DOE OSTI2024

UHTC-TPMS Heat Exchangers for Concentrating Solar Power Applications with Thermal Energy Storage in Molten Chlorides

Concentrating solar power (CSP) plants convert energy from sunlight into electricity. Generally, a heliostat field is used to reflect sunlight and concentrate it onto a receiver, which heats the receiver and/or the media flowing through it. A flow loop transports the media through the system to a heat exchanger before returning the media back to the receiver to be reheated. The heat extracted by the heat exchanger is then converted into electricity using a conventional heat engine.

14 SOLAR ENERGY↗
DOE OSTI2024

High Temperature Mechanical Behavior of Refractory Alloys with Digital Image Correlation

Gas turbine efficiency is typically limited by the maximum allowable temperature for components at the inlet side and in the hot gas flow. Refractory alloys and SiC/SiC ceramic-matrix composites (CMCs) are promising candidates for advancing operating temperatures beyond those of Ni-based alloys (>1200 °C). Refractory alloys are more suitable than SiC/SiC CMCs for dynamic components, due to the latter's low toughness and ductility. However, it is well known that refractory alloys suffer from poor oxidation behavior under service lifetimes and conditions, leading to embrittlement concerns. The ARPA-E ULTIMATE program has set out to combine new alloys with advanced coatings to mitigate oxidation/embrittlement effects, while increasing the mechanical performance benefits of refractory materials. Low oxygen (inert gas) or vacuum systems are needed to assess high temperature mechanical performance of developed alloys. To investigate the environmental sensitivity of candidate alloys and develop high temperature testing capabilities, four argon tensile frames were upgraded as well as a single vacuum system at Oak Ridge National Laboratory. Digital image correlation was incorporated into the vacuum frame allowing for surface strain determination and refined insight into thermomechanical response. Creep testing was performed at 1300 °C on two alloys, C-103 and MHC in vacuum and high purity argon environments. The Mo-based alloy showed less sensitivity to oxygen, indicating that testing in well-controlled argon environments may be suitable. The C-103 alloy demonstrated a stronger sensitivity to oxygen in the well-controlled argon environment, illustrating the need for the developed vacuum testing capabilities. “Small” 25 mm and “large” 76 mm MHC specimens showed comparable results in terms of strain rate during creep testing and ultimate tensile strength during tensile testing, suggesting the viability of smaller geometries that use less material of advanced developmental alloys.

Bell, Sam↗
DOE OSTI2024

Evaluation of the Mechanical Properties of Cast and Wrought CF8C-Plus Relevant to ASME Code Case Qualification

The mechanical behavior of a cast form of an advanced austenitic stainless steel, CF8C-Plus, is compared with that of its wrought equivalent in terms of both tensile and creep-rupture properties and estimated allowable stress values for pressurized service at temperatures up to about 850°C. A traditional Larson-Miller parametric model is used to analyze the creep-rupture data and to predict long-term lifetimes for comparison of the two alloy types. The cast CF8C-Plus exhibited lower yield and tensile strengths, but higher creep strength compared to its wrought counterpart. Two welding methods, shielded-metal-arc welding (SMAW) and gas-metal-arc welding, met the weld qualification acceptance criteria in ASME BPVC Section IX for the cast CF8C-Plus. However, for the wrought CF8C-Plus, while SMAW and gas-tungsten-arc welding passed the tensile acceptance criteria, they failed the side bend tests due to lack of fusion or weld metal discontinuities.

Chen, Xiang↗
DOE OSTI2024

Summary of Structural Alloy Compatibility in Supercritical CO2 at 450°-800°C

Supercritical CO2 (sCO2) is of interest as a working fluid for several concepts including the direct- fired Allam cycle as a low-emission fossil energy power cycle. Over the past 10 years, laboratory exposures at 300 bar sCO2 have found reasonably good compatibility for Ni-based alloys at <800°C, including an assessment of the sCO2 impact on room temperature mechanical properties after 750°C exposures. However, initial screening tests at 1 and 20 bar CO2 at 900°-1100°C showed poor compatibility for Ni-based alloys. In an open cycle, the introduction of 1%O2 and 0.1- 0.25%H2O impurities at 300 bar increased the reaction rates ≥2X at 750°C. At lower temperatures, steels are susceptible to C ingress and embrittlement. Creep-strength enhanced ferritic steels may be limited to <550°C and conventional stainless steels to <600°C. Two strategies to increase those temperatures are higher Ni and Cr alloying additions and Al- or Cr-rich coatings. Alloy 709 (Fe- 20Cr-25Ni) shows some promising results at 650°C in sCO2 but reaction rates were accelerated with the addition of O2 and H2O impurities. Pack aluminized and chromized Gr.91 (Fe-9Cr-1Mo) and type 316H stainless steel show some promise at 600°-650°C but further coating optimization is needed.

Pint, Bruce↗
DOE OSTI2024

Assessing the Impact of Molten Halide Salts on Creep of Structural Alloys at 650°-750°C

There is a critical lack of data on the mechanical behavior of candidate structural materials for advanced nuclear reactors under molten halide salt environments. Limited legacy data from the molten salt reactor experiment (MSRE) program showed a significant reduction in creep rupture strength of a Ni-base alloy in molten fluoride salt. With ongoing efforts to commercialize different molten salt reactor concepts, the industry can considerably benefit from quantitative information on the impact of molten halide salts on the engineering properties such as creep and fatigue strength of materials of interest. The present work aims to assess the role of molten salt corrosion on the creep behavior of three alloys 316H, 617 and 282 at 650-816 °C. Creep tests were conducted in fluoride (FLiNaK) and chloride (NaCl-MgCl2) salts. Initial results from the ongoing testing will be presented which suggest that the molten salt environment caused a 25-50% reduction in creep rupture lifetime compared to air exposures. Physics-based corrosion and creep models were employed to gain some insights into the potential degradation mechanisms.

Pillai, Rishi↗
DOE OSTI2024

Interface stability of ultrasonic additively manufactured Zircaloy-4 during hydrothermal corrosion

Simulated pressurized water reactor conditions (330 °C, 15.6 MPa, ~20 ppb oxygen) without irradiation were used to investigate the hydrothermal corrosion behavior of ultrasonic additively manufactured Zircaloy-4 up to 1000 h. X-ray computed tomography allowed for visualization of defects from processing and their progression after corrosion experiments. The specimens were found to have clear variability in the mass change data, compared to typical wrought Zircaloy-4 specimens. The variation in the mass change after exposure was attributed to weld defects connected to the specimen surface which allowed ingress of oxidant into the samples. Defects visualized by computed tomography were found via metallography and characterized. In conclusion, ultrasonic additively manufactured Zircaloy-4 was found to have comparable corrosion behavior as wrought Zircaloy-4 for specimens which did not have clear surface defects along weld interfaces.

36 MATERIALS SCIENCE↗
DOE OSTI2024

NSUF BOILER Pre-Irradiation Characterization and High Flux Isotope Reactor Experiment Design

Alumina-forming austenitic (AFA) stainless steels have emerged as a candidate alloy because of their high-temperature strength, formability, cost, and compatibility with primary coolants for lead-cooled fast reactors (LFRs). This class of steels has exceptional high-temperature oxidation performance; however, a high concentration of Ni is required to stabilize the austenite phase and to provide sufficient creep strength. AFA stainless steels are also susceptible to liquid metal embrittlement (LME). Additionally, under neutron irradiation, Ni will enrich at grain boundaries due to radiation-induced segregation (RIS). Nickel RIS can increase the LME under these coupled effects. Oak Ridge National Laboratory (ORNL) and the NSUF program have leveraged its High Flux Isotope Reactor (HFIR) and experience with complex irradiation experiments to design experiment capsules that test the aforementioned coupled effects. These capsules are designed for insertion in the central flux trap, the highest flux region, of HFIR. The experiment capsules will be filled with Pb, designed to passively melt from the gamma heating in HFIR. The specimens were fabricated into miniature tensile specimens from two different alloys, GA05-25Ni and GA05-20Ni, varying Ni concentrations. The experiment capsules are designed to achieve target temperatures of 400 °C and 650 °C with accumulated dosage of 3 dpa. This report documents the specimen alloy characterization, experimental design, and expected performance of the capsules.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗
DOE OSTI2024

Understanding EBC Lifetimes and Performance for Industrial Gas Turbines

Hydrogen or hydrogen blend fuels are expected to replace natural gas in land-based industrial gas turbines (IGTs) to support a greener power economy. Silicon carbide (SiC) base ceramic matrix composites (CMCs) are considered for replacement of Ni-based superalloys to facilitate future efficiency improvements. SiC CMCs require environmental barrier coatings (EBCs) to mitigate volatilization from high-temperature steam, thus making the EBC lifetime critical information for identifying CMC component lifetimes. The goal of this project is to determine the maximum bond coating temperature underneath the EBC for achieving an IGT component lifetime goal of 25,000 h, which is far greater than current CMC component lifetime requirements for aero-turbine applications. To provide data for the lifetime model, laboratory testing used plasma-sprayed rare-earth silicate EBCs on monolithic SiC substrates with an intermediate Si bond coating. Specimens exposed to 1-h thermal cycles in flowing air-steam environments and reaction kinetics were assessed from 700°-1350°C by measuring the thickness of the thermally grown silica scales. The silica growth and phase transformation appear critical in predicting EBC lifetime and several strategies have been explored to reduce the oxide growth rate and improve EBC durability at elevated temperatures. Advanced characterization using Raman spectroscopy has helped clarify this system.

Ridley, Mackenzie↗
DOE OSTI2024

Environmental barrier coatings on SiC without a silicon bond coating: oxidation resistance, failure modes, and future improvements

Environmental barrier coatings (EBCs) are used to mitigate chemical reactions between SiC ceramic matrix composite (CMC) components and the H 2 O in combustion gas in turbine hot sections. CMCs are currently temperature-limited by the Si-bond coating, which melts at ~ 1414 °C. This work explores EBCs where the bond coating was removed to achieve higher operating temperatures. Various versions of enhanced roughness SiC were utilized to improve EBC adhesion to the substrates prior to 1 h furnace cycle testing in steam at 1250–1425 °C. The enhanced SiC roughness resulted in short coating lifetimes as the roughness was oxidized away with SiO 2 formation. Further, isothermal furnace exposures at 1400–1600 °C showed Yb 2 Si 2 O 7 /Yb 2 SiO 5 EBC microstructural changes, resulting in premature debonding from the substrates. Finally, this work provides baseline requirements for the development of both next-generation EBCs and bond coating strategies to overcome the current limitation of the Si-bond coating melting temperature.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Advanced Coating Compositions and Microstructures to Improve Uptime and Operational Flexibility in Cyclic, Low-Load Thermal Utility Plants

GE, the University of Tennessee, and Oak Ridge National Laboratory collaborated from 2020 to 2023 developing two key technologies for improving the viability of fuel switching and load following in thermal utility plants: a) cost-effective weld overlay compositions for boiler tubing b) cathodic arc coatings that deliver improvements in both erosion resistance and oxidation resistance in high temperature steam for HP turbine blades The team worked through a robust, logical project map to de-risk these two technologies and advance them from TRL 3 to TRL 6. For the cost-effective weld overlay, the team developed a ferritic filler material which was fabricated at a vendor for 18% the average market cost of Inconel 625 wire, had a corrosion rate 3x lower in conditions simulating a biomass-fired superheater and 10x lower in conditions simulating a coal-fired superheater, and was fabricated into prototype overlaid tubing that passed ASME requirements including transverse bending, dye penetrant inspection, and ASTM G-76 evaluation. For the cathodic arc coatings applied to steam turbine blades, the team developed a novel composition that was successfully transferred to a qualified vendor. The vendor was able to produce coated prototypes with 4x the as-deposited erosion resistance and 10.4x the post-steam-exposure erosion resistance of the TiN coating the vendor currently applies on GE steam turbine components, without significantly increasing process cost. These coated prototypes also passed a GE inspection and showed favorable performance in high temperature erosion, nanoindentation, sliding wear, scratch adhesion, and high cycle fatigue testing. If successfully deployed by GE, it is anticipated that the technologies will enable the following: • 25%-50% increase in time between outages for both boilers and HP turbines. • 50% decrease in cost for weld overlay on a per foot basis relative to todays NiCr alloys. • Adequate oxidation resistance and erosion for HP turbine inlet steam at >620°C and >220 bar. • No need for changes in component supply chain or any notable Capital Expenditures. 5 Decreasing component cost, increasing performance, and extending time between outages represent direct value propositions to GE and their customers. For the American consumer, these objectives translate into increased grid reliability (fewer unexpected outages), decreased Levelized Cost of Electricity, and improved environmental health (low-loading/load following to accelerate penetration of renewables). The results also have implications for wear resistant tooling, wire arc additive manufacturing, more durable components for syngas cleanup, and deployment of more efficient thermochemical pathways for carbon negative fuel production

09 BIOMASS FUELS↗
DOE OSTI2023

Ultimate FY23 Vacuum Creep Testing Facility Operation Report

This facility operation report covers the refurbishment and initial testing of a vacuum creep frame used to conduct 1300°C tensile and creep tests on Mo- and Nb-based alloys. The report details the refurbishment of the frame and initial operation including 100 h creep experiments compared to similar tests in argon. Unlike the 25 mm dogbone specimens tested in argon, the vacuum load train requires 76 mm dog bone specimens. Testing in vacuum has eliminated concern of O embrittlement in argon and Nb alloy CB103 showed >120% tensile elongation at 1300°C and 1450°C. Also, a window in the vacuum chamber allows the use of digital image correlation (DIC) to measure strain rather than the load train displacement used in the argon frames. Comparison of the displacement and DIC results in the vacuum frame showed significant variation in primary creep deformation, likely due to the machine compliance, but similar secondary creep rates. Recently, ULTIMATE teams have submitted specimens for testing in vacuum. With the relatively low volume of creep testing, the facility performance metric of testing within 4 weeks of receiving specimens has been met.

36 MATERIALS SCIENCE↗
DOE OSTI2023

THE IMPACT OF OXIDATION-INDUCED DEGRADATION ON MATERIALS USED IN HYDROGEN-FIRED MICROTURBINES

Hydrogen-fueled microturbines are being considered as part of the future green microgrid. However, the use of hydrogen as a fuel presents new challenges for selection and development of suitable high temperature materials for hydrogen combustion. The burning of hydrogen is expected to result in higher operating temperatures and higher than typically observed water vapor contents in exhaust gases than after burning natural gas. In the present work, foil specimens of various Fe- and Ni-based alloys were oxidized in air + 10vol.% H2O and air + 60vol.% H2O for up to 5,000 h at 700 °C to simulate the exhaust atmosphere of natural gas and hydrogen-fueled microturbines. The impact of alloy composition and water vapor content on the oxidation/ volatilization induced loss of wall thickness was experimentally evaluated. Enhanced external oxidation and volatilization of Cr¬2O3 and Ti-doped Cr2O3 scales was observed in 60 % H2O compared to 10% H2O. No significant impact of the higher water vapor content was observed on Al2O3 scales formed on Fe-based alumina forming alloys. Lifetime modeling was employed to predict the combined effects of water vapor content, gas flow rates, temperature and alloy composition on the oxidation-induced lifetime of the investigated materials

Romedenne, Marie↗