Manganese-rich high entropy oxides for lithium-ion batteries:materials design approaches to address voltage fade
Lithium- and manganese-rich oxides are of interest as lithium-ion battery cathode materials as Mn is earth abundant, low cost, and can deliver high capacity. Herein, a high entropy strategy was used to prepare Mn rich high entropy oxide (HEO) materials by including four additional metals (Ni, Co, Fe and Al) in the compositions using a mild co-precipitation method. Two HEOs (Li x Ni 0.1 Mn 0.6 Co 0.1 Al 0.1 Fe 0.1 O y , where x = 1.5 for HEO-L and x = 0.5 for HEO-H) with layered and spinel-layered hybrid structures were investigated where the morphology, elemental composition, structure, atomic level phase distribution, and electrochemistry were determined. The HEO-L samples involve a Li 2 TMO 3 layered structure with ~39% stacking faults. HEO-H is a hybrid structure comprised of 80 wt% spinel and 20 wt% LiMO 2 layered structure. The high entropy manganese-rich HEO-L showed higher capacity and 93% retention of the average voltage after 100 cycles while HEO-H showed higher capacity retention and near 100% average voltage retention. Finally, operando X-ray absorption spectroscopy revealed that the Ni, Co, and Mn are redox active in both materials while the Fe center remains at the Fe 3+ oxidation state throughout cycling, where the changes in the oxidation states for both materials during discharge were consistent with the delivered electrochemical capacity rationalizing the observed electrochemistry.
Identifying point defects and ordering in the high-entropy layered oxide Li 1.5 MO 3-δ (M=Mn, Al, Fe, Co, Ni) for energy storage applications
High-entropy layered oxides (HELOs) represent a very promising class of next-generation battery cathodes, combining the well-studied properties of layered cathode materials such as LiCoO 2 with the chemical tunability and stability of high-entropy materials. HELO materials often form particles with complex defects and domain structures, complicating accurate characterization of structure and cation mixing. Understanding disorder and order in HELO materials is necessary for understanding their performance and utility as cathodes. Here we demonstrate the characterization of the HELO Li 1.5 MO 3-δ (M = Mn, Al, Fe, Co, Ni), wherein X-ray powder diffraction, transmission electron microscopy imaging, and electron diffraction patterns are analyzed to reveal the presence of ordering in the HELO, with imaging and diffraction simulation employed to compare experimental results to atomic modeling. Finally, without rigorous characterization at the atomic scale, important features such as defect ordering can be easily overlooked and therefore remain unconsidered when interpreting experimental results.
Defect-Driven Configurational Entropy in the High-Entropy Oxide Li 1.5 MO 3-δ
Layered lithiated oxides are promising materials for next generation Li-ion battery cathode materials; however, instability during cycling results in poor performance over time compared to the high capacities theoretically possible with these materials. Here, in this paper, we report the characterizations of a Li 1.47 Mn 0.57 Al 0.13 Fe 0.095 Co 0.105 Ni 0.095 O 2.49 high-entropy layered oxide (HELO) with the Li 2 MO 3 structure where M = Mn, Al, Fe, Co, and Ni. Using electron microscopy and X-ray spectroscopy, we identify a homogeneous Li 2 MO 3 structure stabilized by the entropic contribution of oxygen vacancies. This defect-driven entropy would not be attainable in the LiMO 2 structure sometimes observed in similar materials as a secondary phase owing to the presence of fewer O sites and a 3+ oxidation state for the metal site; instead, a Li 2-γ MO 3-δ is produced. Beyond Li 2 MO 3 , this defect-driven entropy approach to stabilizing novel compositions and phases can be applied to a wide array of future cathode materials including spinel and rock salt structures.
Mechanism of Chalcophanite Nucleation in Zinc Hydroxide Sulfate Cathodes in Aqueous Zinc Batteries
Aqueous Zn-ion batteries with MnO 2 -based cathodes have seen significant attention owing to their high theoretical capacities, safety, and low cost; however, much debate remains regarding the reaction mechanism that dominates energy storage. In this work, we report our electron microscopy study of cathodes containing zinc hydroxide sulfate (Zn 4 SO 4 (OH) 6 ·xH 2 O, ZHS) together with carbon nanotubes cycled in electrolytes containing ZnSO 4 with varied amounts of MnSO 4 incorporated. The primary Mn-containing phase is formed in situ in the cathode during cycling, where a dissolution-deposition reaction is identified between ZHS and chalcophanite (ZnMn 3 O 7 ·3H 2 O). Mechanistic details of this reaction, in which the chalcophanite nucleates then separates from the ZHS flakes as the ZHS dissolves while acting as the primary Zn source for the reaction, are revealed using surface sensitive methods. Importantly, these findings indicate the reaction is local to the ZHS flakes, providing new insight toward the importance of ZHS and the cathode microstructure.
Iridium Incorporation into MnO 2 for an Enhanced Electrocatalytic Oxygen Evolution Reaction
Here, we have investigated the structure and activity of electrocatalysts for the oxygen evolution reaction (OER) that had low loadings of Ir incorporated into the 2D layered MnO 2 , (birnessite, nominally δ-MnO 2 ) and the 3D MnO 2 (pyrolusite, β-MnO 2 ). The Ir-incorporated β-MnO 2 (Ir/β-MnO 2 ) electrocatalysts were prepared for the first time via a thermally induced phase transition of δ-MnO 2 containing 16-22 wt% Ir. This phase transition of δ-MnO 2 to β-MnO 2 was facilitated by the presence of Ir in the structure, as both Ir in IrO 2 and Mn in β-MnO 2 could adopt a thermodynamically favored rutile structure. Extended X-ray absorption fine structure (EXAFS) of Ir/β-MnO 2 showed that the catalyst consisted of Ir substituted into the crystalline β-MnO 2 lattice. 22 wt% Ir/β-MnO 2 (60 μg Ir cm $\ ^{-2}_{geo}$) exhibited an OER overpotential (η) of 337 mV, lower than the η for commercial IrO 2 . This η was constant for 6 h, at 10 mA cm $\ ^{-2}_{geo}$ in 0.5 M H 2 SO 4 . EXAFS, high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and X-ray absorption near edge structure (XANES) showed that 22 wt% Ir/β-MnO 2 had a strained structure containing ~41% Mn 3+ , an OER active species, along with a modified Ir bond covalency consisting of both Ir-O-Ir and Ir-O-Mn.
Simultaneous Elucidation of Solid and Solution Manganese Environments via Multiphase Operando Extended X-ray Absorption Fine Structure Spectroscopy in Aqueous Zn/MnO 2 Batteries