Understanding the Elastic, Plastic, and Damage Features in Fracturing of Self-reinforced Thermoplastic Composites via Non-destructive Digital Imaging Correlation

This work demonstrated the utilization of non-destructive Digital Imaging Correlation (DIC) method to characterize the elastic, plastic, and damage features during the Mode I intra-laminar fracturing process of self-reinforced thermoplastic composites by using a self-reinforced polypropylene (PP) composite as an example. The DIC results clearly showed the development of huge plastic zone (PZ) and non-negligible Fracture Process Zone (FPZ) in front of the notch tip during the fracturing process, and the geometries and sizes of the foregoing zones at the peak load were further quantified. Such an interesting fracturing behavior of self-reinforced thermoplastic composites is way different from brittle materials (e.g., glass, acrylic, etc.), ductile materials (e.g., aluminum, steel, etc.), and even quasi-brittle materials (e.g., concrete, nanoparticle-reinforced composites, tough ceramics, wood, cement, carbon/glass fiber-reinforced polymers, etc.). Thus, understanding the elastic, plastic, and damage features is the first step before better characterizing the material fracture properties of self-reinforced thermoplastic composites through new analytical methods and computational modeling. These efforts are of utmost importance for wide applications of self-reinforced thermoplastic composites in various engineering fields in the future.

Lightweight Composites, Self-reinforced Thermoplas↗
DOE OSTI2022

PNNL FY2021 Sibling Pin Testing Results

The post-irradiation examination, axial tensile, burst, and four-point bend testing results of the first two sibling pins, 6U3/L8 and 5K7/P2 are presented.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2021

Hot rolling of ZK60 magnesium sheet with isotropic tensile properties from tubing made by Shear Assisted Processing and Extrusion (ShAPE)

In order to evaluate the viability of ShAPE processed Mg alloys as a feedstock for fabricating lightweight sheet material, tubes consisting of ShAPE-extruded Mg alloy ZK60 were flattened into plates and hot rolled at 450 °C to reductions of 37%, 68%, and 93%. The mechanical properties and microstructure of the rolled material were characterized through tensile testing and electron backscattered diffraction (EBSD). ZK60 specimens rolled to 68% reduction had tensile properties similar to published properties of rolled ZK60 sheets fabricated using conventional processes, and exhibited negligible tensile anisotropy referenced to the rolling direction. Additional rolling from 68% to 93% reduced the ultimate tensile stress in the rolling direction from 341.74±5.96 MPa to 260.76±22.4MPa. The yield stress and elongation to failure of the material also decreased from 292.16±1.11 MPa to 256.93±18.4 MPa and 6.95±1.94% to 3.38±0.51%, respectively, but negligible little anisotropy was observed with respect to loading direction. EBSD mapping indicated that the as-extruded ZK60 had texture rotated away from the basal direction which developed into a strong basal texture over numerous hot rolling steps. This evolution in texture has been observed after rolling for hot-rolled ZK60 fabricated through conventional extrusion processes. The initial grain structure was found to have experienced noticeable twinning from flattening the tube into plate. After hot rolling, the grain structure became more equiaxed, but the average grain diameter did not change appreciably from 5.15 ± 3.39 µm in the ShAPE extruded material, to 5.27 ± 12.44 µm in the 93% hot rolled sheet. This response to hot rolling is similar to the response of ZK60 fabricated using other methods such as Equal Channel Angular Processing (ECAP). Therefore, this work demonstrates ShAPE has the potential as an alternative method to producing feedstock for Mg alloy sheets. Modifications to the experimental procedure which could lead to improvements in observed properties are briefly discussed.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Effect of hydrogen on tensile properties of 304L stainless steel at cryogenic temperatures

Safe and efficient hydrogen storage and distribution are key attributes to realizing hydrogen as an alternative energy carrier. To this end, cryogenic liquid and cryo-compressed gaseous hydrogen are considered high energy density alternatives to ambient temperature gas. However, these alternatives have significant material demands to overcome extreme temperature (20 K) and pressure (700 bar) as well as hydrogen effects. Austenitic stainless steels are widely used for cryogenic pressure vessels owing to relatively high ductility even at 4 K. However, the influence of hydrogen on mechanical properties at cryogenic temperatures has rarely been studied. In this study, the tensile properties of 304L austenitic stainless steel with internal hydrogen were evaluated at 20 K, 77 K, and 113 K. Test specimens were saturated with internal hydrogen to concentration of 140 wtppm in a high pressure environment at elevated temperature, a process called thermal precharging. While lower temperature in known to increase strength properties and reduced elongation at fracture, the presence of internal hydrogen increased both strength and elongation at fracture, but reduced ductility. Magnetic evaluation of the uniformly strained region of the test specimens suggest that hydrogen mitigates the strain-induced transformation to a’-martensite. Brittle fracture features and secondary cracking indicative of hydrogen embrittlement were observed on the fracture surfaces of hydrogen-precharged specimens, which is consistent with the loss of ductility.

Merkel, Daniel R.↗
DOE OSTI2021

Microstructural Progression of Shear-Induced Mixing in a CuNi Alloy

Shear deformation has been highlighted in multiple research efforts for its ability to impart mechanical properties improvements and unique microstructures. When used to process and densify powdered material, these shear-based consolidation techniques are commonly referred to as friction consolidation (FC). In this paper, we have examined the microstructural evolution from compacted Cu and Ni powders to a consolidated Cu0.5Ni0.5 alloy. We have shown various stages of porosity reduction and preferential deformation being accommodated by the more ductile material early in the process, leading to formation of a tortuous microstructural zone. Porosity reduction was extensive, decreasing from ~65% in the unprocessed powder to ~1% in the fully consolidated alloy. The final consolidated alloy showed roughly a 2X hardness improvement over the unalloyed, compacted material. Unique aspects of this work include demonstration of the ability to use FC processing to produce a submicron and equiaxed grain size in samples within a 0.5 to 2 minute processing time.