DOE OSTI2024

Measuring the density, viscosity, and surface tension of molten titanates using electrostatic levitation in microgravity

Rare earth and barium titanates are useful as ferroelectric, dielectric, and optical materials. Measurements of their thermophysical properties in the liquid state can help guide melt processing technologies for their manufacture and advance understanding of fragile liquids' behavior and glass formation. Here, we report the density, thermal expansion, viscosity, and surface tension of molten BaTi 2 O 5 , BaTi 4 O 9 , and 83TiO 2 -17RE 2 O 3 (RE = La or Nd). Measurements were made using electrostatic levitation and droplet oscillation techniques in microgravity, which provide access to quiescent liquid droplets and deep supercooling of 510–815 K below the equilibrium melting points. Densities were measured over 900–2400 K. Viscosities were similar for all four compositions, increasing from ~10 mPa s near 2100 K to ~30 mPa s near 1750 K. Surface tensions were 450–490 dyn cm -1 for the rare earth titanates and 383–395 dyn cm -1 for the barium titanates; surface tensions of all compositions had small or negligible temperature dependence over 1700–2200 K. In conclusion, for solids recovered after melt quenching, x-ray microtomography revealed the fracture mechanics in crystalline products and minimal internal porosity in glass products, likely arising from entrapped gas bubbles. Internal microstructures were generally similar for products processed either in microgravity or in a terrestrial aerodynamic levitator.

42 ENGINEERING↗

DOE OSTI2024

Microgravity effects on nonequilibrium melt processing of neodymium titanate: thermophysical properties, atomic structure, glass formation and crystallization

The relationships between materials processing and structure can vary between terrestrial and reduced gravity environments. As one case study, we compare the nonequilibrium melt processing of a rare-earth titanate, nominally 83TiO 2 -17Nd 2 O 3 , and the structure of its glassy and crystalline products. Density and thermal expansion for the liquid, supercooled liquid, and glass are measured over 300–1850 °C using the Electrostatic Levitation Furnace (ELF) in microgravity, and two replicate density measurements were reproducible to within 0.4%. Cooling rates in ELF are 40–110 °C s -1 lower than those in a terrestrial aerodynamic levitator due to the absence of forced convection. X-ray/neutron total scattering and Raman spectroscopy indicate that glasses processed on Earth and in microgravity exhibit similar atomic structures, with only subtle differences that are consistent with compositional variations of ~2 mol. % Nd 2 O 3 . The glass atomic network contains a mixture of corner- and edge-sharing Ti-O polyhedra, and the fraction of edge-sharing arrangements decreases with increasing Nd 2 O 3 content. X-ray tomography and electron microscopy of crystalline products reveal substantial differences in microstructure, grain size, and crystalline phases, which arise from differences in the melt processes.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Mid-infrared luminescence properties of erbium and dysprosium doped lanthanum titanate glasses

Glasses of composition x RE 2 O 3 -(17− x ) La 2 O 3 -83 TiO 2 were prepared by levitation melting from x = 0.1 to 9 for RE=Er and at x =0.1 and 1 for RE=Dy. The glasses have high transition temperature, exhibit low OH, and 1 mm thick discs are transparent out to 6 μ m. Mid-infrared emission lineshapes and lifetimes are comparable to what is seen in tellurite glasses containing Er 3+ and Dy 3+ . For x fixed at 1, the Er 3+ : 4 I 11/2 → 4 I 13/2 transition at 2716 nm has a fluorescence lifetime of 254 μ s and the Dy 3+ : 6 H 13/2 → 6 H 15/2 transition at 2957 nm has a fluorescence lifetime of 9.09 μ s. The results indicate that doped lanthanum titanate glasses offer the thermal stability of a ’hard’ glass with the host properties typically associated with ’soft’ glasses. Problems with the measurement of spectral features in the mid-infrared that could erroneously be assigned as resulting from rare-earth ion emissions are presented and discussed.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Revisiting metastable immiscibility in SiO 2 –Al 2 O 3 : Structure and phase separation of supercooled liquids and glasses

Understanding and controlling liquid–liquid phase separation in aluminosilicates is crucial for optimizing glass properties. However, the metastable nature of aluminosilicates’ phase separation has made it difficult to study experimentally, and uncertainty persists regarding the compositional and temperature extents of the miscibility gap. Here, we present new experimental evidence that suggests a consolute temperature between 1440 and 1590°C and endmember compositions of 7 and 62 mol.% Al 2 O 3 for the phase-separated glasses. Using containerless melt processing, deeply supercooled liquids over the 0–60 mol.% Al 2 O 3 range are probed with in situ small- and wide-angle X-ray scattering, which simultaneously reveals changes in nanoscale density heterogeneity and atomic structure. Correlations between phase separation and atomic coordination environments are compared for liquids and glasses. Pair distribution function analysis shows mean O–(Si + Al) coordination increases with Al 2 O 3 content and decreases with temperature.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Phase separation in mullite-composition glass

Aluminosilicates (AS) are ubiquitous in ceramics, geology, and planetary science, and their glassy forms underpin vital technologies used in displays, waveguides, and lasers. In spite of this, the nonequilibrium behavior of the prototypical AS compound, mullite (40SiO 2 -60Al 2 O 3 , or AS60), is not well understood. By deeply supercooling mullite-composition liquid via aerodynamic levitation, we observe metastable liquid–liquid unmixing that yields a transparent two-phase glass, comprising a nanoscale mixture of AS7 and AS62. Extrapolations from X-ray scattering measurements show the AS7 phase is similar to vitreous SiO 2 with a few Al species substituted for Si. The AS62 phase is built from a highly polymerized network of 4-, 5-, and 6-coordinated AlO x polyhedra. Polymerization of the AS62 network and the composite morphology provide essential mechanisms for toughening the glass.

36 MATERIALS SCIENCE↗