DOE OSTI2024

Measuring the density, viscosity, and surface tension of molten titanates using electrostatic levitation in microgravity

Rare earth and barium titanates are useful as ferroelectric, dielectric, and optical materials. Measurements of their thermophysical properties in the liquid state can help guide melt processing technologies for their manufacture and advance understanding of fragile liquids' behavior and glass formation. Here, we report the density, thermal expansion, viscosity, and surface tension of molten BaTi 2 O 5 , BaTi 4 O 9 , and 83TiO 2 -17RE 2 O 3 (RE = La or Nd). Measurements were made using electrostatic levitation and droplet oscillation techniques in microgravity, which provide access to quiescent liquid droplets and deep supercooling of 510–815 K below the equilibrium melting points. Densities were measured over 900–2400 K. Viscosities were similar for all four compositions, increasing from ~10 mPa s near 2100 K to ~30 mPa s near 1750 K. Surface tensions were 450–490 dyn cm -1 for the rare earth titanates and 383–395 dyn cm -1 for the barium titanates; surface tensions of all compositions had small or negligible temperature dependence over 1700–2200 K. In conclusion, for solids recovered after melt quenching, x-ray microtomography revealed the fracture mechanics in crystalline products and minimal internal porosity in glass products, likely arising from entrapped gas bubbles. Internal microstructures were generally similar for products processed either in microgravity or in a terrestrial aerodynamic levitator.

42 ENGINEERING↗

DOE OSTI2024

Microgravity effects on nonequilibrium melt processing of neodymium titanate: thermophysical properties, atomic structure, glass formation and crystallization

The relationships between materials processing and structure can vary between terrestrial and reduced gravity environments. As one case study, we compare the nonequilibrium melt processing of a rare-earth titanate, nominally 83TiO 2 -17Nd 2 O 3 , and the structure of its glassy and crystalline products. Density and thermal expansion for the liquid, supercooled liquid, and glass are measured over 300–1850 °C using the Electrostatic Levitation Furnace (ELF) in microgravity, and two replicate density measurements were reproducible to within 0.4%. Cooling rates in ELF are 40–110 °C s -1 lower than those in a terrestrial aerodynamic levitator due to the absence of forced convection. X-ray/neutron total scattering and Raman spectroscopy indicate that glasses processed on Earth and in microgravity exhibit similar atomic structures, with only subtle differences that are consistent with compositional variations of ~2 mol. % Nd 2 O 3 . The glass atomic network contains a mixture of corner- and edge-sharing Ti-O polyhedra, and the fraction of edge-sharing arrangements decreases with increasing Nd 2 O 3 content. X-ray tomography and electron microscopy of crystalline products reveal substantial differences in microstructure, grain size, and crystalline phases, which arise from differences in the melt processes.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Atomic and Electronic Structure in MgO–SiO 2

Understanding disordered structure is difficult due to insufficient information in experimental data. Here, we overcome this issue by using a combination of diffraction and simulation to investigate oxygen packing and network topology in glassy (g-) and liquid (l-) MgO–SiO 2 based on a comparison with the crystalline topology. We find that packing of oxygen atoms in Mg 2 SiO 4 is larger than that in MgSiO 3 , and that of the glasses is larger than that of the liquids. Moreover, topological analysis suggests that topological similarity between crystalline (c)- and g-(l-) Mg 2 SiO 4 is the signature of low glass-forming ability (GFA), and high GFA g-(l-) MgSiO 3 shows a unique glass topology, which is different from c-MgSiO 3 . We also find that the lowest unoccupied molecular orbital (LUMO) is a free electron-like state at a void site of magnesium atom arising from decreased oxygen coordination, which is far away from crystalline oxides in which LUMO is occupied by oxygen’s 3s orbital state in g- and l-MgO–SiO 2 , suggesting that electronic structure does not play an important role to determine GFA. We finally concluded the GFA of MgO–SiO 2 binary is dominated by the atomic structure in terms of network topology.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗