Understanding a novel form of intergranular corrosion of stainless steel 316L exposed to molten LiCl-Li 2 O-Li

We report stainless steel 316 L exposed to LiCl-Li2O molten salt containing Li metal for 500 and 1000 h experiences deep intergranular attack and bulk void formation. This degradation is due to a synergistic corrosion mechanism, different than other forms of molten salt corrosion, where Cr and Mn oxides and carbides form along grain boundaries and are dissolved by Li metal. Synchrotron transmission X-ray microscopy 3D imaging is used to show corrosion morphology and Cr enrichment and depletion in a novel format that has not previously been used for bulk corrosion samples.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2023

First-of-a-Kind Fuel-bearing Molten Chloride Irradiation Experiment

As a dozen MSR developers in the U.S. work toward an aggressive commercialization timeline, many of their fueled-salts—notably, chloride-based compositions—have never been irradiated. Licensing and operating these reactors requires an understanding of (1) the source term, radiation chemistry, and gas generation; (2) unanticipated irradiation-induced corrosion effects; and (3) the impact of burnup on thermophysical properties, all of which can be deduced through irradiation testing. Idaho National Laboratory (INL) is ideally suited to leverage its expertise in chloride salt chemistry, as well as its Neutron Radiography Reactor (NRAD) facility in the Hot Fuels Examination Facility (HFEF) at the Materials and Fuels Complex (MFC), to conduct the world’s first fuel-bearing chloride salt irradiation and fill in the knowledge gaps pertaining to salt chemistry under irradiation. Molten-salt Research Temperature-controlled Irradiation (MRTI) consists of a salt-containing capsule that is internally heated inside of a secondary containment. The experiment must rely on resistive heating to melt the salt before irradiation (to avoid the impact of radiolysis) and once the reactor is turned on and fission reactions commence in the salt, the resistive power can then be reduced. Salt-immersed thermocouples coupled to a controller allow for the heater power to be adjusted as needed to meet experimental objectives. The bulk of the experimental results will be achieved through Post-Irradiation Examination (PIE). At which point a range of different measurements are anticipated to assess the salt/plenum/wall composition, the capsule corrosion rate, and the evolution of salt properties.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2023

First-of-a-Kind Fuel-bearing Molten Chloride Irradiation Experiment

Molten salt reactors (MSRs) have garnered increasing attention recently with several demonstration efforts on the way. A key challenge to the licensing basis for these reactors is the lack of experimental data on fueled salts. This is expected to be crucial to the safety evaluation and licensing basis of reactors of this type deployed in the future. While capability for irradiating molten salts has been reestablished in the recent decade, no enriched fuel irradiation capability has been developed and tested as of yet. A new experiment vehicle under development at Idaho National Laboratory (INL) is presented here. The Molten-salt Research Temperature-controlled Irradiation (MRTI) experiment was developed to host enriched uranium bearing salt samples to be irradiated at a test reactor within the lab complex. One of the key scientific objectives is to provide irradiated salt samples for post-irradiation examination (PIE) to study the impact of fission product generation and neutron/gamma radioactivity on the salt solution and salt-facing wall material. This paper provides a detailed overview of the mechanical design of the experiment, followed by an overview of the fabrication and assembly of an initial prototype vehicle (with non-fuel-bearing salt). A summary of the key analyses conducted as a part of the performance and safety evaluation is then provided. Lastly, an overview of the test conducted in prototypic out-of-pile (non-neutron) environment are shown. These evaluations provide the foundation for a planned irradiation of an enriched uranium-bearing chloride salt sample in the near term. The upcoming irradiation will contain 13 cm3 of UCl3-NaCl salt (93% enrichment) generating around 20 W/cm3 of fission energy during irradiation and a temperature range that can be contained between bounds of 525-900°C.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2023

Design and Fabrication of a Temperature-Controlled Fueled Molten Salt Capsule Irradiation Experiment

Idaho National Laboratory (INL) is developing a Molten salt Research Temperature-controlled Irradiation (MRTI) experimental capsule for the Neutron Radiography (NRAD) reactor. The experiment is envisaged to be versatile and able to host a variety of salt-wall material combinations. The first test is designed to contain actinide-bearing chloride salt, which previously has not been subjected to a neutron field. The main objectives of the experiment are to produce irradiated salt samples for Post Irradiation Examination (PIE), to evaluate salt behavior under irradiation, and to test in-situ sensors/instrumentation. The final design for the experiment completed in 2022, and fabrication of the experiment is underway. The salt is double encapsulated providing insulation and redundancy in the case of leakage. A gas-gap between the inner capsule and the outer container enables tuning of thermal conduction to the NRAD coolant by altering its thickness and its gas-mixture. An inert gas mixture ratio in the gas-gap ensures the configurations reached a targeted average salt temperature of 600oC, while avoiding salt freezing or exceeding material limits. A resistive heater placed within a thermowell and controls the temperature of the experiment (both when the reactor is on or off). The selected configurations can contain over 10 cm3 of fuel-bearing chloride salt, which is sufficient for the purposes of the post-irradiation examination (PIE) and provides sufficient volume for two submerged thermocouple probes to monitor salt temperature. The capsule wall material is Inconel 625, and weld qualifications for the assembly have been developed. A glove-box laser weld technique was refined as part of this process to ensure a leak-tight assembly for the salt-bearing assembly and reduce the risks of impurities permeating into the salt. This work was supported through the INL Laboratory Directed Research & Development (LDRD) Program under DOE Idaho Operations Office Contract DE-AC07-05ID14517.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2023

ENYGF 2023 - Design of Temperature-controlled Fuel-salt Irradiation Experiment

Idaho National Laboratory (INL) is developing a Molten salt Research Temperature-controlled Irradiation (MRTI) experimental capsule for the Neutron Radiography (NRAD) reactor. The experiment is envisaged to be versatile and able to host a variety of salt-wall material combinations. The first test is designed to contain actinide-bearing chloride salt, which previously has not been subjected to a neutron field. The main objectives of the experiment are to produce irradiated salt samples for Post Irradiation Examination (PIE), to evaluate salt behavior under irradiation, and to test in-situ sensors/instrumentation. The final design for the experiment completed in 2022, and fabrication of the experiment is underway. The salt is double encapsulated providing insulation and redundancy in the case of leakage. A gas-gap between the inner capsule and the outer container enables tuning of thermal conduction to the NRAD coolant by altering its thickness and its gas-mixture. An inert gas mixture ratio in the gas-gap ensures the configurations reached a targeted average salt temperature of 600oC, while avoiding salt freezing or exceeding material limits. A resistive heater placed within a thermowell and controls the temperature of the experiment (both when the reactor is on or off). The selected configurations can contain over 10 cm3 of fuel-bearing chloride salt, which is sufficient for the purposes of the post-irradiation examination (PIE) and provides sufficient volume for two submerged thermocouple probes to monitor salt temperature. The capsule wall material is Inconel 625, and weld qualifications for the assembly have been developed. A glove-box laser weld technique was refined as part of this process to ensure a leak-tight assembly for the salt-bearing assembly and reduce the risks of impurities permeating into the salt. This work was supported through the INL Laboratory Directed Research & Development (LDRD) Program under DOE Idaho Operations Office Contract DE-AC07-05ID14517.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

Vacuum Assisted Filtered Salt Sampling Progress

Several different design iterations for a filtered salt sampling technique have been tested in non-radiological molten salts. A piston vacuum assembly was designed and reliably and repeatably used to take salt samples through multiple different porous quartz frit sizes (as small as 5 – 10 µm). This design has been modified slightly and sent into the HFEF hot cell for upcoming testing with used fuel electrorefiner salt.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗