Superconducting radio frequency linear collider HELEN

This article discusses a proposed Higgs-Energy LEptoN (HELEN) $e^+e^-$ linear collider based on advanced traveling wave superconducting radio frequency technology. Here, the proposed collider offers cost and AC power savings, smaller footprint (relative to the ILC), and could be built at Fermilab. After the initial physics run at 250 GeV, the collider could be upgraded either to higher luminosity or to higher, up to 500 GeV, energies.

43 PARTICLE ACCELERATORS↗
DOE OSTI2023

Flux Expulsion and Material Properties of Niobium Explored in 644-650 MHz Cavities

Upcoming projects requiring high-Q ~650 MHz medium-to-high-${\beta}$ elliptical cavities drive a need to understand magnetic RF loss mechanisms and mitigations in greater detail. High-temperature annealing and fast-cooldowns have proven effective techniques for promoting magnetic flux expulsion in cavities, however the extent of their effectiveness has been observed to vary between niobium material lot and vendor. We explore the fast-cooldown method, and high-temperature annealing (900{\deg}C) in 644-650 MHz cavities fabricated from two different niobium vendors: Tokyo-Denkai, and Ningxia. which promote flux-expulsion efficiency. Using EBSD and PPMS methods, we aim to trace cavity flux expulsion efficiency to specific, measurable properties of the bulk niobium material, which, if identified, can lead to methods by which the flux expulsion properties of Nb material can be predicted prior to cavity fabrication, and can enable fine-tuning of cavity temperature treatments.

43 PARTICLE ACCELERATORS↗
DOE OSTI2023

Flux expulsion and material properties of Nb

Upcoming projects requiring high-Q ~650 MHz medium-to-high-! elliptical cavities drive a need to understand magnetic RF loss mechanisms and mitigations in greater detail. We explore the fastcooldown method, and high-temperature annealing (900°C) in 644- 650 MHz SRF cavities fabricated from two different niobium vendors: Tokyo-Denkai (TD), and Ningxia (NX). Using EBSD and PPMS methods, we aim to trace cavity flux expulsion efficiency to specific, measurable properties of the bulk niobium material, which, if identified, can lead to methods by which the flux expulsion properties of Nb material can be predicted prior to cavity fabrication.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2023

Electropolishing parameters study for surface smoothening of low-$\beta$650 MHz five-cell niobium superconducting radio frequency cavity

Electropolishing (EP) is applied to niobium (Nb) superconducting radio frequency (SRF) cavities, which are used in particle accelerators for their surface treatment. The EP process for 1.3 GHz cavities has been extensively studied earlier. In this work, a parametric study on EP of low-β (0.61) 650 MHz Nb SRF cavities (LB650), which will be used in pre-production cryomodule for proton improvement plan-II (PIP-II) linear accelerator, was conducted to determine adequate EP conditions for attaining a smooth surface of the cavities. EP performed with the standard parameters and an initial cathode (cathode-I) having a cathode surface area of ~5% of the cavity surface area yielded a rough equator surface of the cavity. The grain step height on the equator weld position was measured to be ~ 32 μm. The rough surface was attributed to preferential grain etching confirmed by a polarization curve showing a linear relationship between the EP current and voltage and the absence of the current plateau region. The cathode was modified to make its surface area twice that of cathode-I. The modified cathode (cathode-M) provided a current plateau region in the corresponding I-V curves measured at different cavity temperatures. The onset voltage for the plateau was found to be higher at higher cavity temperatures. Here this study revealed that even with cathode-M, the standard 18 V was low for EP of such large-sized cavities when the cavity temperature was 18 °C. EP performed at a higher voltage of 22–24.5 V with cathode-M yielded a smooth surface with a grain step height of only 0.6 μm. The applied EP conditions also improved removal uniformity along the cavity length. In contrast to the cavity treated with cathode-I, the cavities treated with cathode-M achieved a significantly higher accelerating gradient (E acc ) in vertical tests conducted in a cryostat at 2 K. The modified EP was found efficient to produce the cavities that achieved E acc of 22.4 MV/m, required by PIP II project in the baseline RF tests, to qualify for further surface processing used to enhance their quality factors.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗