Publications and source records attributed to Mcdonald, G..
The creep of plasma sprayed ZrO2-8Y2O3 was measured at temperatues from 98 to 1250 C (180 to 220 F), and compared to creep of identical samples after annealing at temperatures from 98 to 1316 C (1800 to 2400 F). Loads and temperatures which produced significant creep of as sprayed ceramics produced no creep after annealing.
Ceramics on metal substrates for potential use as high temperature seals or other applications are exposed to forces originating from differences in thermal expansion between the ceramic and the metal substrate. This report develops a relationship between the difference in expansion of the ceramic and the substrate, defines conditions under which shear between the ceramic and the substrate occurs, and those under which bending forces are produced in the ceramic. The off-axis effect of compression forces resulting from high temperature plastic flow of the ceramic producing buckling of the ceramic is developed. Shear is associated with the edge or boundary stresses on the component while bending is associated with the distortion of an interior region. Both modes are significant in predicting life of the ceramic.
The residual stresses in a ceramic sheet material used for turbine blade tip gas path seals, were estimated. These stresses result from the plasma spraying process which leaves the surface of the sheet in tension. To determine the properties of plasma sprayed ZrO2-Y2O3 sheet material, its load deflection characteristics were measured. Estimates of the mechanical properties for sheet materials were found to differ from those reported for plasma sprayed bulk materials.
(Previously announced in STAR as N82-17453)
(Previously announced in STAR as N82-32633)
An analysis has been developed which relates the effects of inelastic behavior of Y2O3 stabilized ZrO2 (YSZ) materials. The results show these materials to be sensitive to small changes in temperature and are supported by measurements of inelastic behavior in disk and bar specimens at temperatures as low as 1010 C (1850 F). At higher thermomechanical loads, the test specimens can deform to strains greater than 1 percent and for bar specimens, with sufficient strength, to remain bonded to the metallic substrate.
Some experimental and analytical studies of plasma sprayed ZrO2-Y2O3 thick seal thermoprotective materials over NiCrAlY bond coats with testing to 1040 deg C in a Mach 0.3 burner flame are reviewed. These results indicate the need for material to have both compliance and sufficient strength to function successfully as a thick thermoprotective seal material. Fibrous materials may satisfy many of these requirements. A preliminary analysis simulating the simplified behavior of a 25 mm cylindrical SiO2-fiber material indicated significant radial temperature gradients, a relatively cool interface and generally acceptable stresses over the initial portion of the thermal cycle. Subsequent testing of these fiberlike materials in a Mach 0.3 Jet A/air burner flame confirmed these results.
An analysis of thermal cycle life data for four sets of eight thermal barrier coated specimens representing arc currents (plasma gun power) of 525, 600, 800, or 950 amps is presented. The ZrO2-8Y2O3/NiCrAlY plasma spray coated Rene 41 rods were thermal cycled to 1040 C in a Mach 0.3-Jet A/air burner flame. The experimental results indicate the existance of a minimum or threshold power level which coating life expectancy is less than 500 cycles. Above the threshold power level, coating life expectancy more than doubles and increases with arc current.
The effects of inelastic behavior of yttria-stabilized zirconia (YSZ) materials were analyzed. The results show these materials to be sensitive to small changes in temperature and are supported by measurements of inelastic behavior in disc and bar specimens at temperatures as low as 1010 C (1850 F). At higher thermomechanical loadings, the test specimens can deform to strains above 1 percent.
The reported study had the purpose to examine variations in cyclic life and in adhesive/cohesive coating strength. Possible effects of heating rate, stress reversal, temperature level, and ceramic deposition methods on coating life were also investigated. Life cycle data for 22 thermal barrier coated rods were examined and found to be statistically modeled by normal or log-normal distributions. The sample mean was 1330 cycles with a standard deviation of 520 cycles. Adhesive/cohesive pulloff strength data for 20 thermal barrier coated flat head piston specimens were taken. The average pulloff stress was 9 MPa with a standard deviation of 4.2 MPa. It was found that variations in heating rate can produce significant variations in the life cycle data.
Thermal barrier coatings applied to the heated side of engine components such as seals, combustor, and blades of a gas turbine offer a potential increase in efficiency through the use of higher gas temperatures or less cooling air or benefits arising from extended component life by reducing component metal temperatures. The considered investigation has the objective to show that while a thermal barrier coated (TBC) specimen can be brought to a fixed temperature using various fuel-air ratio (F/A) values, lower calculated stresses are associated with lower (F/A) values. This implies that control of (F/A) values (i.e., rates of heat input) during the starting transient and to a lesser extent during shutdown and operation, offers a potential method of improving TBC lifetime through thermal cycle management.
Measurements were made of the rate of increase in temperature of a ZrO2-8Y2O3 thermal barrier coated (TBC) specimen for various values of fuel/air (F/A) ratios when the specimen is exposed to a 0.3 Mach burner flame. For rod specimens in a carousel, the heating rates increased with (F/A) ratio and were higher at the inward facing surface for a given (F/A). Plate specimens were more sensitive to burner variations. Calculated results are given for the radial stress in the coated rod specimens for variations in (F/A) ratios from 0.04 to 0.065. Over this range, the radial stress varies from 4.3 to 5.3 MPa. The results indicate that controlling the heating rate of a TBC by controlling the (F/A) ratio offers a potential method to prolong TBC cyclic life; uncontrolled (F/A) ratios will produce scatter in experimental results. Geometric arrangement can have an equivalent effect, but is usually fixed by design.
An analysis of thermal cycle life data for 22 thermal barrier coated (TBC) specimens was conducted. The Zr02-8Y203/NiCrAlY plasma spray coated Rene 41 rods were tested in a Mach 0.3 Jet A/air burner flame. All specimens were subjected to the same coating and subsequent test procedures in an effort to control three parametric groups; material properties, geometry and heat flux. Statistically, the data sample space had a mean of 1330 cycles with a standard deviation of 520 cycles. The data were described by normal or log-normal distributions, but other models could also apply; the sample size must be increased to clearly delineate a statistical failure model. The statistical methods were also applied to adhesive/cohesive strength data for 20 TBC discs of the same composition, with similar results. The sample space had a mean of 9 MPa with a standard deviation of 4.2 MPa.
Black cobalt oxide coatings were deposited on thin layers of silver or gold which had been deposited on oxidized stainless steel substrates. The reflectance properties of these coatings were measured at various thicknesses of cobalt oxide for integrated values of the solar and infrared spectrum. The values of absorptance and emittance were calculated from the measured reflectance values before and after exposure in air at 650 C for 1000 hours. Also, these cobalt oxide/noble metal/oxide diffusion barrier coatings have absorptances greater than 0.90 and emittances of approximately 0.20 even after about 1000 hours at 650 C.
The paper studies the comparative life of plasma-sprayed ZrO2-Y2O3 thermal barrier coatings on NiCrAlY bond coats on Rene 41 in short (4 min) and long (57 min) thermal cycles at 1040 C in a 0.3-Mach flame. Attention is given to determining the effect of short- and long-duration cycles on ZrO2-Y2O3 coatings, the cause of any cycle frequency effects, and methods to improve tolerance to thermal stress. Short cycles greatly reduced the life of the ceramic coating in terms of time at temperatures as compared to longer cycles, the failed coating indicating compressive failure. The experiments and stress calculations show that repeatedly subjecting a ceramic coating to high rates of initial heating has a more destructive influence on the coating than sustained operation at temperature. The effect of such thermal compressive stresses might be minimized through coating deposition and thickness control and by turbine cycle measurement to keep starting heating rates below critical values.
Black cobalt oxide coatings (high solar absorptance layer) were deposited on thin layers of silver or gold (low emittance layer) which had been previously deposited on oxidized (diffusion barrier layer) stainless steel substrates. The reflectance properties of these coatings were measured at various thicknesses of cobalt for integrated values of the solar and infrared spectrum. The values of absorptance and emittance were calculated from the measured reflectance values, before and after exposure in air at 650 C for approximately 1000 hours. Absorptance and emittance were interdependent functions of the weight of cobalt oxide. Also, these cobalt oxide/noble metal/oxide diffusion barrier coatings have absorptances greater than 0.90 and emittances of approximately 0.20 even after about 1000 hours at 650 C.
A study was made of the comparative life of plasma sprayed ZrO2-Y2O3 thermal barrier coatings on NiCrAlY bond coats on Rene 41 in short (4 min) and long (57 min) thermal cycles to 1040 C in a 0.3 Mach flame. Short cycles greatly reduced the life of the ceramic coating in terms of time at temperature as compared to longer cycles. Appearance of the failed coating indicated compressive failure. Failure occurred at the bond coat-ceramic coat junction. At heating rates greater than 550 kw/sq m, the calculated coating detachment stress was in the range of literature values of coating adhesive/cohesive strength. Methods are discussed for decreasing the effect of high heating rate by avoiding compressive stress.
Concentric glass-tube-envelope device surrounds flat-plate absorber having spectrally selective coating. Transparent envelope has antireflection coating. Heat-transfer medium is gas that circulates along hairpin path.