Challenges in atomic layer etching of gallium nitride using surface oxidation and ligand-exchange

Two atomic layer etching (ALE) methods were studied for crystalline GaN, based on oxidation, fluorination, and ligand exchange. Etching was performed on unintentionally doped GaN grown by hydride vapor phase epitaxy. For the first step, the GaN surfaces were oxidized using either water vapor or remote O 2 -plasma exposure to produce a thin oxide layer. Removal of the surface oxide was addressed using alternating exposures of hydrogen fluoride (HF) and trimethylgallium (TMG) via fluorination and ligand exchange, respectively. Several HF and TMG super cycles were implemented to remove the surface oxide. Each ALE process was monitored in situ using multiwavelength ellipsometry. X-ray photoelectron spectroscopy was employed for the characterization of surface composition and impurity states. Additionally, the thermal and plasma-enhanced ALE methods were performed on patterned wafers and transmission electron microscopy (TEM) was used to measure the surface change. The x-ray photoelectron spectroscopy measurements indicated that F and O impurities remained on etched surfaces for both ALE processes. Ellipsometry indicated a slight reduction in thickness. TEM indicated a removal rate that was less than predicted. In conclusion, we suggest that the etch rates were reduced due to the ordered structure of the oxide formed on crystalline GaN surfaces.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Space charge limited corrections to the power figure of merit for diamond

An interpretation of the unipolar figure of merit is formulated for wide bandgap (WBG) semiconductors based on the on-state specific resistance (RON,sp) derived from the space charge limited current–voltage relationship (Mott–Gurney square law). The limitations of the traditional Ohmic R ON,sp for WBG semiconductors are discussed, particularly at low doping, while the accuracy of the Mott–Gurney based R ON,sp is confirmed by Silvaco ATLAS drift–diffusion simulations of diamond Schottky pin diodes. The effects of incomplete ionization are considered as well.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗
DOE OSTI2022

Excess noise in high-current diamond diodes

We report the results of an investigation of low-frequency excess noise in high-current diamond diodes. It was found that the electronic excess noise of the diamond diodes is dominated by the 1/f and generation-recombination noise, which reveals itself as Lorentzian spectral features (f is the frequency). The generation-recombination bulges are characteristic of diamond diodes with lower turn-on voltages. The noise spectral density dependence on forward current, I, reveals three distinctive regions in all examined devices—it scales as I 2 at the low (I < 10 μA) and high (I > 10 mA) currents and, rather unusually, remains nearly constant at the intermediate current range. The characteristic trap time constants, extracted from the noise data, show a uniquely strong dependence on current. Interestingly, the performance of the diamond diodes improves with the increasing temperature. The obtained results are important for the development of noise spectroscopy-based approaches for device reliability assessment for high-power diamond electronics.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗
DOE OSTI2021

Comparison of AlF 3 thin films grown by thermal and plasma enhanced atomic layer deposition

Films of aluminum fluoride (AlF 3 ) deposited by thermal and plasma enhanced atomic layer deposition (PEALD) have been compared using in situ multiwavelength ellipsometry (MWE) and monochromatic x-ray photoelectron spectroscopy (XPS). The AlF 3 films were grown using cyclic exposures of trimethylaluminum, hydrogen fluoride, and H radicals from a remote H 2 inductively coupled plasma. Films were characterized in situ using MWE and XPS for growth rate, film composition, and impurity incorporation. The MWE showed a growth rate of 1.1 and 0.7 Å per cycle, at 100 °C, for thermal and plasma enhanced ALD AlF 3 films, respectively. Carbon incorporation was below the XPS detection limit. The plasma enhanced ALD AlF 3 film showed the presence of Al-Al chemical states, in the Al 2p scans, suggesting the presence of Al-rich clusters with a concentration of 14%. The Al-rich clusters are thought to originate during the hydrogen plasma step of the PEALD process. Finally, the Al-rich clusters were not detected in thermal ALD AlF 3 films using the same precursors and substrate temperature.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Current generation from radiation with diamond diode-based devices for detection or power generation

Diamond diode-based devices are configured to convert radiation energy into electrical current, useable for sensing (i.e., detection) or delivery to a load (i.e., energy harvesting). A diode-based detector includes an intrinsic diamond layer arranged between p-type diamond and n-type diamond layers, with the detector further including at least one of (i) a boron containing layer arranged proximate to the n-type and/or the intrinsic diamond layers, or (ii) an intrinsic diamond layer thickness in a range of 10 nm to 300 microns. A diode-based detector may be operated in a non-forward biased state, with a circuit used to transmit a current pulse in a forward bias direction to reset a detection state of the detector. An energy harvesting device may include at least one p-i-n stack (including an intrinsic diamond layer between p-type diamond and n-type diamond layers), with a radioisotope source arranged proximate to the at least one p-i-n stack.

Holmes, Jason M.↗
DOE OSTI2021

AlGaN/GaN metal–insulator–semiconductor high electron mobility transistors (MISHEMTs) using plasma deposited BN as gate dielectric

AlGaN/GaN metal–insulator–semiconductor high electron mobility transistors (MISHEMTs) were fabricated on Si substrates with a 10 nm boron nitride (BN) layer as a gate dielectric deposited by electron cyclotron resonance microwave plasma chemical vapor deposition. The material characterization of the BN/GaN interface was investigated by X-ray photoelectric spectroscopy (XPS) and UV photoelectron spectroscopy. The BN bandgap from the B1s XPS energy loss is ~5 eV consistent with sp2 bonding. The MISHEMTs exhibit a low off-state current of 1 × 10 –8 mA/mm, a high on/off current ratio of 10 9 , a threshold voltage of –2.76 V, a maximum transconductance of 32 mS/mm at a gate voltage of –2.1 V and a drain voltage of 1 V, a subthreshold swing of 69.1 mV/dec, and an on-resistance of 12.75 Ω·mm. The interface state density (D it ) is estimated to be less than 8.49 × 10 11 cm –2 eV –1 . Gate leakage current mechanisms were investigated by temperature-dependent current–voltage measurements from 300 K to 500 K. The maximum breakdown electric field is no less than 8.4 MV/cm. Poole–Frenkel emission and Fowler–Nordheim tunneling are indicated as the dominant mechanisms of the gate leakage through the BN gate dielectric at low and high electric fields, respectively.

36 MATERIALS SCIENCE↗