncture type damage from stitching.

Portanova, M. A.↗

NASA NTRS1990

Summary of a study to determine low-velocity impact damage and residual tension strength for a thick graphite/epoxy motor case

Impacters of various shapes and masses were dropped from various heights onto 36 mm (1.4 in.) thick graphite/epoxy cylinders, which represented filament wound cases (FWC) for the booster motors of the Space Shuttle. Insert solid propellant was cast into some of the cylinders. The cylinders were impacted numerous times around the circumference and then cut into 51 mm (2.0 in.) wide tension specimens, each containing an impact site. Four indenters were used: a sharp corner, two hemispheres, and a bolt-like rod. The diameters of the hemispheres were 12.7 mm mm (0.5 in.) and 25.4 mm (1.0 in.), and the diameter of the rod was 6.3 mm (0.25 in.). Impacts with the rod were simulated by pressing the rod against the face of specimens. For the hemispheres, the damage initiated beneath the surface at a critical contact pressure and was not visible on the surface until an even larger pressure was exceeded. The damage consisted of matrix cracking and broken fiber. The rod an corner made visible surface damage in all tests. For the hemispheres, the tension strength was reduced considerably before the damage was visible on the surface, 30 percent for the 25.4 mm (1.0 in.) diameter hemisphere and 10 percent for the 12.7 mm (0.5 in.) diameter hemisphere. Analytical methods were used to predict the damage and residual tension strength. A factor of safety to account for nonvisible damage was determined.

Poe, C. C., Jr.↗

NASA NTRS1990

An evaluation of the pressure proof test concept for thin sheet 2024-T3

The concept of pressure proof testing of fuselage structures with fatigue cracks to insure structural integrity was evaluated from a fracture mechanics viewpoint. A generic analytical and experimental investigation was conducted on uniaxially loaded flat panels with crack configurations and stress levels typical of longitudinal lap splice joints in commercial transport aircraft fuselages. The results revealed that the remaining fatigue life after a proof test was longer than that without the proof test because of crack growth retardation due to increased crack closure. However, based on a crack length that is slightly less than the critical value at the maximum proof test stress, the minimum assured life or proof test interval must be no more than 550 pressure cycles for a 1.33 proof factor and 1530 pressure cycles for a 1.5 proof factor to prevent in-flight failures.

Dawicke, D. S.↗

NASA NTRS1990

Relevance of impacter shape to nonvisible damage and residual tensile strength of a thick graphite/epoxy laminate

A study was made to determine the relevance of impacter shape to nonvisible damage and tensile residual strength of a 36 mm (1.4 in.) thick graphite/epoxy motor case. The shapes of the impacters were as follows: 12.7 mm (0.5 in.) and 25.4 mm (1.0 in.) diameter hemispheres, a sharp corner, and a 6.3 mm (0.25 in.) diameter bolt-like rod. The investigation revealed that damage initiated when the contact pressure exceeded a critical level. However, the damage was not visible on the surface until an even higher pressure was exceeded. The damage on the surface consisted of a crater shaped like the impacter, and the damage below the surface consisted of broken fibers. The impact energy to initiate damage or cause visible damage on the surface increased approximately with impacter diameter to the third power. The reduction in strength for nonvisible damage increased with increasing diameter, 9 and 30 percent for the 12.7 mm (0.5 in.) and 25.4 mm (1.0 in.) diameter hemispheres, respectively. The corner impacter made visible damage on the surface for even the smallest impact energy. The rod impacter acted like a punch and sliced through the composite. Even so, the critical level of pressure to initiate damage was the same for the rod and hemispherical impacters. Factors of safety for nonvisible damage increased with increasing kinetic energy of impact. The effects of impacter shape on impact force, damage size, damage visibility, and residual tensile strength were predicted quite well assuming Hertzian contact and using maximum stress criteria and a surface crack analysis.

Poe, C. C., Jr.↗

NASA NTRS1990

Summary of a study to determine low-velocity impact damage and residual tension strength for a thick graphite/epoxy motor case

Impacters of various shapes and masses were dropped from various heights onto 36 mm (1.4 in.) thick graphite/epoxy cylinders, which represented filament wound cases (FWC) for the booster motors of the Space Shuttle. Insert solid propellant was cast into some of the cylinders. The cylinders were impacted numerous times around the circumference and then cut into 51 mm (2.0 in.) wide tension specimens, each containing an impact site. Four indenters were used: a sharp corner, two hemispheres, and a bolt-like rod. The diameters of the hemispheres were 12.7 mm (0.5 in.) and 25.4 mm (1.0 in.), and the diameter of the rod was 6.3 mm (0.25 in.). Impacts with the rod were simulated by pressing the rod against the face of specimens. For the hemispheres, the damage initiated beneath the surface at a critical contact pressure and was not visible on the surface until an even larger pressure was exceeded. The damage consisted of matrix cracking and broken fiber. The rod and corner made visible surface damage in all tests. For the hemispheres, the tension strength was reduced considerably before the damage was visible on the surface, 30 percent for the 25.4 mm (1.0 in.) diameter hemisphere and 10 percent for the 12.7 mm (0.5 in.) diameter hemisphere. Analytical methods were used to predict the damage and residual tension strength. A factor of safety to account for nonvisible damage was determined.

Poe, C. C., Jr.↗

NASA NTRS1990

Proof test and fatigue crack growth modeling on 2024-T3 aluminum alloy

Pressure proof testing of aircraft fuselage structures has been suggested as a means of screening critical crack sizes and of extending their useful life. The objective of this paper is to study the proof-test concept and to model the crack-growth process on a ductile material. Simulated proof and operational fatigue life tests have been conducted on cracked panels made of 2024-T3 aluminum alloy sheet material. A fatigue crack-closure model was modified to simulate the proof test and operational fatigue cycling. Using crack-growth rate and resistance-curve data, the model was able to predict crack growth during and after the proof load. These tests and analyses indicate that the proof test increases fatigue life; but the beneficial life, after a 1.33 or 1.5 proof, was less than a few hundred cycles.

Newman, J. C., Jr.↗

NASA NTRS1988

Strain intensity factor approach for predicting the strength of continuously reinforced metal matrix composites

A method was previously developed to predict the fracture toughness (stress intensity factor at failure) of composites in terms of the elastic constants and the tensile failing strain of the fibers. The method was applied to boron/aluminum composites made with various proportions of 0 to + or - 45 deg plies. Predicted values of fracture toughness were in gross error because widespread yielding of the aluminum matrix made the compliance very nonlinear. An alternate method was developed to predict the strain intensity factor at failure rather than the stress intensity factor because the singular strain field was not affected by yielding as much as the stress field. Strengths of specimens containing crack-like slits were calculated from predicted failing strains using uniaxial stress-strain curves. Predicted strengths were in good agreement with experimental values, even for the very nonlinear laminates that contained only + or - 45 deg plies. This approach should be valid for other metal matrix composites that have continuous fibers.

Poe, C. C., Jr.↗

NASA NTRS1988

Surface crack analysis applied to impact damage in a thick graphite-epoxy composite

The residual tensile strength of a thick graphite/epoxy composite with impact damage was predicted using surface crack analysis. The damage was localized to a region directly beneath the impact site and extended only part way through the laminate. The damaged region contained broken fibers, and the locus of breaks in each layer resembled a crack perpendicular to the direction of the fibers. In some cases, the impacts broke fibers without making a visible crater. The impact damage was represented as a semi-elliptical surface crack with length and depth equal to that of the impact damage. The maximum length and depth of the damage were predicted with a stress analysis and a maximum shear stress criterion. The predictions and measurements of strength were in good agreement.

Poe, C. C., Jr.↗

NASA NTRS1988

Simulated impact damage in a thick graphite/epoxy laminate using spherical indenters

A study was made to determine the extent of fiber damage caused by low-velocity impact of spherical impactors to a very thick graphite/epoxy laminate. The laminate was cut from a filament wound case being developed for the Space Shuttle solid rocket motors. The case was wound using a wet process with AS4W graphite fiber and HBRF-55A epoxy. Impacts were simulated under quasi-static conditions by pressing hemispherically shaped indenters against the laminate at different locations. The contact force and indenter diameter were varied from location to location. The forces were chosen for each indenter diameter to produce contact pressures below and above that required to initiate damage. After the forces were applied, the laminate was cut into smaller pieces so that each piece contained a test site. The pieces were then deplied and the individual plies examined to determine the extent of fiber damage. Broken fibers were found in the outer layers directly beneath the contact site. The locus of broken fibers in each layer resembled a crack normal to the direction of the fibers. The maximum length and depth of the cracks increased with increasing contact pressure and indenter diameter. The internal stresses in the laminate were calculated using Hertz's law and Love's solution for pressure applied on part of the boundary of a semi-infinite body. The maximum length and depth of the cracks were predicted using a maximum shear stress criterion. Predictions and measurements were in good agreement.

Poe, C. C., Jr.↗

NASA NTRS1988

Simulated impact damage in a thick graphite/epoxy laminate using spherical indenters

The extent of fiber damage due to low-velocity impacts was determined for very thick graphite/epoxy laminates. The impacts were simulated by pressing spherical indenters against the laminates. After the forces were applied, the laminate was cut into smaller pieces so that each piece contained a test site. Then the pieces were deplied and the individual plies were examined to determine the extent of fiber damage. Broken fibers were found in the outer layers directly beneath the contact site. The locus of broken fibers resembled cracks. The cracks were more or less oriented in the direction of the fibers in the contiguous layers. The maximum length and depth of the cracks increased with increasing contact pressure and indenter diameter. The length and depth of the cracks were also predicted using maximum compression and shear stress criteria. The internal stresses were calculated using Hertz's law and Love's solution for pressure applied on part of the boundary of a semi-infinite body. The predictions and measurements were in good agreement.

Poe, C. C., Jr.↗

NASA NTRS1987

Strength of a thick graphite/epoxy rocket motor case after impact by a blunt object

The National Aeronautics and Space Administration is developing graphite/epoxy filament-wound cases (FWC) for the solid rocket motors of the Space Shuttle. The membrane region is about 36 mm thick. A study was made to determine the reduction in strength of the FWC due to accidental damage caused by low-velocity impacts. Two 76.2 cm diameter by 30.5 cm long cylinders were impacted every 5 cm of circumference with 1.27 cm radius impacters of various mass. The impacters represented tools and equipment dropped from various heights. One cylinder was empty and the other was filled with inert propellant. Five cm wide test specimens were cut from the cylinder. Each was centered on an impact sight. The specimens were X-rayed and loaded to failure in uniaxial tension. The strengths and depths of impact damage were analyzed in terms of maximum impact force. Rigid body mechanics and the Hertz law were used to derive an equation for impact force in terms of kinetic energy and the masses of the impacter and target. The depth of damage was predicted in terms of impact force using Love's solution of pressure applied on part of the boundary of a semi-infinite body.

Poe, C. C., Jr.↗

NASA NTRS1987

A parametric study of fracture toughness of fibrous composite materials

Impacts to fibrous composite laminates by objects with low velocities can break fibers giving crack-like damage. The damage may not extend completely through a thick laminate. The tension strength of these damage laminates is reduced much like that of cracked metals. The fracture toughness depends on fiber and matrix properties, fiber orientations, and stacking sequence. Accordingly, a parametric study was made to determine how fiber and matrix properties and fiber orientations affect fracture toughness and notch sensitivity. The values of fracture toughness were predicted from the elastic constants of the laminate and the failing strain of the fibers using a general fracture toughness parameter developed previously. For a variety of laminates, values of fracture toughness from tests of center-cracked specimens and values of residual strength from tests of thick laminates with surface cracks were compared to the predictions to give credibility to the study. In contrast to the usual behavior of metals, it is shown that both ultimate tensile strength and fracture toughness of composites can be increased without increasing notch sensitivity.

Poe, C. C., Jr.↗

NASA NTRS1987

A parametric study of fracture toughness of fibrous composite materials

Poe, C. C., Jr.↗

NASA NTRS1986

Tension strength of a thick graphite/epoxy laminate after impact by a 1/2-in. radius impactor

NASA is developing graphite/epoxy filament-wound cases for solid rocket motors of the space shuttle. They are wet-wound with AS4W graphite fiber and HBRF-55A epoxy. The membrane region is about 1.4 inches thick. Two 30-inch-diameter by 12-inch-long cylinders were impacted every two inches of circumference with 1/2-inch radius impactors that were dropped from various heights. One cylinder was empty and the other was filled with inert propellant. Two-inch-wide test specimens were cut from the cylinders. Each was centered on an impact site. The specimens were x-rayed and loaded to failure in uniaxial tension. Rigid body mechanics and the Hertz law were used to predict impact force, local deformations, contact diameters, and contact pressures. The depth of impact damage was predicted using Love's solution for pressure applied on part of the boundary of a semi-infinite body. The predictions were reasonably good. The strengths of the impacted specimens were reduced by as much as 37 percent without visible surface damage. Even the radiographs did not reveal the nonvisible damage.

Poe, C. C., Jr.↗

NASA NTRS1986

Hidden impact damage in thick composites

NASA is developing light-weight graphite/epoxy filament-wound cases (FWC) for the solid rocket motors of the Space Shuttle. The 12-foot-diameter FWC's are about 1.4 inches or more thick. Tests were conducted to determine the tension strength of an FWC after low-velocity impact. Impactors of various kinetic energies, masses, and shapes were used. The conditions that give minimum visual evidence of damage were emphasized. The capability to characterize impact damage with radiography and ultrasonic attenuation was also evaluated. After impact, the specimens were loaded uniaxially in tension to determine residual strengths.

Poe, C. C., Jr.↗

NASA NTRS1985

A fracture mechanics analysis of impact damage in a thick composite laminate

Graphite/epoxy filament-wound cases (FWC) for the solid rocket motors of the space shuttle are being made by NASA. The FWC cases are wound with AS4W graphite fiber impregnated with an epoxy resin and are about 1.4 inches or more thick. Graphite-epoxy composite laminates, unlike metals, can be damaged easily by low velocity impacts of objects like dropped tools. The residual tension strength of the FWC laminate, after impact, is being studied at Langley Research Center. The conditions that give minimum visual evidence of damage are being emphasized. A fracture mechanics analysis was developed to predict the residual strength, after impact, using radiographs to measure the size of the damage and an equivalent surface crack to represent the damage.

Poe, C. C., Jr.↗

NASA NTRS1985

The fracture behavior of filament wound cylinders with surface flaws

The behavior of tensile coupons with surface notches of various semielliptical shapes has been evaluated for specimens obtained from a thick filament wound graphite/epoxy cylinder. Specimens with very shallow notches were observed to be notch insensitive and the unnotched strength from these specimens was determined to be 54.97 Ksi with an associated failure strain of 1.328 percent. Specimens with deeper notches were sensitive to notch depth and notch aspect ratio. Isotropic linear elastic fracture mechanics with an estimated fracture toughness of 27.2 Ksi-in.-to the 1/2 correctly predicted the influence of notch depth, aspect ratio and specimen finite width.

Harris, C. E.↗

NASA NTRS1984

Fracture toughness of fibrous composite materials

Laminates with various proportions of 0 deg, 45 deg, and 90 deg plies were fabricated from T300/5208 and T300/BP-907 graphite/epoxy prepreg tape material. The fracture toughness of each laminate orientation or lay-up was determined by testing center-cracked specimens, and it was also predicted with the general fracture-toughness parameter. The predictions were good except when crack-tip splitting was large, at which time the toughness and strengths tended to be underpredicted. By using predictions, a parametric study was also made of factors that influence fracture toughness. Fiber and matrix properties as well as lay-up were investigated. Without crack-tip splitting, fracture toughness increases in proportion to fiber strength and fiber volume fraction, increases linearly with E(22)/E(11), is largest when the modulus for non-0 deg fibers is greater than that of 0 deg fibers, and is smallest for 0(m)/90(p)(s) lay-ups. (The E(11) and E(22) are Young's moduli of the lamina parallel to and normal to the direction of the fibers, respectively). For a given proportion of 0 deg plies, the most notch-sensitive lay-ups are 0(m)/90(p)(s) and the least sensitive are 0(m)/45(n)(s) and alpha(s). Notch sensitivity increases with the proportion of 0 deg plies and decreases with alpha. Strong, tough matrix materials, which inhibit crack-tip splitting, generally lead to minimum fracture toughness.

Poe, C. C., Jr.↗