NASA NTRS1983

Laboratory experience with voltage breakdown

Voltage breakdown failures in photovoltaic module electrical insulations lead to loss of entire source circuits and require costly maintenance and replacement. Avoiding such catastrophes requires that modules be designed so that voltage breakdown either never occurs or occurs so rarely that it affects the least life cycle energy costs insignificantly. To achieve this desired balance of cost and reliability, the module design engineer must understand the failure mechanisms and use data on materials and failue rates to suppress or retard them. Recently obtained failure mechanism information, rate data and materials property data and a qualitative model of module failure prediction are presented.

Mon, G. R.↗

NASA NTRS1982

Interconnect fatigue design for terrestrial photovoltaic modules

The results of comprehensive investigation of interconnect fatigue that has led to the definition of useful reliability-design and life-prediction algorithms are presented. Experimental data indicate that the classical strain-cycle (fatigue) curve for the interconnect material is a good model of mean interconnect fatigue performance, but it fails to account for the broad statistical scatter, which is critical to reliability prediction. To fill this shortcoming the classical fatigue curve is combined with experimental cumulative interconnect failure rate data to yield statistical fatigue curves (having failure probability as a parameter) which enable (1) the prediction of cumulative interconnect failures during the design life of an array field, and (2) the unambiguous--ie., quantitative--interpretation of data from field-service qualification (accelerated thermal cycling) tests. Optimal interconnect cost-reliability design algorithms are derived based on minimizing the cost of energy over the design life of the array field.

Mon, G. R.↗

NASA NTRS1982

Design solutions for the solar cell interconnect fatigue fracture problem

Mechanical fatigue of solar cell interconnects is a major failure mechanism in photovoltaic arrays. A comprehensive approach to the reliability design of interconnects, together with extensive design data for the fatigue properties of copper interconnects, has been published. This paper extends the previous work, developing failure prediction (fatigue) data for additional interconnect material choices, including aluminum and a variety of copper-Invar and copper-steel claddings. An improved global fatigue function is used to model the probability-of-failure statistics of each material as a function of level and number of cycles of applied strain. Life-cycle economic analyses are used to evaluate the relative merits of each material choce. The copper-Invar clad composites demonstrate superior performance over pure copper. Aluminum results are disappointing.

Mon, G. R.↗

NASA NTRS1981

Defect design of insulation systems for photovoltaic modules

A defect-design approach to sizing electrical insulation systems for terrestrial photovoltaic modules is presented. It consists of gathering voltage-breakdown statistics on various thicknesses of candidate insulation films where, for a designated voltage, module failure probabilities for enumerated thickness and number-of-layer film combinations are calculated. Cost analysis then selects the most economical insulation system. A manufacturing yield problem is solved to exemplify the technique. Results for unaged Mylar suggest using fewer layers of thicker films. Defect design incorporates effects of flaws in optimal insulation system selection, and obviates choosing a tolerable failure rate, since the optimization process accomplishes that. Exposure to weathering and voltage stress reduces the voltage-withstanding capability of module insulation films. Defect design, applied to aged polyester films, promises to yield reliable, cost-optimal insulation systems.

Mon, G. R.↗