Effects of truncation of a predominantly compression load spectrum on the life of a notched graphite/epoxy laminate

Constant amplitude and transport wing spectrum compressive loading tests were used to explore the fatigue behavior of a notched, graphite/epoxy T300/5208 laminate specimen. Results indicate that (1) the amount of buckling near the notch allowed in the tests significantly affected fatigue life; (2) load spectrum truncation at either high or low ends produced lives greater than those obtained for the baseline complete-spectrum test, but with greater impact at the high-load end; and (3) the predictions of the Palmgren-Miner cumulative damage theory were found to always be far longer than those obtained in the spectrum loading tests.

Phillips, E. P.↗
NASA NTRS1981

Application of remote sensing to land and water resource planning: The Pocomoke River Basin, Maryland

Because of the size of the Pocomoke River Basin, the inaccessibility of certain areas, and study time constraints, several remote sensing techniques were used to collect base information on the river corridor, (a 23.2 km channel) and on a 1.2 km wooded floodplain. This information provided an adequate understanding of the environment and its resources, thus enabling effective management options to be designed. The remote sensing techniques used for assessment included manual analysis of high altitude color-infrared photography, computer-assisted analysis of LANDSAT-2 imagery, and the application of airborne oceanographic Lidar for topographic mapping. Results show that each techniques was valuable in providing the needed base data necessary for resource planning.

Wildesen, S. E.↗
NASA NTRS1979

Effects of truncation of a predominantly compression load spectrum on the life of a notched graphite/epoxy laminate

The fatigue behavior of a notched, graphite/epoxy (T300/5208) laminate subjected to predominantly compressive loading was explored in a series of constant-amplitude and transport wing spectrum tests. Results of these tests indicate that (1) the amount of local (near the notch) buckling allowed in the tests significantly affected fatigue life; (2) spectrum truncation of either the high- or low-load end of the spectrum produced lives greater than those obtained in the baseline, complete-spectrum test, but life was much more sensitive to truncations at the high-load end; and (3) the Palmgren-Miner linear cumulative damage theory always predicted lives much longer than the actual spectrum loading test lives.

Phillips, E. P.↗
NASA NTRS1974

Effect of outdoor exposure at ambient and elevated temperatures on fatigue life of Ti-6Al-4V titanium alloy sheet in the annealed and the solution treated and aged condition

Specimens of Ti-6Al-4V titanium alloy sheet in the annealed and the solution-treated and aged heat-treatment condition were exposed outdoors at ambient and 560 K (550 F) temperatures to determine the effect of outdoor exposure on fatigue life. Effects of exposure were determined by comparing fatigue lives of exposed specimens to those of unexpected specimens. Two procedures for fatigue testing the exposed specimens were evaluated: (1) fatigue tests conducted outdoors by applying 1200 load cycles per week until failure occurred and (2) conventional fatigue tests (continuous cycling until failure occurred) conducted indoors after outdoor exposure under static load. The exposure period ranged from 9 to 28 months for the outdoor fatigue-test group and was 24 months for the static-load group. All fatigue tests were constant-amplitude bending of specimens containing a drilled hole (stress concentration factor of 1.6). The results of the tests indicate that the fatigue lives of solution-treated and aged specimens were significantly reduced by the outdoor exposure at 560 K but not by the exposure at ambient temperature. Fatigue lives of the annealed specimens were essentially unaffected by the outdoor exposure at either temperature. The two test procedures - outdoor fatigue test and indoor fatigue test after outdoor exposure - led to the same conclusions about exposure effects.

Phillips, E. P.↗