Defect Chemistry in High‐Voltage Cathode Materials for Lithium‐Ion Batteries

High-voltage cathodes (HVCs) have emerged as a paramount role for the next-generation high-energy-density lithium-ion batteries (LIBs). However, the pursuit of HVCs comes with inherent challenges related to defective structures, which significantly impact the electrochemical performance of LIBs. The current obstacle lies in the lack of a comprehensive understanding of defects and their precise effects. This perspective aims to provide insights into defect chemistry for governing HVCs. The classifications, formation mechanisms, and evolution of defects are outlined to explore the intricate relationship between defects and electrochemical behavior. The pressing need for cutting-edge characterization techniques that comprehensively investigate defects across various temporal and spatial scales is emphasized. Building on these fundamental understandings, engineering strategies such as composition tailoring, morphology design, interface modification, and structural control to mitigate or utilize defects are thoroughly discussed for enhanced HVCs performance. Furthermore, these insights are expected to provide vital guidelines for developing high-performance HVCs for next-generation high-energy lithium-ion batteries.

cross-scale characterization↗

DOE OSTI2024

Demystifying In Situ Pyrolysis Chemistry for High-Performance Polyanionic Cathodes in Sodium-Ion Batteries

In this article, the carbon coating strategy has emerged as an indispensable approach to improve the conductivity of polyanionic cathodes. However, owing to the complex reaction process between precursors of carbon and cathode, establishing a unified screening principle for carbonaceous precursors remains a technical challenge. Herein, we reveal that carbonaceous precursor pyrolysis chemistry undeniably influences the formation process and performance of Na 3 V 2 (PO 4 ) 3 (NVP) cathodes from in situ insights. By investigating three types of carbonaceous precursors, it is found that O/H-containing functional groups can provide more bonding sites for cathode precursors and generate a reducing atmosphere by pyrolysis, which is beneficial to the formation of polyanionic materials and a uniform carbon coating layer. Conversely, excessive pyrolysis of functional groups leads to a significant amount of gas, which is detrimental to the compactness of the carbon layer. Furthermore, the substantial presence of residual heteroatoms diminishes graphitization. In this case, it is demonstrated that carbon dots (CDs) precursors with suitable functional groups can comprehensively enhance the Na+ migration rate, reversibility, and interface stability of the cathode material. As a result, the NVP/CDs cathode displays outstanding capacity retention, maintaining 92% after 10,000 cycles at a high rate of 50 C. Altogether, these findings provide a valuable benchmark for carbon source selection for polyanionic cathodes.

25 ENERGY STORAGE↗

DOE OSTI2023

Enabling Structure/Interface Regulation for High Performance Ni-Rich Cathodes

Here, further commercialization of Ni-rich layered cathodes is hindered by severe structure/interface degradation and kinetic hindrance that occur during electrochemical operation, which leads to safety risks and reduced range in electric vehicles (EVs). Herein, by selecting elements with different solubility properties, a multifunctional strategy that synchronously fabricates perovskite-type SrZrO 3 coating and Sr/Zr co-doping is employed to strengthen the structure/interface stability and the Li + transport mobility of LiNi 0.85 Co 0.10 Mn 0.05 O 2 (NCM). Perovskite-type SrZrO 3 protective layers formed on the particle surface can substantially mitigate the unexpected interfacial side reactions and surface phase transitions. In addition, a robust crystal framework is constructed by optimizing local O coordination through the introduction of strong Zr-O bonds. Notably, Li + diffusion kinetics is effectively improved due to expanded cell parameters and O-Li-O slab spacing with the incorporation of large-diameter Sr pillar ions, as revealed by X-ray diffraction. As a result, the Sr/Zr-modified NCM achieves a remarkable capacity retention of 99.4% after 200 cycles at 1 C, and a high rate capacity of 168.9 mAh g -1 at 10 C. This work opens new avenues to develop high-performance NCM cathodes with high energy and high power for EVs with long calendar life.

25 ENERGY STORAGE↗

DOE OSTI2022

Building interface bonding and shield for stable Li-rich Mn-based oxide cathode

Implementation of Li-rich Mn-based oxide cathode with high-energy-density has been restrained by capacity/voltage degradation that results from irreversible lattice oxygen loss and structure rearrangements. To resolve these challenges, in this work, Li 1.2 Mn 0.54 Ni 0.13 Co 0.13 O 2 encapsulated by amorphous Co x B (CB-LRM) is rationally designed via autocatalytic plating for highly reversible cationic/anionic hybrid cathode material. Band coherency is ingeniously evoked by interface-reconstruction between bulk structure and amorphous coating layer, which lower the energy of O $2p$ states. Furthermore, this is associated with strengthened orbital hybridization of O $2p$-Mn $3d$ and increased formation energy of oxygen vacancy, which mitigates the lattice oxygen loss considerably. Additionally, interface shielding effects that protect electrode against electrolyte corrosion and the reduction of surface oxygen are also present with fully coverage of amorphous Co x B coating layer. As a result, the as-designed CBLRM cathode exhibits excellent cycle stability after 100 loops with only 0.154% per cycle capacity fade and improved voltage degradation. Given this, this work provides a potential avenue for rational design of lattice oxygen-based electrode materials with high-energy-density.

25 ENERGY STORAGE↗

DOE OSTI2022

Structure/Interface Coupling Effect for High-Voltage LiCoO 2 Cathodes

LiCoO 2 (LCO) is widely applied in today's rechargeable battery markets for consumer electronic devices. However, LCO operations at high voltage are hindered by accelerated structure degradation and electrode/electrolyte interface decomposition. To overcome these challenges, co-modified LCO (defined as CB-Mg-LCO) that couples pillar structures with interface shielding are successfully synthesized for achieving high-energy-density and structurally stable cathode material. Benefitting from the "Mg-pillar" effect, irreversible phase transitions are significantly suppressed and highly reversible Li + shuttling is enabled. Interestingly, bonding effects between the interfacial lattice oxygen of CB-Mg-LCO and amorphous Co x B y coating layer are found to elevate the formation energy of oxygen vacancies, thereby considerably mitigating lattice oxygen loss and inhibiting irreversible phase transformation. Meanwhile, interface shielding effects are also beneficial for mitigating parasitic electrode/electrolyte reactions, subsequent Co dissolution, and ultimately enable a robust electrode/electrolyte interface. As a result, the as-designed CB-Mg-LCO cathode achieves a high capacity and excellent cycle stability with 94.6% capacity retention at an extremely high cut-off voltage of 4.6 V. We report these findings provide new insights for cathode material modification methods, which serves to guide future cathode material design.

25 ENERGY STORAGE↗