Correlations Between In-Line X-ray Diffraction Data and In-Field Critical Current of Long, 4-μm Thick Film REBCO Tapes Made by Advanced MOCVD
REBa 2 Cu 3 O 7-δ (REBCO, RE = rare earth) tapes with high critical current can be very impactful in high magnetic field applications at low temperatures and power applications at high temperatures. A pilot-scale Advanced Metal Organic Chemical Vapor Deposition (MOCVD) method was used to fabricate 50-m-long, 4+μm-thick REBCO tape in a single pass. Critical currents 3.3x that of commercial HTS tapes were achieved at 20 K, 12 T in these 50-m-long tapes. An in-line 2D X-ray Diffraction (XRD) system has been used to assess the quality of the long tapes in real-time, during manufacturing. The key peaks of REBCO, REO, and BZO phases were identified and utilized for tape quality analysis. Furthermore, a 20-m tape made by Advanced MOCVD was tested over its entire length by reel-to-reel (R2R) scanning Hall-probe microscopy (SHPM) at 65 K, 0.25 T, 2 T, and 4 T. 4-mm-wide strands of Advanced MOCVD tapes showed mean critical currents at 65 K of 530 A, 200 A, and 104 A at 0.25 T, 2 T, and 4 T respectively. The combined use of in-line and offline characterization techniques provides a reliable approach for assessing long REBCO tapes during manufacturing, serving as an effective feedback source for quality control in scaled-up REBCO tape deposition processes. This advancement contributes to the production of longer and more uniform high-performance REBCO tapes for large-scale, high-field superconducting applications