Transforming nanoscale VO 2 (B) into a scalable sodium-ion electrode
The intermittent nature of renewable energies requires highly reliable grid-level energy storage approaches. A critical consideration in developing this technology is the areal capacity which determines battery performance and influences the cost of battery technology. Of related importance is finding new ways of developing scalable electrodes. In recent years, three-dimensional (3D) printing of conductive scaffolds has emerged as an alternative to overcome the scalability limitations of commercial tape cast electrodes. The research carried out in the current study demonstrates a successful scalability pathway for nanoscale VO 2 (B), a desirable cathode for sodium-ion batteries which has a nano-flower morphology with a crystallite size < 20 nm. By electrodepositing VO 2 (B) onto a graphene aerogel scaffold, we were able to achieve mass loading of over 100 mg·cm −2 and still possess an areal capacity of 10 mAh·cm −2 at a current density of 5 mA·cm −2 . Moreover, after 1000 cycles, these electrodes retained 75% to 80% of their initial capacity. Even at high loading levels, the electrodeposited VO 2 (B) exhibits pseudocapacitive material signatures such as a box-like voltammetry response, linear galvanostatic response, and no phase change upon lithiation. The scalability of the VO 2 (B) electrode is demonstrated in a series of experiments which show the areal capacity to scale upon increase in both mass loading and electrode thickness, with only small changes in specific capacity. Furthermore, this study establishes that nanoscale materials can be scaled up to achieve thick electrodes without compromising their electrochemical properties.