NASA NTRS1988

Extending Fatigue Lives Of Selected Alloys

Rejuvenating treatments demonstrated. Experiments with three alloys show some combinations of heat treatment, hot isostatic pressing, and/or surface treatment extends cycle lives of fatigue-damaged or fatigue-precracked specimens. For each alloy, tests were first done to determine "baseline" high-cycle-fatigue lives and high-cycle-fatigue failure modes over range of test conditions. Controlled fatigue damage introduced into specimens. Damaged specimens subjected to candidate rejuvenating treatments, then tested to failure. Effectiveness of each treatment judged by comparing fatigue data of damaged and treated specimens to "baseline" fatigue and data taken at same test conditions.

Matejczyk, D. E.↗

NASA NTRS1985

Fatigue life extension

Potential fatigue rejuvenation processes were carried out on fatigue-damaged material both with and without observable surface-connected fatigue cracks. The fatigue life of fatigue-damaged MAR-M246(Hf)(DS), a directionally solidified nickel-base superalloy used in turbine airfoils, was extended by reheat treatment. The fatigue life of fatigue-cracked Inconel 718, a wrought nickel-base superalloy used in a wide variety of advanced rocket engine components, was extended by electron-beam welding to close off the surface-connected crack, followed by hot isostatic pressing and reheat treatment.

Matejczyk, D. E.↗