Nutt, S. R.

Publications and source records attributed to Nutt, S. R..

6 records

NASA NTRS1986

A failure mechanism in Al-SiC composites

Divecha et al. (1981) have discussed the advantages of materials obtained by adding silicon carbide whiskers to commercial aluminum alloys, taking into account also certain problems which are related to poor ductility and low fracture toughness. The present investigation has the objective to advance the understanding of the deformation at the whisker ends in reinforced aluminum composites through both observation and analysis. It is suggested that the low fracture toughness of the considered materials is the result of the rapid accumulation of damage at the whisker ends. It is pointed out that the whisker ends are sites of severe stress concentration and intense localized plastic strain. In connection with this situation, voids nucleate and grow at relatively low macroscopic stress levels. The reported studies include an examination of the deformation microstructure beneath the fracture surfaces of specimens with the aid of transmission electron microscopy.

Nutt, S. R.↗

NASA NTRS1986

Interfaces and failure mechanisms in Al-SiC composites

Aluminum alloys reinforced with silicon carbide whiskers exhibit significantly higher strength and modulus than the unreinforced alloys. However, the composites also exhibit low ductility and poor fracture toughness for reasons which are not well-understood. In this study, high resolution and conventional TEM techniques are used to analyze interface microstructure and failure mechanisms in P/M 2124 and 6061 aluminum alloys reinforced with silicon carbide whiskers. Interfacial oxides are typical of both composite materials, often distributed in clusters or in a discrete layer 2-5 nm thick along the whisker-matrix interface. Highly deformed regions beneath bulk tensile fracture surfaces reveal possible fracture nucleation centers as well as sites of stress concentration where intense plastic strain has occurred. Observations of such highly deformed regions include (1) void initiation at whisker ends, (2) interface decohesion involving the thin oxide layer, (3) transverse cracks in whiskers, and (4) cracks in large constituent particles. TEM results are presented and discussed in relation to mechanisms of composite failure.

Nutt, S. R.↗

NASA NTRS1985

Non-equilibrium phase distribution in an Al-SiC composite

The phase distribution in an Al-SiC composite has been investigated using high resolution analytical electron microscopy. Particular attention was focused on Al-SiC interfaces, matrix boundaries and impurity phases which would impede the easy glide of dislocations. Small crystallites of MgO were distributed singly and in clusters along Al-SiC interfaces in all specimens. Interfacial segregation and precipitation involving alloy species apparently affected precipitation in the matrix, where the distribution of phases was found to be very heterogeneous. Matrix phases also included unusually large constituent particles and dispersoids, a consequence of the composite processing methods. The relationship between the observed microstructure and the composite mechanical behavior reported by others is discussed. The heterogeneous distribution of matrix phases is expected to result in a wide variaiton in local yield stress and local work-hardening rate within the composite.

Nutt, S. R.↗

NASA NTRS1985

Silicon carbide filaments - Microstructure

The microstructure of chemically vapor deposited silicon carbide filaments has been examined using transmission electron microscopy. The filament bulk consisted of heavily faulted columnar subgrains of beta-SiC which were preferentially oriented such that 1 1 1 planes were parallel to the surface of the carbon fiber substrate. The protective coating on the filament surface was characterized by several microstructurally distinct layers, all of which consisted primarily of carbon. The first layers of the coating contained small crystallites of SiC in addition to turbostratic carbon, while the outer layers showed no evidence of SiC. Implications of the filament microstructure with respect to mechanical properties are discussed.

Nutt, S. R.↗

NASA NTRS1983

Microstructural characterization of SiC (SCS) filaments

Microstructural features of SiC('SCS') fibers demonstrating growth properties have been investigated using scanning and transmission electron microscopy. An etchant of fused KOH:KNO3 was developed which adequately brought out previously undetermined features.

Wawner, F. W.↗

NASA NTRS1980

Investigation of diffusion barrier materials on silicon carbide filaments

The formation of diffusion barrier materials on SiC filaments is discussed. The filaments possess a carbon-rich surface layer and, consequently, are difficult to wet by molten Al and tend to react with the molten metal, degrading filament strength. Characterization of the filament with various CVD barrier materials is reported.

Wawner, F. E.↗