DOE OSTI2025

Tailoring the Reaction Heterogeneity for Robust Li‐Rich Cathodes

The practical application of Li-rich Mn-based layered oxides (LLO) cathode is hindered by severe capacity and voltage degradation resulting from severe oxygen release and irreversible phase transition. In this work, the reaction heterogeneity, which describes the spatially resolved electrochemical divergence within individual cathode particles, is engineered through compositional gradient design to couple Li + transport kinetics and the anion redox activity between particle interiors and surfaces. It is revealed that Co/Mn concentration gradient within particles creates heterogeneous phase content distribution and structural ordering, inducing surface-bulk reaction heterogeneity that significantly impacts the overall electrochemical performance. Specifically, Li 2 MnO 3 -poor and Co-enriched surface effectively mitigates the oxygen loss and enhances electrochemical reaction kinetics, benefited from the reduced surface redox reactivity and induced highly ordered intra-layered cationic arrangement. Meanwhile, the Li 2 MnO 3 -enriched core with slight Li/Ni intermixing provides high reversible capacity and strong mechanical stability. Consequently, the greatly enhanced anion redox reversibility, Li + diffusion dynamics, and structure stability endow LLO with exceptional electrochemical properties, showing a capacity retention of 86.0% and a reduced voltage decay of 0.518 mV per cycle after 500 cycles at 1 C. This work provides a valuable strategy to tailor the redox chemistry and achieve robust LLO.

25 ENERGY STORAGE↗

DOE OSTI2025

Isotope-dependent Tafel analysis probes proton transfer kinetics during electrocatalytic water splitting

Proton transfer plays an important role in both hydrogen and oxygen evolution reactions during electrocatalytic water splitting to produce green hydrogen. However, directly adapting the conventional proton/deuterium kinetic isotope effect to study proton transfer in heterogeneous electrocatalytic processes is challenging. Here we propose using the shift in the Tafel slope between protic and deuteric electrolytes, or the Tafel slope isotope effect, as an effective probe of proton transfer characteristics. Comparison of the Tafel slope isotope effect for diverse hydrogen and oxygen evolution reaction electrocatalysts in different pH environments reveals that proton transfer is both pH and structure dependent. Using ruthenium oxide as an example, we show that local structure modification can change the rate-determining step from an electrochemical, concerted proton–electron transfer step to a chemical step and improve the oxygen evolution activity in acid. The isotope-dependent Tafel analysis will facilitate a better understanding of the proton transfer behaviours during electrocatalytic processes and provide guidance for designing efficient electrocatalysts.

Chemistry↗

DOE OSTI2025

Intralattice-bonded phase-engineered ultrahigh-Ni single-crystalline cathodes suppress strain evolution

Single crystallization remains a debated strategy for advancing Ni-rich cathode materials. While it mitigates particle cracking and improves tap density by eliminating particle boundaries, extended diffusion pathways introduce volumetric and lattice distortions, compromising electrochemical and structural stability. These challenges hinder the commercialization of high-Ni single-crystal cathodes, calling for a reassessment of their viability. Here, in this study, we report a structural design: intralattice-bonded phase single-crystal LiNi 0.92 Co 0.03 Mn 0.05 O 2 (IBP-SC92). This architecture maintains structural integrity while shortening diffusion pathways, resulting in almost zero electrochemical degradation during cycling. The robust structure and fast ion transport mitigate lattice strain, as confirmed by multiscale high-resolution diffraction and imaging techniques, preventing intragranular cracks and irreversible phase transitions. As a result, IBP-SC92 shows outstanding cycling stability, with nearly 100% capacity retention after 100 cycles in half cells and 94.5% retention after 1,000 cycles in full cells. This redefined single-crystal cathode represents a significant step towards the industrial adoption of high-energy-density materials.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Modulating Surface Anionic Redox Chemistry toward Highly Stable Li-Rich Cathodes with Negligible Oxygen Loss

Low initial Coulombic efficiency and severe capacity/voltage fading during cycling caused by serious irreversible oxygen release, especially in the initial cycle, and resultantly induced unstable electrode/electrolyte interfacial chemistry, largely prohibit the commercial application of high-capacity Li-rich layered oxide cathodes (LLOs). Here, in this work, a dual reductive gas interface cotreatment strategy is applied to regulate the lattice oxygen redox activity and reversibility with a multiple defective structure design including Li/O/TM (TM = transition metal) vacancies and the intrinsic TM doping as well as a full-surface protective layer, which can suppress the irreversible TM migration and then undesirable phase transformation, resisting the corrosion of electrolyte during cycling effectively. Importantly, the introduced reversible SO 3 2- /SO 4 2- redox couple that provides extra capacity compensation could alleviate the distortion of oxygen-central octahedral structure and structural collapse caused by immoderate oxygen oxidation. Thus, the lattice oxygen redox chemistry is optimized, with negligible oxygen loss during the initial cycle. And the designed AS-LLO cathode with greatly enhanced structure stability shows high-capacity retentions of 99.2% at 0.3C after 100 cycles and 82.4% even after 1000 cycles at 5C. This work provides a guideline for manipulating the oxygen redox chemistry to achieve long-lifespan Li-rich layered oxide cathodes for high-energy-density lithium batteries.

25 ENERGY STORAGE↗