Phosphorus incorporated into epoxies and polyamides via curing agent. According to report, use of 1-(di(2-chloroethoxyphosphinyl)methyl)-2,4- and -2,6-diaminobenzene (DCEPD) as curing agent for epoxies and polyamides makes these polymers more fire-retardant than corresponding polymers made with standard curing agents not containing phosphorus.
Report describes testing of commercial and experimental fire retardants for incorporation into acrylic printing inks used on aircraft-interior sandwich panels. Films of acrylic ink containing fire-retardant additives prepared by casting on glass plates. Solvent evaporated in vacuum, cast films cured at 80 to 100 degree C for 30 minutes in air-circulating oven. Thermochemical properties of films examined by thermogravimetric analysis and differential scanning calorimetry (DSC). Samples of inks cast on sheets of polyvinylfloride (PVF), and their limiting oxygen indices and smoke evolution measured.
1-(Diorganooxyphosphonyl)methyl2,4- and-2,6diamino benzenes are reacted with polyacylhalides and optionally comonomers to produce polyamides which have desirable heat and fire resistance properties. These polymers are used to form fibers and fabrics where fire resistance properties are important, e.g., aircraft equipment and structures.
A phosphonyl methyl benzene is prepared by nitration to produce a 2,4-dinitro phosphonyl methyl benzene, which is then reduced to a diamino compound. The diamino compound is then used to cure a polymerizable monomer. The diamino compound may be polymerized with polyfunctional epoxides to produce heat and fire resistant polymer structures for making flame and fire resistant polymer structures such as for aircraft secondary structures.
Commercial and experimental fire retardants were screened as potential fire retardants for acrylic printing inks used on aircraft interior sandwich panels. The fire retardants are selected according to their physical properties and their thermostabilities. A criterion for selecting a more stable fire retardant is established. Thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) are used to determine thermostabilities. Results show that the fire retardant formulations are more thermally stable than the acrylic ink control. It is determined that an ink formulation containing a brominated phenol and carboxy-terminated butadiene acrylonitrile which has been modified with a brominated polymeric additive (BPA), yields the highest limiting oxygen index (LOI) of all the compounds tested. All of the fire-retardant formulations have a higher oxygen index than the baseline acrylic ink.
Phosphorus-containing polyimides and copolyimides are synthesized in a two-step polycondensation reaction from 1- (diorganooxyphosphonl)methly 2,4- and 2,6-diaminobenzenes and tetracarboxylic anhydride. The diorgano position of the diorganooxyphosphonyl group includes alkyl, such as ethyl, substituted alkyl, such as 2-chloroethyl, and aryl such as phenyl. The tetracarboxylic anhydries include compounds such as pyrometallitic dianhydride and benzophenone tetracarboxylic dianhydride. The glass transition temperature (Tg) of the polyimides is reduced by incorporation of the (dialkoxyphosphonyl)methyl groups. The phosphorus-containing copolyimides show a considerably higher degree of fire-resistance as compared to that of the corresponding common polyimides.
Epoxy with increased resistance to fire made by reacting any of three commercial epoxide monomers with curing agent consisting of mixture of isomers called "DCEPD". Curing agent incorporates phosphorus and chlorine directly into crosslinking part of polymer. DCEPD produced by nitrating precursor phosphonylmethyl benzene, then reducing resulting isomeric mixture of dinitro compounds.
Phosphorus containing polyamides and copolyamides were prepared from 1-(dialkoxyphosphinyl)methyl-2,4- and -2,6-diaminobenzenes. The polymers produced were characterized by infrared and proton nuclear magnetic resonance spectroscopy, differential scanning calorimetry, and thermogravimetric analysis. Their thermal properties were compared with those of the corresponding common polyamides. In addition, by determining the limiting oxygen index value of some of these polyamides, their fire resistance was evaluated.
Commercial and experimental fire retardants were screened for possible use wiith acrylic printing inks on aircraft interior sandwich panels. The fire retardants were selected according to their physical properties and thermostabilities. Thermostabilities were determined by thermogravimetric analysis and differential scanning calorimetry. A criterion was then established for selecting the more stable agent. Results show that some of the bromine-containing fire retardants are more thermostable than the acrylic ink, alone, used as a control. Also, the bromine-containing fire retardants yield even better limiting oxygen index values when tested after adding carboxy-terminated butadiene acrylonitrile (CTBN) rubber.
Fire resistant compositions were prepared using 1-di(2-chloroethoxy-phosphinyl)methyl-2,4- and -2,6-diaminobenzene (DCEPD) as a curing agent for typical epoxy resins such as EPON 828 (Shell), XD 7342 (Dow), and My 720 (Ciba Geigy). In addition, compositions of these three epoxy resins with common curing agents such as m-phenylenediamine (MPD) or 4,4'-diaminodiphenylsulphone (DDS) were studied to compare their reactions with those of DCEPD. The reactivity of the three curing agents toward the epoxy resins, measured by differential calorimetry (DSC), was of the order MPD DCEPD DDS. The relatively lower reactivity of DCEPD toward epoxy resins was attributed to electronic effects.
Phosphorus containing polyamides and copolyamides were prepared from 1-(dialkoxyphosphinyl)methyl-2,4- and -2,6-diaminobenzenes. The polymers produced were characterized by infrared and proton nuclear magnetic resonance spectroscopy, differential scanning calorimetry, and thermogravimetric analysis. Their thermal properties were compared with those of the corresponding common polyamides. In addition, by determining the limiting oxygen index value of some of these polyamides, their fire resistance was evaluated.
Fire resistant compositions were prepared using 1-di(2-chloroethoxy-phosphinyl)methyl-2,4- and -2,6-diaminobenzene (DCEPD) as a curing agent for typical epoxy resins such as EPON 828 (Shell), XD 7342 (Dow), and My 720 (Ciba Geigy). In addition, compositions of these three epoxy resins with common curing agents such as m-phenylenediamine (MPD) or 4,4'-diaminodiphenylsulphone (DDS) were studied to compare their reactions with those of DCEPD. The reactivity of the three curing agents toward the epoxy resins, measured by differential calorimetry (DSC), was of the order MPD DCEPD DDS. The relatively lower reactivity of DCEPD toward epoxy resins was attributed to electronic effects.