The evolution of axisymmetric equilibrium shapes of a rotating liquid drop can be extended beyond the 2-lobed shape bifurcation point if the rotating drop is driven in the n=2 axisymmetric shape oscillation (perturbation), where n is the mode of oscillation.
Five thermophysical properties of molten silicon measured by the High Temperature Electrostatic Levitator (HTESL) at JPL are presented. The properties measured are the density, the constant pressure specific heat capacity, the hemispherical total emissivity, the surface tension and the viscosity.
We investigate the phenomenon of acoustic pressure-induced nucleation by using a novel approach involving the large amplitude resonant radial oscillations and collapse of a single bubble intentionally injected into a supercooled liquid. Using a combination of previously developed and proven techniques, the bubble is suspended in a fluid host by an ultrasonic field which supplies both the levitation capability as well as the forcing of the radial oscillations. We observe the effects of an increase in pressure (due to bubble collapse) in a region no larger than 100 microns within the supercooled melt to rigorously probe the hypothesis of pressure-induced nucleation of the solid phase. The use of single bubbles operating in narrow temporal and spatial scales will allow the direct and unambiguous correlation between the origin and location of the generation of the disturbance and the location and timing of the nucleation event. In a companion research effort, we are developing novel techniques for the non-contact measurements of the surface tension and viscosity of highly viscous supercooled liquids. Currently used non-invasive methods of surface tension measurement for the case of undercooled liquids generally rely of the quantitative determination of the resonance frequencies of drop shape oscillations, of the dynamics of surface capillary waves, or of the velocity of streaming flows. These methods become quickly ineffective when the liquid viscosity rises to a significant value. An alternate and accurate method which would be applicable to liquids of significant viscosity is therefore needed. We plan to develop such a capability by measuring the equilibrium shape of levitated undercooled melt droplets as they undergo solid-body rotation. The experimental measurement of the characteristic point of transition (bifurcation point) between axisymmetric and two-lobed shapes will be used to calculate the surface tension of the liquid. Such an approach has already been validated through the experimental verification of numerical modeling results. The experimental approach involves levitation, melting, and solidification of undercooled droplets using a hybrid ultrasonic-electrostatic technique in both a gaseous as well as a vacuum environment. A shape relaxation method will be investigated in order to derive a reliable method to measure the viscosity of undercooled melts. The analysis of the monotonic relaxation to equilibrium shape of a drastically deformed and super-critically damped free drop has been used to derive interfacial tension of immiscible liquid combinations where one of the component has high viscosity. A standard approach uses the initial elongation of a droplet through shear flows, but an equivalent method could involve the initial deformation of a drop levitated in a gas by ultrasonic radiation pressure, electric stresses, or even solid body rotation. The dynamic behavior of the free drop relaxing back to equilibrium shape will be modeled, and its characteristic time dependence should provide a quantitative means to evaluate the liquid viscosity.
A two-frequency acoustic apparatus has been developed to study the dynamics of a single gas or vapor bubble in water.
A two-frequency acoustic apparatus is used to study resonant coupling of oscillating gas or vapor bubbles in water.
Explore the source record for details and available documents.
The dendritic growth velocity of ice crystals is measured at undercooling levels between 5-8.5 K using a unique apparatus. The result shows that the measured velocities are smaller that the theoretical prediction based on the thermal diffusion theory with the scalling constant, Q= 0.025, which has been shown to agree with the experimental results at lower undercooling levels between 0.4 -2.5 K.
Thermophysical properties of high temperature molten materials have not been determined accurately because of the experimental problems associated with taking measurements at high temperatures.
The specific volumes and viscosities of the Ni-Zr liquid alloys as a function of temperature are determined by employing a digitizing technique and numeric analysis methods applied to the optical images of the electrostatically levitated liquid alloys.
The specific volumes of the Zr(41.2)Ti(3.8)Cu(2.5)Ni(10.0)Be(22.5) alloy as a function of temperature, T, are determined by employing an image digitizing technique and numerical calculation methods applied to the electrostatically levitated spherical alloy. The linear fitting of the volumes of the alloy in the liquid, V(sub l), glass, V(sub g) and crystalline V(sub c), states in the temperature ranges shown in parentheses are V(sub l)(T) = 0.1583 + 8.877 x 10(exp -6) T(cu cm/g) (700-1300 K);V(sub g)(T) = 0.1603 + 5.528 x 10(exp -6) T (400-550 K);V(sub c)(T) = 0.1583 + 6.21 x 10(exp -6)T(400-850 K). The average volume thermal expansion coefficients within the temperature ranges are determined to be 5.32, 3.39. and 3.83 x 10(exp -5) (1/K) for the liquid, glass, and crystalline states, respectively.
We have determined the densities of Si in the liquid, rho1(T), and solid,rho s(T), states as a function of temperature,T, by employing an image digitizing technique and numerical calculation methods in combination with an electrostatic levitator.
The specific volumes of the Zr 41.2 Ti 13.8 Cu 12.5 Ni 10.0 Be 22.5 alloy as a function of temperature, T, are determined by employing an image digitizing technique and numerical calculation methods applied to the electrostatically levitated spherical alloy.
Explore the source record for details and available documents.
In alloys, solidification takes place along various paths which may be ascertained via phase diagrams; while there would be no single formula applicable to all alloys, an approximate formula for a specific solidification path would be useful in estimating the fraction of the solid formed during recalescence. A formulation is here presented of recalescence in binary eutectic alloys. This formula is applied to Ag-Cu alloys which are of interest in containerless solidification, due to their formation of supersaturated solutions.
Supercooling of a liquid prior to the nucleation of a solid and the subsequent rapid growth are necessary conditions for producing novel microstructures including metastable phases which are not formed by conventional solidification processes. Since containerless techniques, such as levitation and free fall of a sample, are capable of achieving a significant supercooling level of liquids, they are under consideration as possible techniques for material processing on earth and in space.
The heats of eutectic melting and devitrification, and the specific heats of the crystalline, glass, and liquid phases have been measured for a Ni24Zr76 alloy. The data are used to calculate the Gibbs free-energy difference, Delta G(AC), between the real glass and the crystal on an assumption that the liquid-glass transition is second order. The result shows that Delta G(AC) continuously increases as the temperature decreases in contrast to the ideal glass case where Delta G(AC) is assumed to be independent of temperature.
A versatile electromagnetic levitator for ground-based experiments is under development at the Jet Propulsion Laboratory.
The heat of fusion and the specific heats of the solid and liquid have been experimentally determined for a Ti60Cr40 alloy. The data are used to evaluate the Gibbs free energy difference, delta-G, between the liquid and the beta phase as a function of temperature to verify a reported spontaneous vitrification (SV) of the beta phase in Ti-Cr alloys. The results show that SV of an undistorted beta phase in the Ti60Cr40 alloy at 873 K is not feasible because delta-G is positive at the temperature. However, delta-G may become negative with additional excess free energy to the beta phase in the form of defects.