Uranium Processing Signatures for Nuclear Forensics (NA22 End of FY23 Report)
A vacuum induction melting (VIM) furnace was used to produce an ~120 kg depleted uranium (DU) rod in November 2021 from well characterized feedstock to investigate the separation of thorium (Th) and protactinium (Pa) from uranium (U) during U metal casting and quantify the behavior of the 230 Th/ 234 U and 231 Pa/ 235 U radiochronometry systems. This work suggested that while 234 Th, measured by gamma spectrometry, appears to segregate to the top and surface of the rod, the concentration of 230 Th determined by isotope dilution mass spectrometry (IDMS) in drill turnings from multiple locations in the rod, including the hot top, is relatively consistent. To evaluate whether Th is potentially enriched at only the very outer surface of the cast DU rod relative to the bulk material in the cast rod, thin surface samples were collected from the cast DU rod. Locations sampled included the inner diameter (ID) and outer diameter (OD) of the bottom of the casting and the ID, OD, and top face of the hot top (very top of the casting). The locations are shown in Figure 1. Four samples were taken from each location at different depths in the cast material. Each cut took approximately 0.03 – 0.05” off of the casting.