All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Wrought FeCrAl alloy (C26M) cladding behavior and burst under simulated loss-of-coolant accident conditions

Cladding burst experiments for FeCrAl cladding were performed in the Severe Accident Test Station facility at Oak Ridge National Laboratory. These experiments were simulated using the BISON fuel performance code to better understand the cladding plastic behavior and failure under simulated loss-of-coolant accident conditions. 3D cladding surface boundary conditions were generated using composite axial and azimuthal profiles from experiment thermocouple data. To improve the simulation analysis capabilities in BISON for cladding burst behavior, new thermal creep, plasticity, and failure stress models specific to C26M, a wrought FeCrAl alloy, were developed and implemented. Initial cladding burst results indicated a general underprediction in the failure temperature of the six cladding burst simulations versus the observed failure temperatures. Close investigation of the experiment timing versus the underlying tensile test data revealed that, compared with the tensile specimens, the cladding tubes did not experience the same long holding time at high temperatures. New tensile tests were performed at high temperatures using a temperature ramp similar to the simulated loss-of-coolant accident experiments. These new tensile curves showed an approximately 80% increase in the ultimate tensile strength of the C26M alloy, indicating that a holding time of 10 min at 700 °C and 800 °C allows annealing to change the material microstructure. Using the updated tensile properties, the burst temperatures and stresses from the simulations showed remarkable agreement with the experimental results. This study was then extended by varying the initial pressure to highlight the burst temperature difference between standard Zircaloy-4 and C26M cladding under equivalent conditions. The results show that C26M has a burst temperature that is approximately 70–130 K greater than that of Zircaloy-4. In conclusion, these modeling predictions can be further improved by collecting high-temperature tensile data for C26M beyond the temperature ranges used in this work.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Hydrogen embrittlement of Zircaloy-4 fabricated by ultrasonic additive manufacturing

Ultrasonic additive manufacturing (UAM) was successfully applied to the zirconium material system to create a planar geometry. Following fabrication, SS-J3 type tensile specimens of the UAM and wrought Zircaloy-4 with a nominal gage section of 5×1.2×0.75 mm were machined for hydriding studies and mechanical testing. The SS-J3 type tensile specimens were gas-charged with hydrogen using a custom system that precisely controls hydrogen gas flow rate, hydrogen partial pressure, and temperature. To avoid altering the UAM material, the maximum process temperature was limited to 550°C. Using different initial hydrogen gas pressures and flow rates, various hydrogen contents (70–1755 wppm) were achieved for Zircaloy-4 specimens. Tensile testing shows that, regardless of hydrogen content, all UAM specimens measured yield strengths in the range of 557±16 MPa and ultimate tensile strengths of 660±4MPa. However, total elongation clearly decreased as a function of increasing hydrogen content. Further, at the lowest hydrogen content, the total plastic elongation measured 21.5%, and this value decreased to less than 2% when the hydrogen content was increased to 1000 wppm. Cross-sectional optical microscopy images revealed that the hydride distributions are randomly oriented. For the low hydrogen content specimen, these randomly distributed hydrides are isolated from each other. A sandwiched structure, consisting of high-density and low-density layers, was also observed for the specimens with hydrogen content between 200 and 400 wppm. As the hydrogen content increases, the hydrides diffuse into the low-density hydride layers to form a network across the whole specimen. Although the tensile properties of UAM and wrought Zircaloy-4 exhibit the same behavior with increasing hydrogen content, the distinctions in grain orientations led to differences in the hydride orientations at low and intermediate hydrogen concentrations.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Strength stability at high temperatures for additively manufactured alumina forming austenitic alloy

Several fast-spectrum nuclear reactors designed to generate high power (~450 MWe) rely on forced convection of media such as supercritical CO 2 , sodium, or liquid lead to cool the nuclear core, operating at temperatures up to 600 °C. Cost-effective, high-strength Fe-based alumina forming austenitic (AFA) alloys are a promising candidate for the fabrication of critical nuclear components. This study investigated laser powder bed fusion (LPBF) processing of an AFA alloy composition optimized for improved creep resistance. Electron microscopy revealed an elongated grain structure along the build direction with a fine sub-grain cellular structure decorated with (Cr,Fe,Nb) 23 C 6 carbide precipitates at the intercellular boundaries. Finally, at temperatures of 20–900 °C, the LPBF alloy's superior tensile properties compared to its arc-melted counterpart and other advanced steels (e.g., SS316) were attributed to the distribution of nano-sized carbide precipitates, whereas the high ductility was attributed to the LPBF alloy's elongated grain structure.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Status report on HFIR irradiation of optimized alumina forming alloys

Properties of FeCrAl alloys under neutron irradiation are of interest because of these materials’ potential application as accident-tolerant fuel cladding in nuclear systems. In parallel, alumina-forming austenitic (AFA) alloys are of interest for use as structural materials in advanced nuclear systems for their potential higher resistance to embrittlement and high-temperature steam oxidation resistance. An irradiation campaign for fiscal year 2024 has been developed under the Advanced Fuels Campaign to perform irradiation testing of various FeCrAl and AFA alloys in Oak Ridge National Laboratory’s High Flux Isotope Reactor (HFIR). The goals of this irradiation campaign are to (1) study the impact of minor alloying elements on the neutron-irradiated mechanical properties of FeCrAl alloys and (2) collect neutron-irradiated mechanical properties on AFA alloys for comparison with those of FeCrAl alloys. This campaign will include both tensile and fracture toughness specimens tested following HFIR irradiation at temperatures representative of normal operating conditions in light-water reactors. The pre-irradiation characterization to date, the irradiation plan for the FeCrAl and AFA specimens, and the subsequent post-irradiation experimental test plan are presented in this report, along with the status of HFIR builds and scheduled insertion dates.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Post-irradiation examination of commercial tantalum alloys following neutron irradiation

Post irradiation examination of two commercial tantalum alloys (based on Ta-8 %W) revealed significant irradiation hardening following neutron irradiation in the High Flux Isotope Reactor at Oak Ridge National Laboratory. Tensile samples of commercial Ta alloys T-111 and ASTAR-811C were irradiated to a total neutron fluence (E > 0.1 MeV) in the range (2–4)x10 21 n/cm 2 (0.39–0.75 dpa) at an irradiation temperature near 900 °C. Tensile testing conducted at room temperature and at 800 °C revealed significant irradiation hardening under all test conditions. Samples that were tensile tested at room temperature exhibited brittle failure, whereas ductility was maintained for elevated temperature testing. The irradiation hardening and embrittlement noted for both alloys was attributed to irradiation-induced dislocation loop formation as confirmed through scanning transmission electron microscopy analysis. Corresponding energy dispersive x-ray spectroscopy revealed radiation-induced segregation of Hf in these loop populations. This Hf enrichment is shown to result in eventual co-precipitation of elongated (Hf,O)-rich precipitates along the dislocation loops. Further, these results show that irradiation hardening is enhanced via irradiation-enhanced precipitation at elevated irradiation temperatures. Consequently, the minimum recommended operating temperature window for Ta alloys should be increased to account for observed hardening/embrittlement at irradiation temperatures as high as 900 °C (1,173 K).

36 MATERIALS SCIENCE↗
DOE OSTI2023

AMMT FY23 HFIR Irradiation Test Matrix – Supported by the Design of a Miniature Bend Bar Irradiation Vehicle

With the continued advancement of additive manufacturing (AM) techniques, interest has grown in the development and qualification of steels produced via these methods for use in the structural components of advanced nuclear reactors. Therefore, it is crucial that the properties of these materials such as the tensile strength and fracture toughness be investigated following neutron irradiation to support their use in industry. To that end, a test plan to irradiate several tensile and bend bar specimens in the High Flux Isotope Reactor (HFIR) at Oak Ridge National Laboratory was proposed, along with the development of a new “MINBEN” capsule design that features MBS-1 bend bar specimens that have a larger cross-sectional area than those of previous designs, which allows for higher temperature out-of-pile testing. The specimens include AM 316H stainless steel with wrought 316H and A709 stainless steels for reference, and they will be irradiated at 2 dpa and 10 dpa—corresponding to roughly 1 and 5 cycles at the HFIR midplane—at temperatures of 400°C and 600°C. The MINBEN design was found to be capable of providing specimen test plane average temperatures in the range of 220–660°C for six specimens, with a min-max spread in this temperature of ~40°C and a 95% confidence interval of ~24°C. This analysis shows that the capsule provides an effective vehicle for gathering needed high-temperature fracture toughness data.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Analysis of orientation-dependent deformation mechanisms in additively manufactured Zr using in-situ micromechanical testing: Twinning and orientation gradient

Here, orientation-dependent plasticity in zirconium (Zr)-alloy, which is produced through ultrasonic additive manufacturing (UAM) with subsequent hot-isostatic pressing (HIP), was analyzed by recording electron backscattered diffraction (EBSD) data during in-situ micromechanical testing. Three (0001) plane orientations of a hexagonal close-packed (HCP) structure were analyzed parallel to (1) the rolling direction [X||tensile direction (TD)], (2) the build direction [Z], and (3) the transverse direction [Y]. The analysis revealed that the grains with ~<0001>||TD show twin-dominant plasticity with three variants from {10 $\overline{1}$ 2}<$\overline{1}$ 011>; minor slipping with ($10\overline{1}$ 1)[$\overline{2}$ 113], and ($11\overline{2}$ 2)[$\overline{1} \overline{1}$ 23] pyramidal slip has also been observed. However, grains with orientation ~<0001>⊥TD are mainly sensitive to dislocations assisted plasticity-leading to orientation gradients formation. Furthermore, the neck formation was identified as originating from higher populated micro-crack locations and their association with localized plasticity at defect points in the UAM material. These results demonstrate that minimization of impurities to enable grain growth across prior foil interfaces makes HIP an effective methodology for producing Zr plate, with deformation characteristics expected for conventionally manufactured Zr.

36 MATERIALS SCIENCE↗
DOE OSTI2022

On the efficacy of post-build thermomechanical treatments to improve properties of Zirconium fabricated using ultrasonic additive manufacturing

Here, hot-isostatic pressing has been applied to Zirconium plate fabricated using the ultrasonic additive manufacturing (UAM) technique to enhance interfacial bond quality. Specimens heated to 800 C for 1 h at 100 MPa pressure showed grain growth across many prior foil-to-foil interfaces, thereby increasing foil adhesion. In addition to the material softening induced by a loss of Hall-Petch strengthening, premature failure of specimens loaded parallel to the build direction was observed. Premature specimen failure was attributed to the local delamination at prior foil-to-foil boundaries where grain growth was pinned by Ti impurities introduced during the UAM process via the interaction between a Ti-alloy buffer foil and the welded Zr-foils underneath. In addition, the presence of Ti along select foil interfaces resulted in the nucleation and growth of secondary (Zr,Ti)(Fe,Cr) laves phases during higher-temperature thermomechanical processing. Using a combination of micro-scale X-ray computed tomography, fractography, and in-situ digital image correlation, the effect of defects along prior foil-to-foil boundaries was revealed as delamination-assisted plasticity accelerated specimen failure in preferred tensile orientations. These findings underscore the importance of impurity control when optimizing weld quality of higher-strength material systems using ultrasonic welding.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Hydrothermal corrosion and steam oxidation behavior comparison of UAM and conventional Zry-4

Here, hydrothermal corrosion and steam exposures on ultrasonic additively manufactured (UAM) Zircaloy-4 (Zry-4) specimens were conducted to compare to wrought Zry-4 performance in both simulated pressurized water reactor (PWR) operation (330°C, 15 MPa, <50 ppb oxygen, 500h) and representative accident conditions (100% H 2 O(g) at 700, 900, and 1100°C for up to 1h). UAM Zry-4 specimens showed 50% higher mass gain in PWR conditions and 50-80% more mass gain in steam oxidation due to internal oxidation between build layers in both cases. UAM Zry-4 in 900°C steam showed breakaway oxidation leading to sample deformation. Titanium used as an interlayer in the UAM process was detected in the substrate after the 1100°C exposure. Additional experiments to better link as-built defects to oxidation behavior are needed.

36 MATERIALS SCIENCE↗
DOE OSTI2022

High-Temperature Tensile and Creep Test Results on Thin Wall Tube Specimens of ODS Alloys 14YWT and OFRAC

High-temperature tensile and strain rate jump (SRJ) creep tests were conducted on axial specimens fabricated from thin wall tubes of the oxide dispersion strengthened (ODS) alloys 14YWT and OFRAC. The dimensions of the 14YWT thin wall tube was 10.7 mm OD, 0.5 mm WT and 0.92 m and of the OFRAC thin wall tube was 8.5 mm OD + 0.5 mm WT and 1.78 m in length. The axial specimens fabricated from the thin wall tubes were based on a dual-gauge design with gauge dimensions of 4 mm long and 2 mm wide. The tensile tests were conducted in air at 800ºC, 900ºC and 1,000ºC and the SRJ creep tests were conducted in air at 800ºC. Two axial specimens were used in each tensile and SRJ creep tests. The results of the tensile tests showed much lower yield stress (YS) compared to ultimate tensile strength (UTS) indicative of large work hardening properties. The results showed the UTS of OFRAC was higher than that of 14YWT by ~35 MPa at 800ºC. At 900ºC, the UTS of OFRAC and 14YWT was similar at 900ºC and at 1000ºC, the UTS of 14YWT was higher than that of OFRAC by ~10 MPa. The ductility properties of OFRAC were greater than that of 14YWT with higher values of uniform elongation (UE) and total elongation (TE) at all tensile test temperatures. The creep properties of 14YWT and OFRAC were evaluated by the strain rate jump test method at 800ºC. The stress exponent (n) for creep was obtained from the SRJ test data by plotting the values of the log strain rate against the log stress, which is measured from the stress-strain curve generated during the SRJ test. The results showed the highest stress exponents of n = 19.8 and n = 35.0 were measured from the two SRJ tests on 14YWT. The stress exponent measured from one successful SRJ test on OFRAC was n = 13.3, which was lower than that of 14YWT. Nevertheless, these high values of stress exponent are consistent with ODS ferritic alloys such as 14YWT and OFRAC since they indicate dislocation-particle interactions are the dominant creep mechanism for specific ranges of temperature and stress. The results obtained from the tensile and SRJ creep tests conducted on axial specimens in this study indicate that 14YWT and OFRAC retain high strengths at temperatures up to 1,000ºC and good creep performance at 800ºC.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Improved irradiation resistance of accident-tolerant high-strength FeCrAl alloys with heterogeneous structures

In this work, post–neutron irradiation examination is performed on advanced accident-tolerant fuel (ATF) cladding iron-chromium-aluminum (FeCrAl) alloys with ~10–13at. % Cr, ~10–12 at. % Al, ~1 at. % Mo, and minor alloying elements including Y irradiated to a damage level of 7 displacements per atom (dpa) at irradiation temperatures of 267–282 °C. A compositional dependency of the Cr and Al content is observed on the ratio of sessile and glissile dislocation loops, where the density of a$\langle$100$\rangle$ type loops is somewhat higher than the a/2$\langle$111$\rangle$ type loops. The α' precipitate number density is inversely correlated to the starting Cr concentration of the alloys of interest. The irradiation to a higher dose of 7 dpa results in a higher density of dislocation loops and α' precipitates for the same alloys at a lower irradiation dose, such as 1.8 dpa. In this work, the effect of α' precipitates on the dislocation loop density is discussed, and the presence of α' appears to inhibit the nucleation of loops. Compared with first-generation FeCrAl alloys, these advanced alloys with heterogeneous structure exhibit a lower Cr concentration in α' precipitation at the same dose level; they act as weaker obstacles deviating from the primary hardening contribution from the mature α'. Hence, the overall irradiation-induced hardening decreases; our alloys show improved radiation resistance because of their stronger sink strengths. The results presented in this paper could provide insights for the design and optimization of ATF cladding materials for future fission and space applications.

36 MATERIALS SCIENCE↗
DOE OSTI2022

BISON validation of FeCrAl cladding mechanical failure during simulated reactivity-initiated accident conditions*

Here, a reactivity-initiated accident (RIA) is a postulated design basis accident in light water reactors (LWRs) in which a rapid reactivity insertion induces a fission rate increase and a fuel pellet temperature rise. During RIA, the fuel pellet thermally expands and may cause pellet-cladding mechanical interaction (PCMI). Separate effects PCMI tests were performed on C26M FeCrAl cladding tube samples, introducing biaxial stress via a well understood modified burst test (MBT) system. A high-speed camera in the MBT system captured the projections, covering a 360° view of the cladding deformation and enabling a digital image correlation (DIC) method to quantify the surface strains with high fidelity. Representative hot zero-power RIA mechanical loading conditions were applied to the sample, and the test duration ranged from 20 to 500 ms at an average temperature of 573 K. BISON finite element–based fuel performance code modeling was performed against the high-fidelity DIC data produced from the MBTs. Validation calculations were conducted with 2D models and systematically compared with test data of the burst time, burst pressure, burst hoop strains, and hoop strain rates. Based on the behaviors from the separate effects test, BISON calculations satisfactorily predicted the cladding deformation behaviors. Sensitivity analysis was conducted to identify highly influential mechanical properties responsible for the cladding failure behavior during the MBT experiments. The results highlight the significance of the cladding's mechanical strength in governing cladding strain, followed by the significance of the mechanical interactions between the pellet and the cladding.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2021

Strength and rupture geometry of un-irradiated C26M FeCrAl under LOCA burst testing conditions

Ferritic iron-chromium-aluminum (FeCrAl) alloys are an accident tolerant fuel candidate to replace the incumbent Zr-based claddings. Nuclear grade FeCrAl alloys are marked by superior high temperature mechanical behavior and exceptional steam oxidation resistance, both of which increase safety margins during accident scenarios. In the present study, the loss of coolant accident (LOCA) burst behaviors of three un-irradiated commercially fabricated cladding materials in a simulated LOCA environment were compared: (1) T35Y2, a 1 st generation nuclear grade FeCrAl, (2) C26M, a 2 nd generation nuclear grade FeCrAl, and (3) Zircaloy-2. Both FeCrAl alloys showed improved mechanical strength and steam oxidation resistance compared to Zircaloy-2. C26M claddings burst at significantly higher temperatures for all tested engineering hoop stresses, had limited ballooning, and demonstrated preferential fuel retention behavior in terms of burst opening area and length. High temperature tensile data for C26M is also presented. For both un-irradiated FeCrAl alloys, it was found that a distinct “threshold” burst stress signified the transition between small and large openings. Finally, higher threshold hoop stresses were associated with higher uniaxial strength for the FeCrAl alloys, indicating that tensile data, rather than creep data, could be useful for predicting rupture size and assessing fuel dispersal concerns.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Oxidation Behavior Comparison of UAM and Conventional Zry-4

Initial hydrothermal corrosion and steam exposures have been completed on ultrasonic additive manufacturing (UAM) Zry4 specimens to compare to wrought Zry4 performance in both normal operation and accident conditions. Slightly higher mass gains were found for the UAM Zry4 specimens in both conditions, but these were generally associated with internal oxidation where delamination of build layers occurred in the UAM material. Further characterization is being completed to conclude this first phase of testing while a second phase is being planned.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Fracture Toughness Characterization of Generation II FeCrAl Alloys after ~18 dpa Irradiation

FeCrAl alloys are promising candidate materials for the accident tolerant fuel (ATF) cladding applications due to their excellent corrosion resistance to the elevated temperature steam environment. Currently, the handbook on FeCrAl material properties contains only limited data regarding the fracture toughness properties of any FeCrAl alloy. This includes alloys currently under investigation within the Advanced Fuels Campaign (AFC) at Oak Ridge National Laboratory (ORNL). In this project, a series of irradiation capsules have been irradiated in the High Flux Isotope Reactor (HFIR) at ORNL with two Generation II FeCrAl candidate alloys, i.e., C06M and C36M, to assess the fracture response of these alloys after neutron irradiation. These alloys represent the “book-end” compositions for C26M, the alloy currently being developed as the leading candidate for LWR cladding. A total of six irradiation capsules were irradiated in HFIR at target temperatures of 200°C, 330°C, and 500°C up to target damage doses of 8 displacements per atom (dpa) and 16 dpa. These damage doses represent the expected middle and end of life damage levels for typical LWR cladding while the irradiation temperature regimes will provide insight into the role of varying microstructural features on the fracture toughness properties of neutron irradiated FeCrAl alloys. To date, irradiation of all capsules has been completed in HFIR. This report summarizes the latest results of microhardness and fracture toughness PIE for the 16 dpa capsules (FCAB2, FCAB4, and FCAB6), for which the measured irradiation conditions were: 204°C/17.6dpa, 343°C/18.3dpa, and 507°C/18.6dpa. The main conclusions of this study can be summarized as follows: 1) After the 204°C/17.6dpa irradiation, both C06M and C36M exhibited significant irradiation hardening and embrittlement 2) After the 343°C/18.3dpa irradiation, both C06M and C36M exhibited small irradiation hardening without irradiation embrittlement 3) After the 507°C/18.6dpa irradiation, both C06M and C36M exhibited irradiation softening without irradiation embrittlement 4) Comparing the microhardness and Master Curve reference temperature T 0q before and after neutron irradiation, we did not observe a linear correlation between the two parameters for both C06M and C36M. This should be mainly due to a flat response of the Master Curve reference temperature T 0q to the irradiations at 166-204°C and 315-343°C ranges 5) C06M showed a lower T 0q , meaning better toughness, than C36M at the unirradiated condition and such trend was kept even after neutron irradiation except for the 166-204°C irradiation where both materials had similar T 0q . 6) In terms of hardening and embrittlement, the irradiation effect on both C06M and C36M appeared to saturate after an irradiation dose of 7 dpa.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Assembly of MiniFuel Targets for Irradiation of U-Mo Fuel Specimens in the High Flux Isotope Reactor

To support the development of advanced low-enriched uranium for use in nuclear reactors, irradiation testing of U-Mo disk specimens was performed at the Oak Ridge National Laboratory (ORNL) High Flux Isotope Reactor (HFIR) to collect experimental irradiation data on this type of fuel at pressurized water reactor–relevant temperatures. U-Mo is a uranium alloy that has superior dimensional stability relative to alpha-phase uranium metal and has a substantially higher uranium density compared to UO 2 . U-Mo disks specimens were fabricated at Idaho National Laboratory and inserted into MiniFuel targets for HFIR irradiation. Three MiniFuel targets were successfully assembled, welded, tested, and delivered to HFIR, along with their quality assurance documentation. The targets were inserted into HFIR’s inner vertical experiment facility within the permanent beryllium reflector. Each target contains six disk specimens and will be irradiated in HFIR for three, four, and eight cycles, with target temperatures between 250 and 500°C. This report summarizes the experiment design, test matrix, pre-characterization of specimens, and experiment assembly.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2021

Demonstration of Dimensional and Microstructural Postirradiation Examination Capabilities on MiniFuel Disk Specimens

This work demonstrates two new MiniFuel postirradiation examination (PIE) capabilities, laser profilometry and serial sectioning, for future use on alpha-U specimens for the upcoming Mini-99 irradiation campaign. Representative U–Mo disk specimens—3 mm in diameter and approximately 0.75 mm in thickness—were subjected to dimensional measurements using standard calipers, as well as a new Keyence CL-3000 series laser profilometry system designed to measure the surface of both sides of the disk simultaneously. The laser profilometry system captured thickness gradients across the specimens as large as 0.2 mm. Additionally, because of the limitations inherent to the use of calipers, caliper measurements consistently overestimated the initial volume of MiniFuel disk specimens compared to the laser profilometry method by up to 5%. However, the results show that optimal data collection and analysis procedures are crucial to avoiding significant artifacts during data collection that can lead to large errors (approximately 10%). Serial sectioning using a combination of ion milling and electron imaging was also demonstrated for the analysis of micron-sized control volumes. Nanometer- to micron-scale porosity was resolved on a representative U–Mo specimen before irradiation, even when the surface of the specimen appeared free of porosity. Future efforts to relate microstructural features (porosity, fission product distributions, and so on) to macroscale effects (dimensional changes, thermal conductivity degradation) require accurate characterization methods such as those demonstrated in this work. These advanced PIE capabilities will be applied to optimized alpha-U specimens for the upcoming Mini-99 neutron irradiation campaign.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗