DOE OSTI2020

Combined Spatially Resolved Characterization of Antireflection and Antisoiling Coatings for PV Module Glass

Characterization of photovoltaic (PV) module materials throughout different stages of service life is crucial to understanding and improving the durability of these materials. Currently the large-scale of PV modules (>1 m 2 ) is imbalanced with the small-scale of most materials characterization tools (= 1 cm 2 ). Furthermore, understanding degradation mechanisms often requires a combination of multiple characterization techniques. Here, we present adaptations of three standard materials characterization techniques to enable mapping characterization over moderate sample areas (=25 cm 2 ). Contact angle, ellipsometry, and UV-Vis spectroscopy are each adapted and demonstrated on two representative samples: a commercial multi-functional coating for PV glass and an oxide combinatorial sample library. Best practices are discussed for adapting characterization techniques for large area mapping and combining mapping information from multiple techniques.

14 SOLAR ENERGY↗

DOE OSTI2020

Correlation of Advanced Accelerated Stress Testing with Polyamide-Based Photovoltaic Backsheet Field-Failures

Cracking of polyamide (PA)-based photovoltaic (PV) backsheet materials has been widely reported for field-aged modules. Failure was not detected by conventional accelerated stress tests (ASTs), which lacked the necessary combination of stress factors and/or factor sequences. PA-based AAA backsheet cracking has since been reproduced through combined and sequential stress testing. Planar- and cross-sectional-optical microscopy as well as Fourier-transform Infrared Spectroscopy (FTIR), have been used to elucidate the mechanical and chemical changes which lead to failure of the backsheet. Field-aged backsheet samples demonstrating failure in various climates (including locations in China and Italy) are also analyzed. Through the analysis, a comparison is made between the different stress testing protocols and the field-aged samples to validate relevance of the advanced stress tests. It is shown that the changes induced through combined-accelerated stress testing (C-AST) were most representative of changes induced by the field, supporting the relevance of C-AST and providing validity for the test protocol.

14 SOLAR ENERGY↗

DOE OSTI2020

Understanding PV Polymer Backsheet Degradation through X-Ray Scattering

Understanding how photovoltaic (PV) module backsheet polymers age and degrade in response to environmental stresses is important for designing polymers that can maintain their structural integrity after decades of outdoor use. X-ray scattering is a powerful technique for exploring backsheet polymer structure at the angstrom- (wide-angle, WAXS) and nanometer- (small-angle, SAXS) length-scales. We present the use of SAXS and WAXS to study pristine and aged polymer backsheets. The structural insight from these techniques can be used to compare the degradation induced by accelerated testing with the degradation seen in field-aged PV materials.

14 SOLAR ENERGY↗