The role of thermal shock in cyclic oxidation

The effect of thermal shock on the spalling of oxides from the surfaces of several commercial alloys was determined. The average cooling rate was varied from approximately 240 C per second to less than 1.0 C per second during cyclic oxidation tests in air. The tests consisted of one hundred cycles of one hour at the maximum temperature (1100 or 1200 C). The alloys were HOS-875, TD-Ni, TD-NiCrAl, IN-601, IN-702, and B-1900 plus Hf. All of these alloys exhibited partial spalling within the oxide rather than total oxide loss down to bare metal. Thermal shock resulted in deformation of the metal which in turn resulted, in most cases, in changing the oxide failure mode from compressive to tensile. Tensile failures were characterized by cracking of the oxide and little loss, while compressive failures were characterized by explosive loss of platelets of oxide. This behavior was confirmed by examination of mechanically stressed oxide scales. The thermally shocked oxides spalled less than the slow cooled samples with the exception of TD-NiCrAl. This material failed in a brittle manner rather than by plastic deformation.

Lowell, C. E.↗

Effect of a chromium-containing fuel additive on hot corrosion

Four cast superalloys (one cobalt-base and three nickel-base) were tested at 900 C for 100 h in Mach 0.3 combustion gases. 5 ppm of synthetic sea salt were added to the gases in the combustion chamber. Several types of thermal cycle and washing procedures were employed. Similar tests were made with the addition of 300 ppm of a chromium-containing fuel additive. In both sets of tests the extent of hot corrosion was evaluated by specific weight change and metal recession. In general, the chromium additive in the fuel reduced the extent of hot (salt) corrosion but did not eliminate it. The percentage reduction of hot corrosion attack was similar for all four alloys. As great a reduction of hot corrosion was achieved by reducing the number of thermal cycles during the test from 100 to 5 or 6. The effect of washing the alloys every ten cycles as opposed to the end of the test was erratic; some alloys were attacked slightly more, others somewhat less. A NiCrAlY coating was found to be more effective in reducing hot corrosion than either the fuel additive or the washing schedule.

Lowell, C. E.↗

High temperature environmental effects on metals

The current status of knowledge and ability to predict high-temperature environmental attack of metals is reviewed with particular reference to the gas turbine engine. Environmental attack is caused by high temperatures, combustion products, and impurities. A schematic representation of life-limiting factors of turbine components shows that environmental attack can lead to very early failures. Attention is given to high-temperature oxidation with prevailing modes of oxidation attack, and to hot corrosion and other impurity effects. Erosion attack results from the direct mechanical removal of component material by impact of hard substances like ash, sand, or dirt. Solutions to hot-corrosion problems can be found semiempirically by using improved alloys or ceramics, protective surface coatings, additives to the engine environment, and air/fuel cleanup to eliminate detrimental impurities.

Grisaffe, S. J.↗

Burner rig alkali salt corrosion of several high temperature alloys

The hot corrosion of five alloys was studied in cyclic tests in a Mach 0.3 burner rig into whose combustion chamber various aqueous salt solutions were injected. Three nickel-based alloys, a cobalt-base alloy, and an iron-base alloy were studied at temperatures of 700, 800, 900, and 1000 C with various salt concentrations and compositions. The relative resistance of the alloys to hot corrosion attack was found to vary with temperature and both concentration and composition of the injected salt solution. Results indicate that the corrosion of these alloys is a function of both the presence of salt condensed as a liquid on the surface and of the composition of the gas phases present.

Deadmore, D. L.↗

High Velocity Oxidation and Hot Corrosion Resistance of Some ODS Alloys

Several oxide dispersion strengthened (ODS) alloys were tested for cyclic, high velocity, oxidation, and hot corrosion resistance. These results were compared to the resistance of an advanced, NiCrAl coated superalloy. An ODS FeCrAl were identified as having sufficient oxidation and hot corrosion resistance to allow potential use in an aircraft gas turbine without coating.

Lowell, C. E.↗

Plugging of cooling holes in film-cooled turbine vanes

The plugging of vane cooling holes by impurities in a marine gas turbine was closely simulated in burner rig tests where dopants were added to the combustion products of a clean fuel (Jet-A). Hole plugging occurred when liquid phases, resulting from the dopants, were present in the combustion products. Increasing flame temperature and dopant concentration resulted in an increased rate of deposition and hole plugging.

Deadmore, D. L.↗

The effect of delta T /oxidizing temperature minus cooling temperature/ on oxide spallation

Several alloys (one iron base and five nickel base) were cyclically oxidized in a series of tests in which the higher temperature (1100 or 1200 C) of the cycle was fixed at a level to allow ample oxidation in reasonable time and the lower temperature was variable to allow cycle temperature differences of up to 1400 C. For all nickel alloys, as delta T increased the extent of spallation increased. This effect was attributed to thermal expansion mismatches between the oxide and the nickel substrate. The FeCrAl alloy was not sensitive to delta T and resisted spalling at delta T levels to 1400 C. FeCrAl, and the Al2O3 scale which forms on it, have thermal expansion coefficients which are substantially more alike than any of the other oxide-metal combinations tested.

Deadmore, D. L.↗

High temperature environmental effects on metals

The gas turbine engine was used as an example to predict high temperature environmental attack on metals. Environmental attack in a gas turbine engine derives from high temperature, combustion products of the air and fuel burned, and impurities. Of all the modes of attack associated with impurity effects, hot corrosion was the most complicated mechanistically. Solutions to the hot corrosion problem were sought semi-empirically in: (1) improved alloys or ceramics; (2) protective surface coating; (3) use of additives to the engine environment; and (4) air/fuel cleanup to eliminate harmful impurities.

Grisaffe, S. J.↗

Toward more environmentally resistant gas turbines - Progress in NASA-Lewis programs

The paper surveys programs for improving the environmental resistance of gas turbine and power system materials to oxidation and hot corrosion. A computer program Corest has been produced which provides an initial method for predicting long-time metal loss using short-time oxidation data. The role of the coefficient of thermal expansion mismatch on oxide spallation is being studied. A paralinear oxidation attack model in conjunction with regression analysis of weight change data has been applied to the study of oxidation and hot corrosion attack of some Ni-Cr-Al system alloys. Oxide-dispersion strengthened alloys based on the Ni-Cr-Al system are being developed. Sodium sulfate formation during turbine combustion is being investigated from a thermodynamic viewpoint.

Lowell, C. E.↗

Effect of a chromium-containing fuel additive on hot corrosion

Four superalloys were tested at 900 C in high velocity combustion gases containing synthetic sea salt and, in some cases, a chromium containing fuel additive. While the additive reduced hot corrosion of the alloys over the 100 hour test period, the attack was not eliminated nor was the mode of attack changed. Reduction of the number of thermal cycles had as large a beneficial effect as the Cr additive. Intermittent washing during testing had either small beneficial or adverse effects depending on the alloy.

Lowell, C. E.↗

Resistance of nickel-chromium-aluminum alloys to cyclic oxidation at 1100 C and 1200 C

Nickel-rich alloys in the Ni-Cr-Al system were evaluated for cyclic oxidation resistance in still air at 1,100 and 1,200 C. A first approximation oxidation attack parameter Ka was derived from specific weight change data involving both a scaling growth constant and a spalling constant. An estimating equation was derived with Ka as a function of the Cr and Al content by multiple linear regression and translated into countour ternary diagrams showing regions of minimum attack. An additional factor inferred from the regression analysis was that alloys melted in zirconia crucibles had significantly greater oxidation resistance than comparable alloys melted otherwise.

Barrett, C. A.↗

Toward more environmentally resistant gas turbines: Progress in NASA-Lewis programs

A wide range of programs are being conducted for improving the environmental resistance to oxidation and hot corrosion of gas turbine and power system materials. They range from fundamental efforts to delineate attack mechanisms, allow attack modeling and permit life prediction, to more applied efforts to develop potentially more resistant alloys and coatings. Oxidation life prediction efforts have resulted in a computer program which provides an initial method for predicting long time metal loss using short time oxidation data by means of a paralinear attack model. Efforts in alloy development have centered on oxide-dispersion strengthened alloys based on the Ni-Cr-Al system. Compositions have been identified which are compromises between oxidation and thermal fatigue resistance. Fundamental studies of hot corrosion mechanisms include thermodynamic studies of sodium sulfate formation during turbine combustion. Information concerning species formed during the vaporization of Na2SO4 has been developed using high temperature mass spectrometry.

Lowell, C. E.↗

High gas velocity oxidation and hot corrosion testing of oxide dispersion-strengthened nickel-base alloys

Several oxide dispersion strengthened (ODS) nickel-base alloys were tested in high velocity gases for cyclic oxidation resistance at temperatures to 1200 C and times to 500 hours and for hot corrosion resistance at 900 C for 200 hours. Nickel-chromium-aluminum ODS alloys were found to have superior resistance to oxidation and hot corrosion when compared to bare and coated nickel-chromium ODS alloys. The best of the alloys tested had compositions of nickel - 15.5 to 16 weight percent chromium with aluminum weight percents between 4.5 and 5.0. All of the nickel-chromium-aluminum ODS materials experienced small weight losses (less than 16 mg/sq cm).

Deadmore, D. L.↗

Thermal expansion in the nickel-chromium-aluminum and cobalt-chromium-aluminum systems to 1200 degrees C

Thermal expansion data were obtained on 12 Ni-Cr-Al and 9 Co-Cr-Al alloys by high temperature X-ray diffraction. The data were computer fit to an empirical thermal expansion equation developed in the study. It is shown that the fit is excellent to good, and that the expansion constants depend on phase but not on composition. Phases for the Ni-Cr-Al system and Co-Cr-Al system are given. Results indicate that only alpha Cr has an expansion constant low enough to minimize oxide spalling or coating cracking induced by thermal expansion mismatch.

Lowell, C. E.↗

Comparison of isothermal and cyclic oxidation behavior of twenty-five commercial sheet alloys at 1150 C

Twenty-five commercial nickel-, iron-, and cobalt-base sheet alloys incorporating chromium or chromium and aluminum additions for oxidation resistance were tested at 1150 C in air for 100 hr in both isothermal and 1-hr cyclic furnace exposures. The alloys were evaluated by sample specific weight change, by type of scale formed, by amount and type of spall, and by sample thickness change and microstructure.-

Barrett, C. A.↗

Effects of silicon additions on oxidation and mechanical behavior of the nickel-base superalloy B-1900

Test specimens with nominal additions of Si were tested in oxidation, thermal fatigue, sulfidation, tension, and stress rupture, and were also extensively studied metallographically. Alloy B-1900 modified with 0.6- or 1.2-wt% Si exhibited oxidation resistance equivalent to that of aluminide-coated B-1900 during cyclic, high-gas-velocity oxidation tests. Resistances to thermal fatigue and sulfidation were improved by the Si additions, but were not superior to aluminide-coated B-1900. Stress-rupture tests at 1000 C of specimens given the standard heat treatment to simulate an aluminide coating cycle showed Si to be detrimental. However, application of another heat treatment increased the rupture life of the alloy with 0.6-wt% Si to that of the unmodified B-1900 given the standard heat treatment.

Miner, R. V., Jr.↗