Highly Active and Durable Air Electrodes for Reversible Protonic Ceramic Electrochemical Cells Enabled by an Efficient Bifunctional Catalyst

The commercialization of reversible protonic ceramic electrochemical cells is hindered by the lack of highly active and durable air electrodes exposed to high concentration of steam under operating conditions. We report findings that dramatically enhance the electrocatalytic activity and stability of a conventional (La 0.6 Sr 0.4 ) 0.95 Co 0.2 Fe 0.8 O 3-δ (LSCF) air electrode by a multiphase catalyst coating composed of a conformal Pr 1-x Ba x CoO 3-δ thin film and exsolved BaCoO 3-δ nanoparticles, are reported. At 600 °C, the catalyst coating decreases the polarization resistance of the LSCF air electrode by a factor of 25 (from 1.09 to 0.043 Ω cm 2 ) in air and the degradation rate by two orders of magnitude (from 1.0 × 10 -2 to 1.8 × 10 -4 Ω cm2 h -1 in humidified air with 30 vol% H2O). Further, a single cell with the catalyst-coated LSCF air electrode at 600 °C demonstrates a high peak power density of 1.04 W cm -2 in the fuel cell mode and a high current density of 1.82 A cm -2 at 1.3 V in the electrolysis mode. The significantly enhanced performance of the LSCF air electrode is attributed mainly to the high rate of surface oxygen exchange, fast surface proton diffusion, and the rapid H 2 O and O 2 dissociation on the catalysts.

36 MATERIALS SCIENCE↗

DOE OSTI2021

A highly efficient and durable air electrode for intermediate-temperature reversible solid oxide cells

Solid oxide cells (SOCs) are considered the most efficient system for reversible conversion between chemical and electrical energy, thus having potential to be an attractive technology for a sustainable energy future. To achieve high round-trip efficiency, highly efficient and durable air electrode materials are needed to minimize energy loss associated with oxygen reduction reaction (ORR) and oxygen evolution reaction (OER). Here we report a bi-functional air electrode material, PrBa 0.9 Co 1.96 Nb 0.04 O 5+δ , demonstrating outstanding electrochemical performance (e.g., achieving peak power densities of over 1.5 and 1 W cm –2 , respectively, for Gd 0.1 Ce 0.9 O 1.95 and BaZr 0.1 Ce 0.7 Y 0.1 Yb 0.1 O 3-δ based fuel cells at 600 °C) while maintaining excellent stability (e.g., having a degradation rate of 40 mV per 1,000 h for H 2 O electrolysis cells). Finally, the excellent property of the new electrode is attributed to the improved stability from Nb doping and the enhanced electrocatalytic activity from tuning Ba deficiency, as confirmed by experimental results and computational analysis.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

An Active and Robust Air Electrode for Reversible Protonic Ceramic Electrochemical Cells

Reversible protonic ceramic electrochemical cells (RPCECs) are a promising option for efficient and low-cost generation of electricity and hydrogen. Commercialization of R-PCECs, however, hinges on the development of highly active and robust air electrodes. Here, we report an air electrode consisting of PrBa 0.8 Ca 0.2 Co 2 O 5+δ and in situ exsolved BaCoO 3–δ nanoparticles (PBCC–BCO) that shows minimal polarization resistance (~0.24 Ω cm 2 at 600 °C) and high stability when exposed to humidified air with 3–50% H 2 O. An R-PCEC utilizing PBCC-BCO demonstrates remarkable performances at 600 °C: achieving a peak power density of 1.06 W cm –2 in the fuel cell mode and a current density of 1.51 A cm –2 at 1.3 V in an electrolysis mode. More importantly, the RPCECs demonstrate an exceptionally high durability over 1833 h of continuous operation in the electrolysis mode. Furthermore, this work offers an efficient approach to design of high-performance and durable electrodes for R-PCECs.

25 ENERGY STORAGE↗