Ambient pressure synthesis and characterization of layered honeycomb Li 2 PdO 3
Single-phase polycrystalline Li 2 PdO 3 has been synthesized at 640°C in oxygen for the first time under ambient pressure. X-ray and neutron diffraction analyses show that the sample possesses a monoclinic layered structure belonging to the C2/m space group. Rietveld refinements of neutron powder diffraction data indicate ~10% Li–Pd site exchange and DIFFaX modelling manifest ~2% stacking faults present within LiPd 2 layers. A band gap of ~2.23 eV was calculated for the golden Li 2 PdO 3 using absorbance measurements. Thermogravimetric analysis of the sample shows that Li 2 PdO 3 is stable up to 730°C under oxygen. Here a Curie tail is observed at low temperature magnetic measurements (T < 50K), yielding an effective moment of 0.038 μ B , possibly due to spin ½ impurities.