Engineering topics
Publications and source records attributed to Louks, Amy E..
Although a harsher condition, degradation of perovskite solar cells in an open-circuit condition is related to the performance in a quasi-maximum power point condition. Further, shadow masks should be used during illuminated stability studies.
Dunfield et al. discuss various options for satisfying the ISOS light stability series (ISOS-L-#) of tests, a homebuilt testing apparatus and software suite for such tests, and a case study.
Metal halide perovskite photovoltaic performance required for commercial technology encompasses both efficiency and stability. Advances in both these parameters have recently been reported; however, these strategies are often difficult to directly compare due to differences in perovskite composition, device architecture, fabrication methods, and accelerated stressors applied in stability tests. In particular, it is found that there is a distinct lack of elevated temperature, operational (light and bias) stability data. Furthermore, significant testing is required to understand the interactions when combinations are used (e.g., additives used with posttreatments). Herein, individual and combined additive, posttreatment, and contact layer strategies from recent literature reports under standardized operational stability tests of p-i-n CsMAFA perovskites at 70 degrees C are evaluated. Through analysis of over 1000 devices, it is concluded that the hole-transport layer (HTL) is the most significant component impacting elevated temperature operational stability. This analysis motivates future development of high-performance HTLs.
The development of highly stable and efficient wide-bandgap (WBG) perovskite solar cells (PSCs) based on bromine-iodine (Br–I) mixed-halide perovskite (with Br greater than 20%) is critical to create tandem solar cells. However, issues with Br–I phase segregation under solar cell operational conditions (such as light and heat) limit the device voltage and operational stability. This challenge is often exacerbated by the ready defect formation associated with the rapid crystallization of Br-rich perovskite chemistry with antisolvent processes. We combined the rapid Br crystallization with a gentle gas-quench method to prepare highly textured columnar 1.75–electron volt Br–I mixed WBG perovskite films with reduced defect density. Here, with this approach, we obtained 1.75–electron volt WBG PSCs with greater than 20% power conversion efficiency, approximately 1.33-volt open-circuit voltage (V oc ), and excellent operational stability (less than 5% degradation over 1100 hours of operation under 1.2 sun at 65°C). When further integrated with 1.25–electron volt narrow-bandgap PSC, we obtained a 27.1% efficient, all-perovskite, two-terminal tandem device with a high V oc of 2.2 volts.
Metal halide perovskite solar cells have reached a critical point in their development. At a current certified record efficiency of 25.7% for a single-junction, research-scale cell, they now garner serious attention from the solar cell industry as a promising route to widespread, low-cost photovoltaics in single- or tandem-junction configurations. However, more work to demonstrate their durability under real-world outdoor test conditions is necessary to ensure the long-term success and deployment of the technology. Differences in chemistry, processes, and their combination result in unique performance limiters for both efficiency and stability. Further, as many active formulations and layer/cell stack combinations are sensitive to temperature, air, and moisture, it is important to separate intrinsic limitations to stability relative to these extrinsic sources. This presents a particular need for the development of an appropriate and reliable package for environmental (i.e., accelerated and outdoor) testing that will permit these different factors to be evaluated and understood.
All-perovskite tandem solar cells are promising for achieving photovoltaics with power conversion efficiencies above the detailed balance limit of single-junction cells, while retaining the low cost, light weight and other advantages associated with metal halide perovskite photovoltaics. However, the efficiency and stability of all-perovskite tandem cells are limited by the Sn-Pb-based narrow-bandgap perovskite cells. Here we show that the formation of quasi-two-dimensional (quasi-2D) structure (PEA) 2 GAPb 2 I 7 from additives based on mixed bulky organic cations phenethylammonium (PEA+) and guanidinium (GA+) provides critical defect control to substantially improve the structural and optoelectronic properties of the narrow-bandgap (1.25 eV) Sn-Pb perovskite thin films. Additionally, this 2D additive engineering results in Sn-Pb-based absorbers with low dark carrier density (~1.3 x 10 14 cm -3 ), long bulk carrier lifetime (~9.2 us) and low surface recombination velocity (~1.4 cm s -1 ), leading to 22.1%-efficient single-junction Sn-Pb perovskite cells and 25.5%-efficient all-perovskite two-terminal tandems with high photovoltage and long operational stability.