Fatigue damage in notched composite laminates
This communication describes the results of an experimental investigation of the fatigue characteristics of a boron-epoxy laminate containing an unloaded circular hole. The study focuses upon characterization of the fatigue damage incurred and its influence upon axial tensile residual strength. Two apparent anomalies in the fatigue behavior for this laminate were observed. First, the fatigue damage was observed to propagate tangentially to the edge of the notch (parallel to the direction of the load), in contrast to propagation in contemporary metallic materials which is perpendicular to the load direction. Second, the residual strength characteristics for the laminate have revealed a significant increase in residual strength subsequent to a fatigue loading of 500,000 cycles at R = 0.1 and S = 0.8 and 0.67 (S = maximum stress/static ultimate). Failure analyses of the fatigue damage are conducted utilizing ultrasonic 'C' scan techniques.