Combinatorial Synthesis of Cation-Disordered Manganese Tin Nitride MnSnN 2 Thin Films with Magnetic and Semiconducting Properties
Not Available
Engineering topics
Publications and source records attributed to Melamed, Celeste L..
Not Available
Local site ordering offers a new paradigm for property control in functional materials. However, systems that exhibit a propensity for local order and global disorder are often challenging to characterize, and demonstrations of ordering-induced property tuning are few and far between. Here, we demonstrate that short-range ordering tunes the optical absorption edge in the long-range disordered alloy system (ZnSnN2)1-x(ZnO)2x at x = 0.25. We use combinatorial cosputtering to synthesize a set of thin-film samples spanning this alloy space. X-ray diffraction demonstrates lattice contraction as a function of alloy composition, confirming that a mixed-anion and -cation alloy has been synthesized. Using N and O K-edge X-ray absorption near-edge structure in conjunction with simulations of cation-disordered supercell structures, we find that samples exhibit octet-rule-breaking motifs around both anions. Upon annealing at an alloy composition of x = 0.25, X-ray absorption analysis suggests that local motif structure shifts toward octet-rule-conserving while long-range disorder is maintained. Spectroscopic ellipsometry reveals that local ordering increases the absorption edge energy at constant composition. Additionally, alloy-induced optical absorption edge tuning is demonstrated. This work paves the way toward property tuning with short-range ordering in (ZnSnN2)1-x(ZnO)2x and beyond.
In this work, we demonstrate that the surface layers of single-crystal layered-2D Bi 2 Se 3 can be converted to layered-2D rhombohedral ß-In 2 Se 3 by annealing under a trimethylindium (TMIn) flux. Samples were prepared in a metalorganic chemical vapor deposition (MOCVD) chamber, then transferred under vacuum to a surface analysis chamber for analysis with low-energy electron diffraction (LEED) and Auger electron spectroscopy. Additional ex situ characterization included x-ray diffraction, transmission-electron microscopy (TEM), energy dispersive x-ray spectroscopy (EDS) elemental mapping, and Raman spectroscopy. The resulting single-crystal ß-In 2 Se 3 adopts the rhombohedral crystal structure (space group R-3m) and orientation of the underlying Bi 2 Se 3 , and the excess Bi atoms generated by this process create an underlying region of Bi-rich Bi x Se y . Due to the difference in bandgap between Bi 2 Se 3 and In 2 Se 3 , this conversion reaction presents a pathway to lateral heterojunctions if only selected regions are converted by masking the surface to spatially define the TMIn exposure. The conversion may also have implications for heteroepitaxy, because the in-plane lattice constants of Bi 2 Se 3 and In 2 Se 3 (0001) surfaces match those of InP and GaAs (111), respectively, and the natural cleavage planes of a layered-2D crystal facilitate substrate removal and reuse.
Interest in inorganic ternary nitride materials has grown rapidly over the past few decades, as their diverse chemistries and structures make them appealing for a variety of applications. Due to synthetic challenges posed by the stability of N 2 , the number of predicted nitride compounds dwarfs the number that have been synthesized, offering a breadth of opportunity for exploration. This review summarizes the fundamental properties and structural chemistry of ternary nitrides, leveraging metastability and the impact of nitrogen chemical potential. A discussion of prevalent defects, both detrimental and beneficial, is followed by a survey of synthesis techniques and their interplay with metastability. Throughout the review, we highlight applications (such as solid-state lighting, electrochemical energy storage, and electronic devices) in which ternary nitrides show particular promise.
Cation-disordered ZnGeN 2 shows promise for application as a blue-green emitter in light-emitting devices, but more foundational work is necessary to understand structure–property relationships. In this work, we present a combinatorial exploration of the experimental phase space of wurtzite (cation-disordered) ZnGeN 2 using high-throughput co-sputtering. Structure, morphology and optical properties are explored as a function of cation composition and synthesis temperature. ZnGeN 2 is found to crystallize in the wurtzite structure ranging from Zn-rich to Ge-rich compositions. X-ray diffraction refinements reveal a continuous shift in cell volume with off-stoichiometry, indicating alloy-like structural behavior. Furthermore, the optical absorption of all films examined is lower in energy than the value predicted for cation-ordered ZnGeN 2 , suggesting that cation disorder is decreasing the bandgap. Additionally, the absorption threshold shifts continuously to higher energy for Ge-rich samples, consistent with bandgap shifts due to alloy-like structural behavior. Defect formation energy diagrams are calculated to help guide understanding of off-stoichiometry from a defect complex perspective. This work paves the way toward use of ZnGeN 2 as a bandgap-tunable optoelectronic semiconductor.
We report controlling site disorder in ternary and multinary compounds enables tuning optical and electronic properties at fixed lattice constants and stoichiometries, moving beyond many of the challenges facing binary alloy systems. Here, we consider possible enhancements to energy-related applications through the integration of disorder-tunable materials in devices such as light-emitting diodes, photonics, photovoltaics, photocatalytic materials, batteries, and thermoelectrics. However, challenges remain in controlling and characterizing disorder. Focusing primarily on II–IV–V 2 materials, we identify three metrics for experimentally characterizing cation site disorder. Complementary to these experiments, we discuss simulation methods to understand disordered materials. Nonidealities, such as off-stoichiometry and oxygen incorporation, can occur while synthesizing metastable disordered materials. While nonidealities may seem undesirable, we describe how if harnessed they could provide another knob for tuning disorder and subsequently properties. To illustrate the effects of disorder on device-relevant properties, we provide case examples of disordered materials and their potential in device applications.
II–IV–V 2 materials, ternary analogs to III–V materials, are emerging for their potential applications in devices such as LEDs and solar cells. Controlling cation ordering in II–IV–V 2 materials offers the potential to tune properties at nearly fixed compositions and lattice parameters. While tuning properties at a fixed lattice constant through ordering has the potential to be a powerful tool used in device fabrication, cation ordering also creates challenges with characterization and quantification of ordering. In this work, we investigate two different methods to quantify cation ordering in ZnGeP 2 thin films: a stretching parameter calculated from lattice constants , and an order parameter determined from the cation site occupancies ( S ). We use high resolution X-ray diffraction (HRXRD) to determine and resonant energy X-ray diffraction (REXD) to extract S . REXD is critical to distinguish between elements with similar Z -number ( e.g. Zn and Ge). We found that samples with a corresponding to the ordered chalcopyrite structure had only partially ordered S values. The optical absorption onset for these films occurred at lower energy than expected for fully ordered ZnGeP 2 , indicating that S is a more accurate descriptor of cation order than the stretching parameter. Since disorder is complex and can occur on many length scales, metrics for quantifying disorder should be chosen that most accurately reflect the physical properties of interest.
This article demonstrates the successful growth of cubic GaAs (111) on single-crystal 2D layered Bi 2 Se 3 (0001) substrates achieved using a cubic ZnSe buffer layer. This growth sequence was chosen based upon observed reactions between Bi 2 Se 3 (0001) substrates and both Ga and Zn. For the conditions used in our MOCVD reactor, triethylgallium (TEGa) interacts strongly with Bi 2 Se 3 to form Ga 2 Se 3 , which can disrupt the nucleation and growth of GaAs. Therefore, a buffer layer is needed which prevents Ga-Bi 2 Se 3 interactions while simultaneously providing a suitable growth surface for GaAs. ZnSe was chosen because it is lattice-matched to GaAs, and can be created by annealing the Bi2Se3 under a diethylzinc (DEZn) flux. A sample utilizing this growth sequence has been grown, characterized and exfoliated as a possible pathway toward reducing the substrate cost for III-V devices such as solar cells.
Not Available
Inorganic nitrides with wurtzite crystal structures are well-known semiconductors used in optical and electronic devices. In contrast, rocksalt-structured nitrides are known for their superconducting and refractory properties. Breaking this dichotomy, here we report ternary nitride semiconductors with rocksalt crystal structures, remarkable electronic properties, and the general chemical formula Mg x TM 1−x N ( TM = Ti, Zr, Hf, Nb). Our experiments show that these materials form over a broad metal composition range, and that Mg-rich compositions are nondegenerate semiconductors with visible-range optical absorption onsets (1.8 to 2.1 eV) and up to 100 cm 2 V −1 ⋅s −1 electron mobility for MgZrN 2 grown on MgO substrates. Complementary ab initio calculations reveal that these materials have disorder-tunable optical absorption, large dielectric constants, and electronic bandgaps that are relatively insensitive to disorder. These ternary Mg x TM 1−x N semiconductors are also structurally compatible both with binary TM N superconductors and main-group nitride semiconductors along certain crystallographic orientations. Overall, these results highlight Mg x TM 1−x N as a class of materials combining the semiconducting properties of main-group wurtzite nitrides and rocksalt structure of superconducting transition-metal nitrides.
Combinatorial experiments involve synthesis of sample libraries with lateral composition gradients requiring spatially-resolved characterization of structure and properties. Here, due to maturation of combinatorial methods and their successful application in many fields, the modern combinatorial laboratory produces diverse and complex data sets requiring advanced analysis and visualization techniques. In order to utilize these large data sets to uncover new knowledge, the combinatorial scientist must engage in data science. For data science tasks, most laboratories adopt common-purpose data management and visualization software. However, processing and cross-correlating data from various measurement tools is no small task for such generic programs. Here we describe COMBIgor, a purpose-built open-source software package written in the commercial Igor Pro environment, designed to offer a systematic approach to loading, storing, processing, and visualizing combinatorial data sets. It includes (1) methods for loading and storing data sets from combinatorial libraries, (2) routines for streamlined data processing, and (3) data analysis and visualization features to construct figures. Most importantly, COMBIgor is designed to be easily customized by a laboratory, group, or individual in order to integrate additional instruments and data-processing algorithms. Utilizing the capabilities of COMBIgor can significantly reduce the burden of data management on the combinatorial scientist.
Emerging photovoltaic materials need to prove their viability by demonstrating excellent electronic properties. In ternary and multinary semiconductors, disorder and off-stoichiometry often cause defects that limit the potential for high-efficiency solar cells. We report on Zn-rich ZnSnN 2 (Zn/(Zn + Sn) = 0.67) photoluminescence, high-resolution X-ray diffraction, and electronic structure calculations based on Monte-Carlo structural models. The mutual compensation of Zn excess and O incorporation affords a desirable reduction of the otherwise degenerate n-type doping, but also leads to a strongly off-stoichiometric and disordered atomic structure. It is therefore remarkable that we observe only near-edge photoluminescence from well-resolved excitons and shallow donors and acceptors. Based on first principles calculations, this result is explained by the mutual passivation of Zn Sn and O N defects that renders both electronically benign. The calculated bandgaps range between 1.4 and 1.8 eV, depending on the degree of non-equilibrium disorder. The experimentally determined value of 1.5 eV in post-deposition annealed samples falls within this interval, indicating that further bandgap engineering by disorder control should be feasible via appropriate annealing protocols.
In this paper, we present an exfoliation method that produces cm 2 -area atomically flat surfaces from bulk layered single crystals, with broad applications such as for the formation of lateral heterostructures and for use as substrates for van der Waals epitaxy. Single crystals of Bi 2 Se 3 were grown using the Bridgman method and examined with X-ray reciprocal space maps, Auger spectroscopy, low-energy electron diffraction, and X-ray photoelectron spectroscopy. An indium-bonding exfoliation technique was developed that produces multiple ~100 um thick atomically flat, macroscopic (>1 cm 2 ) slabs from each Bi 2 Se 3 source crystal. Two-dimensional X-ray diffraction and reciprocal space maps confirm the high crystalline quality of the exfoliated surfaces. Atomic force microscopy reveals that the exfoliated surfaces have an average root-mean-square (RMS) roughness of ~0.04 nm across 400 μm 2 scans and an average terrace width of 70 um between step edges. First-principles calculations reveal exfoliation energies of Bi 2 Se 3 and a number of other layered compounds, which demonstrate relevance of our method across the field of 2D materials. While many potential applications exist, excellent lattice matching with the III-V alloy space suggests immediate potential for the use of these exfoliated layered materials as epitaxial substrates for photovoltaic development.