Advanced Manufacturing for Harsh Environments at Idaho National Laboratory
Slides for presentation discussing advanced manufacturing work being done at INL.
36 MATERIALS SCIENCE↗
Engineering topics
McMurtrey, Michael D
Publications and source records attributed to McMurtrey, Michael D.
Summary of Alloy 617 and Alloy 709 Elevated Temperature Crack Growth Test Results from the Planned FY24 Crack Growth Test Activities
This report covers the results from crack growth rate testing performed at Idaho National Laboratory in the fiscal year 2024. It includes two creep crack growth rate tests and two creep-fatigue crack growth rate tests. Results are shown for each of these tests, included crack growth measured during the test using direct current potential drop, and measurements based off of the fracture surface. Load line displacement, as well as load, were also collected during the tests. Detailed analysis of the results will continue into the next fiscal year, however, a number of potential improvements to the equipment and testing procedures were identified that will increase testing reliability and throughput, as well as decrease complications with the analysis.
11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
Design, Fabrication and Testing of Surveillance Test Articles for MSR Materials Degradation Management
This report details the design, fabrication, and testing of surveillance test articles aimed at assessing material damage in reactor-relevant environments for effective degradation management. Two types of surveillance test articles with reduced sizes were developed based on design algorithms and finite element modeling: welded design and interlocking design. A furnace heating setup was adopted to apply multiple thermal cyclic loading profiles on the test articles with a temperature range of 500°C - 700°C, while the strain response was monitored using a digital image correlation technique. The testing results demonstrated the successful capturing of expected strain range for welded design while machining tolerance should be improved to engage strain coupling in the interlocking design. Mid-term (500 hours) and long-term (1500 hours) cyclic tests were conducted on welded test articles. A constant strain range of ~0.6% was observed at the specimen with testing under 500 hours, while a gradual decrease of strain at specimen was observed after 500 hours. Non-destructive evaluation through X-ray computed tomography confirmed the microcracks in the welds at specimen-driver joints after cyclic test that caused the strain change. Creep testing of the specimen after long-term cyclic test revealed a short creep life than expected. A multi-profile cyclic test was also conducted on a test article and demonstrated consistent strain response under different temperature ramp rates. The report also briefly discussed the challenges and future research efforts to advance test article development for material surveillance.
11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
Nuclear Structural Component Relevant Properties of Nickel-Based Alloys Produced via Additive Manufacturing
Idaho National Laboratory initiated examination of nickel-based alloys manufactured via three different additive manufacturing methods for potential applications in nuclear, high temperature structural components. The three methods analyzed included laser powder bed fusion, blown powder laser directed energy deposition, and wire-fed gas metal arc directed energy deposition. With the rapid push towards additive manufacturing, codes do not exist that definitively define what is or is not tolerable for each process and application, such as with conventional, wrought products. This report contains the initial work to understand possible manufacturing methods for high temperature alloys, and specifically, void formation, microstructure evolution, corrosion, and mechanical properties. To generate mechanical test data, specimens were tested irrespective of voids and microstructures were analyzed to better understand how to negate/improve these issues. The preliminary results showed major decreases in mechanical performance for material tested. Test specimens will continue to be produced to further improve each additive manufacturing processes, quantify void acceptance, and better understand the most suitable high temperature alloys receptive to additive manufacturing and high temperature nuclear applications.
36 MATERIALS SCIENCE↗
Assessment of preliminary results of baseline high entropy alloys manufactured at INL
Materials development is needed to support the design and deployment of advanced nuclear reactors that will operate at higher temperatures and in harsher environments than the current light water reactor fleet. High entropy alloys have been identified as a class of alloy that could address the needs of advanced reactors, such as the molten salt reactors, due to their potential strength, radiation resistance, and corrosion resistance. This project summarizes the work done in fiscal year 2024 for the Additive Manufacturing of High Entropy Alloys for Nuclear Applications Project. This work has focused on examination of potential alloy compositions, down selection based on simulated results, and preliminary testing of down selected alloys.
36 MATERIALS SCIENCE↗
High Temperature Metals Program Overview
Overview of the Advanced Reactor Technologies Gas Cooled Reactor High Temperature Materials Program.
36 MATERIALS SCIENCE↗
High Temperature Materials
Overview of high temperature metals, including component construction rules for advanced reactor designs, assessment of filler metal for Alloy 800H weldments, high-temperature crack growth rate testing, work packages and contributors for FY24, creep-fatigue damage summation evaluation, GCR metal needs, and high temperature metals from other programs.
11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
Multiobjective Constrained Symbolic Regression for Predictive Modeling of Material Creep Behavior
When creep testing is repeated on samples of the same alloy under the same parametric conditions (i.e., stress and temperature), the resulting strain/time curves can vary from each other considerably as shown in Figure 1 [1]. The time required to creep test a material to rupture can extend to the order of years. Because of this, a numerical model that can quickly analyze the incomplete results of an ongoing experiment to predict 1) the incomplete portion of the strain/time curve leading up to the rupture point and 2) the rupture point itself would be of great utility to the materials community. Such a model has the potential to save 1) the time required to finish running the experiment to rupture 2) the associated monetary cost of finishing said experiment. Furthermore, it would be advantageous if the predictive model could give a parametric function modeling strain/time curves for material scientists to investigate the impact of the temperature and stress parameters on the resulting creep behavior. This work introduces a piecewise symbolic regression algorithm to predict the remainder of the strain/time curve. Preliminary results show good model performance.
36 MATERIALS SCIENCE↗
800H Weldments and Crack Growth Rates of CGR Alloys
Update on FY24 crack growth rate and 800H weldment testing.
36 MATERIALS SCIENCE↗