Composite-powder processing procedure developed along with plasma-spray parameters to achieve homogeneous, well-bonded, low-porosity, self-lubricating coatings. Multicomponent plasma coatings are applied without segretation of components.
Processing-technology development of a multiphase, self-lubricating, plasma-spray powder resulted in greater uniformity and reproducibility of plasma-sprayed coats. The effect of particle-size variation, binder concentration, and reproducible processing parameters are reported. Greater adhesive strengths of coats to substrates were achieved by particle-size variation, use of an intermediate bond coat such as Ni-Cr, or heat treatment. Quantitative analyses of polished, coated specimens are also given.
One of the most important criterion for acceptable commercial application of a multiple phase composition is uniformity and reproducibility. This means that the performance characteristics of the coat - e.g., its lubricating properties, bond strength to the substrate, and thermal properties - can be readily predicted to give a desired performance. The improvement of uniformity and reproducibility of the coats, the oxidation behavior at three temperature ranges, the effect of bond coat and the effect of preheat treatment as measured by adhesive strength tests, coating examination procedures, and physical property measurements were studied. The following modifications improved the uniformity and reproducibility: (1) changes and closer control in the particle size range of the raw materials used, (2) increasing the binder content from 3.2% to 4.1% (dried weight), and (3) analytical processing procedures using step by step checking to assure consistency.
Structural members supporting the afterburners of high thrust rocket engines are subjected to extreme heating, along with severe vibration and high acceleration levels during early lift-off. Chemically-bonded, castable, zircon composite foams were developed and successfully tested to meet specific, laboratory simulated lift-off conditions.
Preparation and characteristics of lightweight refractory insulation
Lightweight ceramic foam for thermal insulation heat shields of launch structures
Foamed refractory oxides provide lightweight, reflective thermal insulation materials. The materials have a low bulk density and high thermal shock resistance.
Ceramic foam as lightweight thermal insulation for rigid heat shields in launch vehicles