NASA NTRS1991

Continuous fiber-reinforced titanium aluminide composites

An account is given of the fabrication techniques, microstructural characteristics, and mechanical behavior of a lightweight, high service temperature SiC-reinforced alpha-2 Ti-14Al-21Nb intermetallic-matrix composite. Fabrication techniques under investigation to improve the low-temperature ductility and environmental resistance of this material system, while reducing manufacturing costs to competitive levels, encompass powder-cloth processing, foil-fiber-foil processing, and thermal-spray processing. Attention is given to composite microstructure problems associated with fiber distribution and fiber-matrix interfaces, as well as with mismatches of thermal-expansion coefficient; major improvements are noted to be required in tensile properties, thermal cycling effects, mechanical damage, creep, and environmental effects.

Mackay, R. A.↗

NASA NTRS1990

Isothermal and nonisothermal fatigue behavior of a metal matrix composite

The isothermal and nonisothermal fatigue resistance of a metal matrix composite (MMC) consisting of Ti-15V-3Cr-3Al-3Sn (Ti-15-3) matrix reinforced by 33 vol pct continuous SiC fibers was investigated. The fibers were nominally oriented parallel to the specimen axis. Isothermal fatigue tests were performed in air at 300 and 550 C. The MMC had good isothermal fatigue resistance at low cyclic stress, with fatigue cracks initiating from fiber-matrix interfaces and foil laminations. At high cyclic stresses, stress relaxation in the matrix reduced isothermal composite fatigue resistance at 550 C. Nonisothermal fatigue loading substantially degraded composite fatigue resistnce. This degradation was produced by a thermomechanical fatigue damage mechanism associated with the fiber-matrix interfaces.

Gabb, T. P.↗

NASA NTRS1990

Coarsening in high volume fraction nickel-base alloys

The coarsening behavior of the gamma-prime precipitate has been examined in high volume fraction nickel-base alloys aged at elevated temperatures for times of up to 5000 h. Although the cube rate law was observed during coarsening, none of the presently available coarsening theories showed complete agreement with the experimental particle size distributions (PSDs). These discrepancies were thought to be due to elastic coherency strains which were not considered by the available models. Increasing the Mo content significantly influenced the PSDs and decreased the coarsening rate of the gamma-prime cubes, as a result of increasing the magnitude of the lattice mismatch. After extended aging times, the gamma-prime cubes underwent massive coalescence into plates at a rate which was much faster than the cuboidal coarsening rate. Once the gamma-prime plates were formed, further coarsening was not observed, and this stabilization of the microstructure was attributed to the development of dislocation networks at the gamma-gamma-prime interfaces.

Mackay, R. A.↗

NASA NTRS1990

Influence of molybdenum on the creep properties of nickel-base superalloy single crystals

The Mo content of an alloy series based on Ni-6 wt pct Al-6 wt pct Ta was systematically varied from 9.8 to 14.6 wt pct, in order to ascertain the influence of Mo on the creep properties of single crystals. The optimum initial gamma-gamma prime microstructure for raft development and creep strength was established in each alloy before testing. It was found that, as the Mo content increased from 9.8 to 14.0 percent, the magnitude of the lattice mismatch increased; upon reaching 14.6 percent, a degradation of mechanical properties occurred due to the precipitation of a third phase. These results suggest that small refractory metal content and initial gamma-prime variations can profoundly affect mechanical properties.

Mackay, R. A.↗

NASA NTRS1989

Analysis of gamma prime shape changes in a single crystal Ni-base superalloy

The microstructural evolution of a commercial single crystal superalloy, NASAIR 100, is analyzed using the existing high-temperature lattice mismatch data and high-temperature moduli obtained from tests on single crystals of gamma and gamma prime. A multiparticle analysis of the microstructural evolution is performed using a novel microstructural lattice simulation technique, MCFET. Under a uniaxial stress, a regular array of gamma prime particles in the simulated microstructure is predicted to coalesce and form a plate morphology, with the broad faces of the plates and stress axis perpendicular in tension but parallel in compression. These results are consistent with changes in gamma prime shape observed in NASAIR 100 following creep testing at 1000 C.

Gayda, J.↗

NASA NTRS1989

Influence of precipitate morphology on intermediate temperature creep properties of a nickel-base superalloy single crystal

The relative creep behavior of cuboidal (as-heat treated) and rafted (precrept at 1000 C) gamma-prime microstructures in the single-crystal Ni-based superalloy NASAIR 100 at 760 C was investigated using SEM and TEM examinations of materials at various stages of creep. It was found that, at high applied stresses, the crystals with cuboidal gamma-prime structure had both lower minimum creep rates and longer rupture lives than the crystals with lamellar gamma-prime. At lower stress levels, the initially cuboidal gamma-prime microstructure maintained a lower creep rate, but exhibited a similar rupture life compared to the prerafted crystals.

Nathal, M. V.↗

NASA NTRS1989

The role of interfacial dislocation networks in high temperature creep of superalloys

The dislocation networks generated during high-temperature creep of several single-crystal nickel-based superalloys are analyzed. The networks continually evolve during creep at relatively low temperatures or eventually reach a more stable configuration at high temperatures. Specifically, the role of these networks in directional coarsening processes are studied, along with their formation kinetics, characteristics, and stability during creep. The results of this study combined with previous findings suggest that the directional coarsening process is strongly influenced by elastic strain energy. The dislocation networks formed during primary creep are found to be stable during all subsequent creep stages. Aspects of these dislocation networks are determined to be a product of both the applied creep stress and coherency strains.

Gabb, T. P.↗

NASA NTRS1988

Lattice parameter variations during aging in nickel-base superalloys

The importance of the state of coherency on measurements of gamma/gamma-prime lattice mismatch has been experimentally demonstrated during aging at 1000 C of specimens of an alloy with composition Ni-(8.6)Cr-(5.3)Al-(10.1)Co-(11.7)W-(1.2)Ti-(0.7)Mo (wt pct). Lattice parameter measurements are given as a function of aging time, and the corresponding sample microstructures are presented. The results show that changes of the two phases during aging did not influence the lattice parameter measurements, indicating that aging specimens to produce a semicoherent gamma/gamma-prime structure provides a good approximation of the true, unconstrained lattice mismatch.

Nathal, M. V.↗

NASA NTRS1987

The stability of lamellar gamma-gamma-prime structures

The stability of stress-annealed gamma/gamma-prime lamellar structures were investigated using three nickel-base single-crystal alloys (the NASAIR 100 and two similar alloys, E and F, containing 5 and 10 wt pct Co, respectively) stress-annealed at 1000 C to form lamellae perpendicular to the applied stress. The rate of the lamellar thickening under various thermal and creep exposures was examined by SEM. For unstressed aging at 1100 C, the lamellar structures of the NASAIR and the E alloys exhibited continuous but slow lamellar coarsening, whereas the lamellae of the alloy F showed pronounced thickening plus spheroidization. Resistance to lamellar thickening was correlated with high magnitudes of lattice mismatch, which promoted a more regular lamellar structure and a finer spacing of misfit dislocations. Specimens which were tension-annealed prior to compressive creep testing exhibited an earlier onset of tertiary creep in comparison with only heat-treated specimens. This was associated with accelerated lamellar coarsening in the stress-annealed specimens.

Nathal, M. V.↗

NASA NTRS1986

Chemical contamination remote sensing

A ground mobile laser test bed system was assembled to assess the feasibility of detection of various types of chemical contamination using Differential Scattering (DISC) and Differential Absorption (DIAL) Lidar techniques. Field experiments with the test bed system using chemical simulants were performed. Topographic reflection and range resolved DIAL detection of vapors as well as DISC detection of aerosols and surface contamination were achieved. Review of detection principles, design of the test bed system, and results of the experiments are discussed.

Carrico, J. P.↗

NASA NTRS1986

Microstructure-property relationships in directionally solidified single crystal nickel-base superalloys

Some of the microstructural features which influence the creep properties of directionally solidified and single crystal nickel-base superalloys are discussed. Gamma precipitate size and morphology, gamma-gamma lattice mismatch, phase instability, alloy composition, and processing variations are among the factors considered. Recent experimental results are reviewed and related to the operative deformation mechanisms and to the corresponding mechanical properties. Special emphasis is placed on the creep behavior of single crystal superalloys at high temperatures, where directional gamma coarsening is prominent, and at lower temperatures, where gamma coarsening rates are significantly reduced. It can be seen that very subtle changes in microstructural features can have profound effects on the subsequent properties of these materials.

Mackay, R. A.↗

NASA NTRS1985

The development of gamma-gamma-prime lamellar structures in a nickel-base superalloy during elevated temperature mechanical testing

The kinetics of the formation and subsequent development of the directional coarsening of the gamma-prime precipitate in model Ni-Al-Mo-Ta superalloy single crystals are examined during tensile creep under various stress levels at 982 and 1038 C. Special attention is given to the gamma and gamma-prime relation to creep time and strain in order to trace the changing gamma-gamma-prime morphology. Directional coarsening of gamma-prime is found to begin during primary creep and its rate is shown to increase with an increase in temperature or stress level. The length of gamma-prime thickness increased linearly with time up to a plateau reached after the onset of steady state creep. The raft thickness, equal to the gamma-prime size, remained constant at this initial value up through the onset of the tertiary creep. The interlaminar spacing indicates the stability of directionally coarsened structure.

Mackay, R. A.↗

NASA NTRS1985

Temperature dependence of gamma-gamma prime lattice mismatch in nickel-base superalloys

High temperature X-ray diffraction techniques were used to determine the gamma-gamma prime lattice mismatch of three different nickel-base superalloys at temperatures between 18 and 1000 C. The measurements were performed on oriented single-crystal disks which had been aged to produce a semicoherent gamma-gamma prime structure. The thermal expansion of the lattice parameters of the gamma and gamma-prime phases was described by a second-order polynomial expression. The expansion of the gamma-prime phase was consistently smaller than that of the gamma phase, which caused the lattice mismatch to become more negative at higher temperatures. It was also shown that high values of lattice mismatch resulted in increased rates of directional gamma-prime coarsening during elevated temperature creep exposure.

Nathal, M. V.↗

NASA NTRS1984

Morphological changes of gamma prime precipitates in nickel-base superalloy single crystals

Changes in the morphology of the gamma prime precipitate were examined during tensile creep at temperatures between 927 and 1038 C in 001-oriented single crystals of a Ni-Al-Mo-Ta superalloy. In this alloy, which has a large negative misfit of -0.80%, the gamma prime particles link together during creep to form platelets, or rafts, which are aligned with their broad faces perpendicular to the applied tensile axis. The dimensions of the gamma and gamma prime phases were measured as directional coarsening developed in an attempt to trace the changing morphology under various stress levels. In addition, the effects of initial microstructure, as well as slight compositional variations, were related to raft development and creep properties. The results showed that directional coarsening of gamma prime began during primary creep, and under certain conditions, continued to develop after the onset of steady-state creep. The length of the rafts increased linearly with time up to a plateau region. The thickness of the rafts, however, remained equal to the initial gamma prime size at least up through the onset of tertiary creep; this is a clear indication of the stability of the finely-spaced gamma-gamma prime lamellar structure. It was found that the single crystals with the finest gamma prime size exhibited the longest creep lives, because the resultant rafted structure had a larger number of gamma-gamma prime interfaces per unit volume of material.

Mackay, R. A.↗

NASA NTRS1984

Factors which influence directional coarsening of Gamma prime during creep in nickel-base superalloy single crystals

Changes in the morphology of the gamma prime precipitate were examined as a function of time during creep at 982 C in 001 oriented single crystals of a Ni-Al-Mo-Ta superalloy. In this alloy, which has a large negative misfit of -0.80 pct., the gamma prime particles link together during creep to form platelets, or rafts, which are aligned with their broad faces perpendicular to the applied tensile axis. The effects of initial microstructure and alloy composition of raft development and creep properties were investigated. Directional coarsening of gamma prime begins during primary creep and continues well after the onset of second state creep. The thickness of the rafts remains constant up through the onset of tertiary creep a clear indication of the stability of the finely-spaced gamma/gamma prime lamellar structure. The thickness of the rafts which formed was equal to the initial gamma prime size which was present prior to testing. The single crystals with the finest gamma prime size exhibited the longest creep lives, because the resultant rafted structure had a larger number of gamma/gamma prime interfaces per unit volume of material. Reducing the Mo content by only 0.73 wt. pct. increased the creep life by a factor of three, because the precipitation of a third phase was eliminated.

Mackay, R. A.↗

NASA NTRS1984

Factors which influence directional coarsening of gamma-prime during creep in nickel-base superalloy single crystals

Changes in the morphology of the gamma prime precipitate were examined as a function of the time during creep at 982 C in 001 oriented single crystals of a Ni-Al-Mo-Ta superalloy. In this alloy, which has a large negative misfit of -0.80 pct., the gamma prime particles link together during creep to form platelets, or rafts, which are aligned with their broad faces perpendicular to the applied tensile axis. The effects of initial microstructure and alloy composition of raft development and creep properties were investigated. Directional coarsening of gamma prime begins during primary creep and continues well after the onset of second state creep. The thickness of the rafts remains constant up through the onset of tertiary creep, a clear indication of the stability of the finely-spaced gamma/gamma prime lamellar structure. The thickness of the rafts which formed was equal to the initial gamma prime size which was present prior to testing. The single crystals with the finest gamma prime size exhibited the longest creep lives, because the resultant rafted structure had a larger number of gamma/gamma prime interfaces per unit volume of material. Reducing the Mo content by only 0.73 wt. pct. increased the creep life by a factor of three, because the precipitation of a third phase was eliminated.

Mackay, R. A.↗

NASA NTRS1983

The development of directional coarsening of the gamma-prime precipitate in superalloy single crystals

A study has been made of the kinetics of the directional coarsening of the gamma-prime precipitates in Ni-5.8Al-14.6Mo-6.2Ta single crystals during creep at 982 C. In this alloy, which is characterized by a large negative lattice misfit between the gamma-prime precipitate and the gamma matrix, the formation of gamma-prime rafts begins during primary creep, and the rafts grow in length as the deformation proceeds into steady-state creep. After that, the length of the rafts stabilizes. The thickness of the rafts remains constant from primary up to tertiary creep. The directional coarsening behavior of the alloy studied is similar to that of a more conventional single-crystal superalloy having a substantially smaller negative misfit.

Mackay, R. A.↗

NASA NTRS1982

The influence of orientation on the stress rupture properties of nickel-base superalloy single crystals

Constant load creep rupture tests were performed on MAR-M247 single crystals at 724 MPa and 774 C where the effect of anisotropy is prominent. The initial orientations of the specimens as well as the final orientations of selected crystals after stress rupture testing were determined by the Laue back-reflection X-ray technique. The stress rupture lives of the MAR-M247 single crystals were found to be largely determined by the lattice rotations required to produce intersecting slip, because second-stage creep does not begin until after the onset of intersecting slip. Crystals which required large rotations to become oriented for intersecting slip exhibited the shortest stress rupture lives, whereas crystals requiring little or no rotations exhibited the lowest minimum creep rates, and consequently, the longest stress rupture lives.

Mackay, R. A.↗