Lewis Acid‐Activated Charge Trapping in Dielectric Polymers for Superior High‐Temperature Electrostatic Energy Storage

Dielectric polymer capacitors are essential for electrostatic energy storage but suffer from charge transport-induced energy losses, particularly at elevated temperatures where thermally activated charge carriers exacerbate conduction. Conventional mitigation strategies rely on introducing heterogeneous interfaces to create charge traps, complicating scalable film fabrication. A homogeneous molecular trapping mechanism would circumvent these complexities, yet remains underexplored. Herein, a charge trapping strategy is devised by modifying the lowest occupied molecular orbitals of dielectric polymers through Lewis acid-base adduct formation. The use of tris(pentafluorophenyl)boron (BCF) as a Lewis acidic molecular additive introduces deeper charge traps in commercial polyetherimide (PEI) while retaining homogeneity. With only 0.5 wt.% loading, the PEI-BCF film exhibits greatly improved breakdown strength, achieving an ultrahigh discharged energy density of 7.3 J cm-3 with excellent cycle stability at 200 °C. This work establishes a facile molecular approach to decoupling charge trapping from heterogeneous interfaces, enabling high-energy-density polymer capacitors operable under extreme thermal conditions.

Fan, Lu↗

DOE OSTI2024

Interfacial Engineering Using Covalent Organic Frameworks in Polymer Composites for High‐Temperature Electrostatic Energy Storage

Abstract The use of inorganic nanofillers has been an effective method to improve high‐temperature capacitive performance of dielectric polymers, though there are unmet challenges such as undesirable organic–inorganic compatibility, and low efficiencies and energy densities. Herein, a surface functionalization strategy using covalent organic frameworks (COFs) is employed to address such challenges in realizing high‐performing polymer composites. Specifically, core–shell structured nanoparticles, where ZrO 2 nanoparticles act as the core and a COF material forms the shell, are constructed and composited with the polyetherimide (PEI) matrix. The design leverages the high electron affinity ( E A ) of the outer COF shell to create energy traps, thereby capturing free charges and limiting electrical conduction. Concurrently, the low E A and wide bandgap of the ZrO 2 core introduce energy barriers to impede charge injection and migration. This orchestrated “energy level cascade” results in a marked reduction of leakage current and energy loss. The resulting polymer composite showcases an impressive discharged energy density of 6.21 J cm −3 at an efficiency above 90%, with a maximum discharged energy density reaching 7.43 J cm −3 at 150 °C. These performance metrics position the PEI/ZrO 2 @COF polymer composite to surpass or be on par with state‐of‐the‐art high‐temperature PEI composites and other advanced polymer dielectrics.

Xie, Zongliang↗