The design and performance of ambient temperature secondary cells based on the titanium disulfide cathode are discussed. These limited performance products were developed for microelectronic applications such as solar rechargeable watches and clocks which require low drain rate and do not require many deep cycles.
Procedure for enhancing operating life and performance of oxygen electrodes in rechargeable metal-oxygen batteries and hydrogen-oxygen fuel cells is discussed. Accumulation of refractory anodic oxide layer and inhibiting effects on oxygen reduction are described. Improvements in service life of batteries by following procedure are explained.
Studies were carried out on a number of factors which may influence the behavior of the platinum electrocatalyst of oxygen electrodes for use in rechargeable metal-oxygen batteries or hydrogen-oxygen fuel cells. The effects of pretreatments for various potentials and added ionic species, which could be present in such systems, were studied with reguard to: (1) the state of surface oxidation, (2) platinum dissolution, (3) the kinetics of oxygen evolution and reduction (including the role of hydrogen peroxide), and (4) changes in porous electrode structure. These studies were carried out on smooth platinum, platinized platinum, and Teflon-bonded platinum black electrodes in carefully purified electrolyte solutions. The main factors which appear to affect rechargeable oxygen electrode performance and life are: (1) the buildup of a refractory anodic layer on extended cycling, and (2) the dissolution of platinum.
A research program is described which consisted of studying the effects of electrode cycling in very pure KOH solutions, with and without controlled additions of impurities, on oxide formation, oxygen evolution kinetics, oxygen reduction kinetics (including hydrogen peroxide formation), and changes in electrode structure. Bright platinum, platinized platinum, and Teflon-bonded platinum black electrodes were studied. Three main problem areas are identified: the buildup of a refractory anodic layer on prolonged cycling, which leads to a degradation of performance; the dissolution and subsequent deposition of dendritic platinum in the separator, leading to short-circuit ing and loss of electrocatalyst; and the disruptive effect of bubbling during gas evolution on charge. Each of these problem areas is analyzed, and remedial solutions are proposed.