NASA NTRS1998

TMC Behavior Modeling and Life Prediction Under Multiaxial Stresses

The goal of this program was to manufacture and burst test small diameter SCS-6/Ti-6Al-4V composite rings for use in the design of an advanced titanium matrix composite (TMC) impeller. The Textron Specialty Metals grooved foil-fiber process was successfully used to make high quality TMC rings. A novel spin test arbor with "soft touch" fingers to retain the TMC ring was designed and manufactured. The design of the arbor took into account its use for cyclic experiments as well as ring burst tests. Spin testing of the instrumented ring was performed at ambient, 149C (300F), and 316C (600F) temperatures. Assembly vibration was encountered during spin testing but this was overcome through simple modification of the arbor. A spin-to-burst test was successfully completed at 316C (600F). The rotational speed of the TMC ring at burst was close to that predicted. In addition to the spin test program, a number of SCS-6/Ti-6Al-4V test panels were made. Neat Ti-6Al-4V panels also were made.

Merrick, H. F.↗

NASA NTRS1998

Simulated Bladed MMC Disk LCF Validation

The goal of this program was to evaluate the low cycle fatigue behavior of an SCS-6/Ti-6Al-4V sub-component under bi-axial loading conditions at 316 C(600 F). A simulated bladed TMC disk was designed having thirty four blades representing the number that would be used in Allied Signal's JTAGG II impeller. The outer diameter of the bladed ring was 254 mm (10.0 inch) and the inner diameter 114.3 mm (4.50 inch). The outer and inner diameter of the composite zone was 177.8 mm (7.00 inch) and 127.O mm(5.00 inch) respectively. Stress analysis showed that the fatigue life of the bladed composite ring would be about 12000 cycles for the test conditions applied. A modal analysis was conducted which showed that the blades would have sufficient life margin from dynamic excitation. The arbor design was the same as that employed in the spin-to burst test of NAS3-27027. A systematic stress analysis of each part making up the arbor was undertaken to assure the design would meet the low cycle fatigue requirements of the program. The Textron Systems grooved foil-fiber process was chosen to make the SCS-6/Ti-6Al-4V core ring based on the success they had in contract NAS3-27027. Fiber buckling, however, was observed at several locations in the first ring made which rendered it unsuitable for spin testing. The fiber buckling was attributed to cracking of the graphite tooling during the consolidation process. On this basis a second ring was made but it too contained fiber buckling defects. Analysis by Textron indicated that the fiber buckling was most likely due to poor placement of the SCS-6 fiber in the etched grooves of the Ti-6Al-4V foil. This was also a contributor to the defects in the first ring. Since there was little indication of control in the process to manufacture a quality ring a third attempt at making a ring was not undertaken.

Merrick, H. F.↗

NASA NTRS1981

Oxide dispersion strengthened superalloy

MA6000E alloy is strengthened at high temperatures by dispersion of yttrium oxide. Strength properties are about twice those of conventional nickel base alloys. Good thermal fatigue, intermediate temperature strength, and good oxidation resistance give alloy unique combination of benefits. Application in aircraft gas turbine is improved.

Glasgow, T. K.↗

NASA NTRS1980

Fatigue properties of MA 6000E, a gamma-prime strengthened ODS alloy

MA 6000E is a corrosion resistant, gamma-prime strengthened ODS alloy under development for advanced turbine blade applications. The high temperature, 1093 C, rupture strength is superior to conventional nickel-base alloys. This paper addresses the fatigue behavior of the alloy. Excellent properties are exhibited in low and high cycle fatigue and also thermal fatigue. This is attributed to a unique combination of microstructural features, i.e., a fine distribution of dispersed oxides and other nonmetallics, and the highly elongated grain structure which advantageously modify the deformation characteristics and crack initiation and propagation modes from that characteristic of conventional gamma-prime hardened superalloys.

Kim, Y. G.↗

NASA NTRS1979

Characterization of an oxide dispersion strengthened superalloy, MA-6000E, for turbine blade applications

Alloy MA 6000E was developed by the mechanical alloying process for turbine blade applications. The nominal composition of the experimental alloy is Ni-15CR-2Mo-4W-4.5Al- 2.5Ti-2Ta- .15Zr-.05C-.01B-1.1Y2O3. The 1000 hour rupture strength in the longitudinal direction is about 145 MPa at 1093 C and about 483 MPa at 760 C. The alloy displays normal three-stage creep behavior. Typically the creep elongation is 3.5% at 760 C and 2% at 1093 C. The alloy is notch ductile (K sub 1 = 3.5). The rupture properties of the alloy are not significantly degraded by thermal cycling or prior stress isothermal exposure. The alloy also has excellent longitudinal high and low cycle fatigue resistance. Limited testing indicates that MA 6000E posesses good off-axis mechanical properties. The transverse tensile elongation at 760 C is about 3%. The 100 hour transverse rupture strength is 331 MPa at 760 C and about 55 MPa at 1093 C.

Kim, Y. G.↗

NASA NTRS1977

Development of oxide dispersion strengthened turbine blade alloy by mechanical alloying

There were three nickel-base alloys containing up to 18 wt. % of refractory metal examined initially for oxide dispersion strengthening. To provide greater processing freedom, however, a leaner alloy was finally selected. This base alloy, alloy D, contained 0.05C/15Cr / 2Mo/4W/2Ta/4.5Al/2.Ti/015Zr/0.01-B/Bal. Ni. Following alloy selection, the effect of extrusion, heat treatment, and oxide volume fraction and size on microstructure and properties were examined. The optimum structure was achieved in zone annealed alloy D which contained 2.5 vol. % of 35 mm Y2O3 and which was extruded 16:1 at 1038 C.

Merrick, H. F.↗