STUDIES ON PIPELINE POLYETHYLENES IN HYDROGEN GAS ENVIRONMENTS USING IN-SITU AND EX-SITU CHARACTERIZATION METHODS

Polymeric materials are commonplace in the natural gas infrastructure as distribution pipes, coatings, seals, and gaskets. Under the auspices of the U.S. Department of Energy HyBlend program, one of the means to reduce greenhouse gas emissions is with replacing natural gas, either partially or completely, with hydrogen. This approach makes it imperative that we conduct near-term and long-term materials compatibility research in these relevant environments. Insights into the effects of hydrogen and hydrogen gas blends on polymer integrity can be gained through both ex-situ and in-situ analytical methods. Our work represented here highlights a study of the behavior of pipeline polyethylene (PE) materials, including HDPE (Dow 2490 and GDB50) and MDPE (Ineos and legacy Dupont Aldyl A), when exposed to hydrogen by means of in-situ X-ray scattering and ex-situ Raman spectroscopy techniques. Samples were tested in ex-situ hydrogen and argon gas environments and in-situ hydrogen environments to identify differences due to permeation and solubility of these gases. These methods complemented each other because Raman spectroscopy could capture permanent effects after materials were removed from gaseous environments, and in-situ X-ray scattering analysis collected real-time data to elucidate the impact of the gas environment on polymer microstructure. Data collected revealed that the aforementioned polymers did not show significant changes in crystallinity and microstructure under the exposure conditions tested. Our findings from these studies will help establish real-time effects caused by hydrogen gas transport through pipeline polyethylenes by way of its influence on polymer structure and chemistry, which is directly related to pipeline mechanical strength and longevity of service.

Hydrogen materials compatibility, Natural gas pipe↗

DOE OSTI2024

In-Situ and Ex-Situ Studies on the Morphology Changes of Polymer Pipeline Materials for Use in Hydrogen Gas Environments

The US natural gas infrastructure is a national asset that could be used to deliver hydrogen and hydrogen blends of natural gas as a pathway to reduce carbon emissions. The distribution system comprises nearly 50% plastic pipe composed of medium- and high-density polyethylene materials (MDPE and HDPE). While these materials perform adequately for natural gas, research on their hydrogen compatibility is essential to understand if any immediate and long-term risks are associated with hydrogen addition. The Blended Gas CRADA, a HyBlend project, has established a comprehensive test method for evaluating MDPE and HDPE of various plastic resin compositions of pipeline material in pure hydrogen and 20% hydrogen/80% methane blends. Both in-situ and ex-situ measurements were performed to capture hydrogen-induced changes in the polyethylene material's crystalline, amorphous and their interphase regions. We investigated MDPE and HDPE pipeline materials made from different polymer resin systems to evaluate the effects of hydrogen gas. The materials were characterized by their density, diffusion coefficient, free volume ratio, and degree of crystallinity. Various advanced characterization methods, including in situ NMR, ex situ XRD, ex situ DSC, and ex situ TDA, were used to analyze the effects of changes in crystalline, amorphous, and interphase regions due to gas exposure. Time-dependent post-decompression quasi-static tensile tests were conducted to explore the effects of gas exposure time on the mechanical behavior of the pipe materials. This work will highlight the time sensitivities during and after gas exposure. The correlation between gas-induced polyethylene morphology changes and the associated material performance will be addressed for the intended applications. These studies will show that polyethylene resin composition and material exposure are important factors when considering whether hydrogen gas affects pipeline materials positively or negatively.

Simmons, Kevin L.↗

DOE OSTI2024

Evaluation of Common Thermoplastic Polymers in High-Pressure Cycling Hydrogen Under Ambient and Cold Environments as Applicable to the Hydrogen Infrastructure

Thermoplastic polymers are required to perform unfailingly under stringent conditions of changing pressures (35 MPa to 70 MPa) and temperatures (-40°C to +85°C) in storage and fueling operations. Although diffusivity in glassy polymers appear to be an order of magnitude lower than elastomers, polymer microstructural attributes such as degree of crystallinity and presence of polar and non-polar groups on the main chain with and without branching can play a substantial role in influencing their behaviors in hydrogen environments. In the work described here, the effect of high-pressure hydrogen cycling on PEEK, PTFE, PA11, HDPE, POM (and different commercial grades of these polymers) under ambient and cold (-40°C) conditions is addressed. Ex-situ characterization for polymer changes included density measurements for impact of hydrogen retention, hardness changes using nanoindentation, storage modulus and glass transition changes using dynamic mechanical and thermal analysis (DMTA), degree of crystallization with Differential Scanning Calorimetry (DSC) and tensile testing following ASTM D412. In other evaluations, solid-state nuclear magnetic resonance (NMR), attenuated total reflectance Fourier transform infra-red spectroscopy (ATRFTIR), X-ray diffraction (XRD), and X-ray CT results are presented. The overall impact of these evaluations is to establish a technical basis for the behaviors of common thermoplastics in cycling hydrogen environments under ambient and cold temperatures while establishing the relationship between polymer structure-based properties and hydrogen transport effects.

Menon, Nalini C.↗

DOE OSTI2023

A diffusion–deformation model with damage for polymer undergoing rapid decompression failure

Green hydrogen is emerging as one of the most promising alternatives to replace fossil fuels. While hydrogen gas has a good energy density by weight, its poor energy density by volume requires it to be stored under high pressure for commercial use. The hydrogen infrastructure developed to handle this high pressure hydrogen contains multiple components made of polymers as sealing agents. Although polymers do not react chemically with hydrogen gas, they undergo a mechanical failure when high pressure hydrogen gas is suddenly depressurized. This phenomenon known as 'rapid decompression failure' occurs due to the diffusion of hydrogen through polymer and getting trapped inside pre-existing cavities or voids. Here, in this paper, a continuum mechanics-based coupled diffusion-deformation-damage model was developed to predict the hydrogen distribution, stress distribution, and damage propagation inside the polymer while it undergoes rapid decompression failure. The polymer was modeled as a hyperelastic material because it represents the nonlinear material response observed in uniaxial tensile tests perfectly. The effects of hydrogen diffusivity, pre-existing cavity size, cavity location, applied hydrogen pressure, and depressurization rate on damage initiation were studied. It was found that the coefficient of diffusion plays an important role in damage initiation and damage was mostly concentrated in the inside areas rather than near the surface. Experiments were conducted with EPDM polymer which agreed well with the predicted trends using the given model. The effect of adding carbon black and silica filler particles and plasticizer to the pure EPDM polymer was also studied. It was found that damage during RDF decreases with the addition of fillers, but increases with the addition of the plasticizer. Finally, the damage evolution in the presence of two cavities was also studied, and was found that the interaction of stress fields around the cavities alters the damage occurring during RDF.