3 records

DOE OSTI2024

Scale-Up of a Two-Stage Cu-Catalyzed Alkaline-Oxidative Pretreatment of Hybrid Poplar

A two-stage alkaline-oxidative pretreatment of hybrid poplar was investigated at scale (20 L reactor volume) with the goals of understanding how reaction conditions as well as interstage mechanical refining impact downstream process responses. The pretreatment comprises a first stage of alkaline delignification (alkaline pre-extraction) followed by a second delignification stage employing Cu-catalyzed alkaline hydrogen peroxide with supplemental O 2 (O 2 -enhanced Cu-AHP). Increasing pre-extraction severity (i.e., temperature and alkali loading) and pre-treatment oxidation (increasing H 2 O 2 loading) were found to increase mass and lignin solubilization in each stage. Lignin recovered from the first stage was subjected to oxidative depolymerization and led to aromatic monomer yields as high as 23.0% by mass. As a result, lignins recovered from the second stage Cu-AHP pretreatment liquors were shown to exhibit aliphatic hydroxyl contents more than six-fold higher than for a typical hardwood kraft lignin, indicating these lignins could serve as a biobased polyol for a range of polyurethane applications.

09 BIOMASS FUELS↗

DOE OSTI2023

Fractionated and purified hybrid poplar lignins as a polyol replacement in rigid polyurethane/polyisocyanurate foams

This study introduces fractionated lignin as an innovative component in the formulation of rigid polyurethane/polyisocyanurate (PUR/PIR) foams. Low-density PUR/PIR rigid foams were prepared by replacing 80% of the petrochemical-based polyol with a hybrid poplar (HP) lignin, recovered via alkaline pretreatment, and also with a fraction of this lignin, isolated via the Aqueous Lignin Purification with Hot Agents (ALPHA) process. The as-recovered HP and ALPHA-fractionated HP lignins were characterized to determine hydroxyl content, molecular weight (Mw) distribution, and pH. Both lignin-based foams met minimum standard requirements in terms of closed cell content, compression strength, and thermal conductivity. Notably, the foams made with ALPHA-based lignin outperformed the as-recovered lignin-based foams in all measured foam properties. Moreover, the ALPHA-based foam had comparable performance to the control foam (without lignin) except for density and even surpassed the control foam in closed cell content and compressive strength. This investigation of the molecular properties of lignin suggests that significant reductions in lignin average molecular weight and polydispersity (PDI) can positively impact the properties of lignin-based rigid foams.

09 BIOMASS FUELS↗

DOE OSTI2023

Lignin-Based Low-Density Rigid Polyurethane/Polyisocyanurate Foams

In this paper, unmodified kraft softwood lignin was utilized to fully replace the petroleum-based polyol for the first time in low-density rigid polyurethane/polyisocyanurate (PUR/PIR) foam. The effects of different lignin incorporation levels (0, 25, 50, 75, and 100%) on foam properties were investigated by measuring foam’s reactivity, polyol viscosity (using a rheometer), apparent density, compression strength, closed cell content (using a gas pycnometer), thermal conductivity, fire resistance, and morphology (observed through SEM). All formulated lignin-based foams met the ASTM minimum requirements for type 1 rigid insulation foams. Remarkably, the foam made by replacing 100% of the petrochemical polyol with the commercially available kraft lignin demonstrated outstanding fire resistance performance, reducing the burn length by 127%.

09 BIOMASS FUELS↗