Decoupling thermal and irradiation effects on grain boundary segregation

Radiation-induced segregation (RIS) is most often measured by peak solute concentration at a boundary. However, this may give an incomplete picture of segregation quantity and phenomena. Radiation-induced and thermal segregation at grain boundaries was investigated in Fe-9.6 at.% Cr after 9 MeV Fe 3+ ion irradiation at 400 °C. The experimental results were compared to kinetic Monte Carlo (KMC) simulations. The study revealed that Cr enrichment (peak segregation) at the grain boundaries was comparable in both the irradiated and non-irradiated conditions, although irradiation resulted in broader segregation profiles in both experiments and simulations, indicating an overall increase in grain boundary segregation due to irradiation. This broadening is attributed to back diffusion into the grain interior. While it is an established phenomenon, this study offers a quantitative evaluation using experimental data and KMC modeling. Further, these results emphasize the importance of analyzing the entire segregation profile and decoupling the thermal and irradiation contributions to solute segregation.

Grain boundary segregation↗

DOE OSTI2025

Grain boundary segregation and chemical ordering in CoCrFeMnNi multi-principal element alloy

Owing to their far-from-dilute compositions, multi-principal element alloys (MPEAs) can exhibit unique combinations of engineering properties. As nearly all MPEAs are polycrystalline aggregates, it is necessary to understand the interactions of various elemental species with grain boundaries (GBs). This is of particular importance in extreme environments, such as radiation and elevated temperatures, where such interactions have implications on the properties of MPEAs. Herein, we employ atomistic simulations to generate a series of [001] asymmetric tilt GBs in a model CoCrFeMnNi MPEA and quantify solute interactions and segregation to these boundaries. We employ the Warren-Cowley order parameters to investigate the interplay between GB segregation and chemical short-range order (SRO). At temperatures above 800 K, simulation results reveal the segregation of Cr and Mn to CoCrFeMnNi GBs and show weak dependence of boundary solute excess on GB geometry, at least for the boundaries explored in this work. At temperatures in the range of 673–800 K, formation of domains rich in Cr is observed at GBs in agreement with experimental observations. Quantitative analysis shows that solute excess of various alloying elements decreases rapidly with the increase in temperature in the range of 1000–1200 K. Furthermore, we show that GB regions exhibit SRO characteristics that are distinct from the bulk crystals, leading to spatial variations in SRO. In broad terms, our study highlights the need to account for GB interactions with alloying elements when designing advanced MPEAs with novel chemistries.

Wang, Yitao [Lehigh University, Bethlehem, PA (Uni↗