DOE OSTI2024

Length scale effects of micro- and meso-scale tensile tests of unirradiated and irradiated Zircaloy-4 cladding

Zircaloy-4 is an essential material for cladding structures within fission-based reactors. To explore the changes in properties measured on differing length scales, FIB-machined micro-scale tensile tests were performed on both irradiated and control groups of Zircaloy-4. This was correlated with tensile testing on femtosecond laser-machined meso-scale specimens. Pronounced size effects were found when varying specimen geometry. Increases in tensile geometry size were associated with a reduction in measured yield stress for both irradiated and unirradiated samples. Here, meso-scale testing found strength and strain values similar to that of bulk-scale testing.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Anisotropic Effects of Loading on Zircaloy Cladding Performance

This presentation provides recent results related to the mechanical behavior of Zircaloy cladding for the Light Water Reactor Fuels Workshop/CRAFT Initiative Update presented by the Advanced Fuels Campaign. This presentation focuses on Zircaloy cladding response to pellet-cladding interactions and how mechanical anisotropy makes the cladding sensitive to the testing mode. Results are compared to existing material models used by BISON, and implications for reactor performance are briefly discussed.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2024

Enhanced Stress Relaxation Behavior via Basal ⟨a⟩ Dislocation Activity in Zircaloy-4 Cladding

Herein this work evaluates the stress relaxation behavior of textured Zircaloy-4 cladding to understand how mechanical anisotropy influences pellet-cladding interactions. Uniaxial and biaxial stress relaxation tests are performed using full-tube axial tension and internal pressurization, respectively, aiming to achieve 0.25%, 1%, and 2% equivalent strains in the cladding samples at a temperature of 300°C. Internal pressure relaxation test results display enhanced stress relaxation compared to axial testing results, particularly for samples loaded beyond yield. Results of electron backscatter diffraction indicate increased deformation microstructure during loading and increased strain homogenization and recovery during relaxation for samples loaded via internal pressurization. Analysis indicates that the increased production and activity of basal ⟨a⟩ dislocations play a significant role in the enhanced relaxation measured in samples subjected to internal pressurization.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2024

Mechanical Response of Cr-Coated Zircaloy-4 Cladding to Pellet-Cladding Interactions

Chromium-coated zircaloy is a promising accident tolerant fuel (ATF) cladding design which can help mitigate high temperature oxidation. The mechanical response of the cladding during and after loading may be altered by the Cr coating throughout anticipated operational and accident occurrences such as a pellet-cladding interaction (PCI). In this work, the mechanical behavior of Cr-coated and uncoated cold worked stress-relieved (CWSR) Zircaloy-4 (Zry-4) cladding to PCI loading conditions are studied. Stress relaxation tests are performed on CWSR Zry-4 cladding using full-tube axial tension and internal pressurization to investigate mechanical anisotropy and rate-limiting deformation mechanisms of the uncoated Zry-4. These results are compared to internal pressure testing results of similar cladding with physical vapor deposition (PVD) Cr-coating to reveal how the Cr-coating affects the cladding mechanical response. Findings are discussed in the context of ATF cladding performance during operation and storage.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2024

Temperature-Dependent Mechanical Anisotropy in Textured Zircaloy Cladding

This work evaluates deformation activity in textured zircaloy-4 cladding with the aim of elucidating the mechanisms that govern mechanical behavior across a temperature range anticipated in reactor service. In particular, the dependence of mechanical anisotropy on temperature and stress state (ratio of applied stresses) is examined via uniaxial and biaxial tensile experiments at room temperature and 400 °C. The mechanical behavior was interpreted based on micro-texture and dominant slip system activity. Thermal activation of basal systems is found as a key mechanism affecting mechanical behavior across the temperature range. The biaxial stress states produce resolved shear stresses contrasting to uniaxial stress states. As a result, mechanical testing and implications for reactor pellet-cladding mechanical interaction stress conditions are discussed.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗