Durable and High-Performance SOECs Based on Proton Conductors for Hydrogen Production

Proton-conducting solid oxide electrolysis cells (P-SOECs) are a promising technology for cost-effective and efficient production of green hydrogen. Breakthroughs in materials development, optimization of cell structure, and achievement of high performance and durability are essential to significantly increase the commercial competitiveness of these technologies. The main objective of this project is to gain scientific knowledge for the rational design, fabrication, and demonstration of a robust, highly efficient, and low-cost SOEC technology based on a proton-conducting electrolyte membrane for hydrogen production. We focused on better understanding the degradation mechanisms of proton-conducting electrolytes, air electrodes, and catalyst materials under electrolysis mode to develop an effective strategy for rationalizing new materials that are vital for enhancing cell performance and durability. The scope includes enhancing the performance and durability of the electrolyte and electrode materials under realistic operating conditions, developing highly active and robust catalysts to minimize electrode losses while improving tolerance to contaminant poisoning, revealing the mechanism of enhanced activity and stability of the catalyst, and understanding the underlying degradation mechanisms. In addition, various characterization techniques were employed to gain a fundamental understanding of the materials’ behavior and their impact on cell performance, providing vital information to guide materials discovery and cell design. After defect chemistry engineering, the optimized donor and acceptor co-doped electrolytes BaMo/W 0.03 Ce 0.71 Yb 0.26 O 3-δ (BM/W03) showed substantially improved chemical stability against high concentrations of CO 2 and H 2 O compared to the state-of-the-art electrolyte (BaZr 0.1 Ce 0.7 Y 0.1 Yb 0.1 O 3-δ , BZCYYb1711) while maintaining comparable ionic conductivity and ionic transference number. To bypass the inherent trade-off between conductivity and chemical stability, we fabricated a bi-layer electrolyte composed of BZCYYb1711 coated with a highly-stable thin layer of BaHf 0.83 Yb 0.17 O 3-δ (BHYb). This bi-layer electrolyte displayed excellent chemical stability against high concentration CO 2 ; there was no detectable formation of BaCO 3 after exposure to 97% CO 2 (with 3% H 2 O) at 500 °C for 1000 hours and the rate of degradation in resistance was about 0.4% per 1,000 hours (kh). In contrast, the same BZCYYb1711 electrolyte without a BHYb coating degraded significantly under the same testing conditions; the degradation rate was increased to 5.1%/kh. In addition, a triple conducting air electrode Ba 0.9 Pr 0.1 Hf 0.1 Y0.1Co 0.8 O 3-δ (BPHYC) was developed by heavily doping transition metal ions into a proton-conducting material. This air electrode material, composed of 3 distinct phases, exhibits superior electrocatalytic activity due to the synergistic effect from the three component phases. Moreover, an active and durable catalyst, La 2 Ni 0.5 Fe 0.5 O 4+δ (LNF), was developed, showing excellent catalytic activity and contaminant tolerance, with a degradation rate of only 0.49%/kh when exposed to high concentrations of steam and Cr. Finally, single cells were constructed from the best electrolytes, electrodes, and catalyst coatings developed in this project. These cells demonstrated superior high current density at a given cell voltage, high roundtrip efficiency, and remarkable durability (up to 1000 hours of operation).

08 HYDROGEN↗
DOE OSTI2024

A Highly Efficient and Affordable Hybrid System for Hydrogen and Electricity Production (Final Project)

The pursuit of clean, secure, and sustainable energy has sparked significant interest in fuel cells for power generation and electrolyzer cells for hydrogen production. Among all types of fuel and electrolyzer cells, solid oxide cells (SOCs) have emerged as promising candidates due to their high efficiency and versatility. However, conventional oxygen-ion conductive SOCs face several challenges related to their performance and durability associated with their high-temperature operation (≥ 800 ºC). This has led to a growing interest in intermediate-temperature (≤ 650 ºC) proton-conducting solid oxide cells (p-SOCs) as potential alternatives. In collaboration between Phillips 66 and Georgia Tech, this project aims to achieve a 1 kW p-SOCs system to demonstrate the commercial viability of efficient SOC systems. This report addresses four primary areas and key challenges we overcame: (1) development of efficient and durable proton-conducting electrolyte (e.g., BaHf 0.1 Ce 0.7 Yb 0.2 O 3-δ ) and electrode/catalyst materials, (2) large area cell fabrication (10 x 10 cm 2 ), (3) scalable stack design and building (250 W and 1 kW), and (4) demonstration of a 1 kW prototype system. Notably, significant challenges faced during the large area cell fabrication process were addressed by achieving cell flatness, improving fabrication yield, and ensuring electrode/electrolyte interfacial adhesion. Stack designs were also developed, focusing on reducing contact resistance and optimizing stack components (e.g., sealants). These efforts resulted in the achievement of high performance and durability with promising outputs of 250 W and 1 kW. Furthermore, the integration of these stacks into a fuel-powered system was explored, with refinements made to heat management, as well as to pressure and heating conditions. The results demonstrated the potential applicability of our p-SOC technology in commercial energy storage and power generation systems. Additionally, the report discusses techno-economic analysis and a market transformation plan, aiming to evaluate and advance the commercial feasibility of this technology.

25 ENERGY STORAGE↗
DOE OSTI2024

Phase segregation of a composite air electrode unlocks the high performance of reversible protonic ceramic electrochemical cells

One breakthrough in developing highly efficient air electrodes for reversible protonic ceramic electrochemical cells (R-PCECs) is optimizing the sluggish oxygen reduction and water oxidation reactions. Here, we present a novel composite material with a nominal formula of high-entropy Ce 0.2 Ba 0.2 Sr 0.2 La 0.2 Ca 0.2 CoO 3–δ (CBSLCC) that spontaneously self-assembles to three-phase electrocatalysts composed of deficient Ce 0.2–y Ba 0.2 Sr 0.2–x La 0.2–x Ca 0.2 CoO 3–δ (CD-CBSLCC), CeO 2 , and La 0.5 Sr 0.5 CoO 3–δ (LSC). Mechanistic studies corroborate that oxygen reduction may occur on entire air electrode surfaces, followed by water formation preferentially at or near CD-CBSLCC. The CeO 2 phase could provide or consume protons to facilitate the oxygen evolution/reduction kinetics in R-PCECs. The developed electrodes demonstrate a record-high electrochemical performance in dual modes of fuel cells and electrolysis cells, delivering a peak power density of 1.66 W cm –2 at 600 °C and a current density of –1.76 A cm –2 at 1.3 V and 600 °C. Finally, excellent operational stabilities of the fuel cell (200 h at 600 °C), electrolysis cell (200 h at 600 °C), and reversible cycling (548 h at 550 °C) provide a promising and reliable step towards realizing the commercialization of R-PCECs.

30 DIRECT ENERGY CONVERSION↗
DOE OSTI2024

Harnessing High‐Throughput Computational Methods to Accelerate the Discovery of Optimal Proton Conductors for High‐Performance and Durable Protonic Ceramic Electrochemical Cells

Abstract The pursuit of high‐performance and long‐lasting protonic ceramic electrochemical cells (PCECs) is impeded by the lack of efficient and enduring proton conductors. Conventional research approaches, predominantly based on a trial‐and‐error methodology, have proven to be demanding of resources and time‐consuming. Here, this work reports the findings in harnessing high‐throughput computational methods to expedite the discovery of optimal electrolytes for PCECs. This work methodically computes the oxygen vacancy formation energy (E V ), hydration energy (E H ), and the adsorption energies of H 2 O and CO 2 for a set of 932 oxide candidates. Notably, these findings highlight BaSn x Ce 0.8‐x Yb 0.2 O 3‐δ (BSCYb) as a prospective game‐changing contender, displaying superior proton conductivity and chemical resilience when compared to the well‐regarded BaZr x Ce 0.8‐x Y 0.1 Yb 0.1 O 3‐δ (BZCYYb) series. Experimental validations substantiate the computational predictions; PCECs incorporating BSCYb as the electrolyte achieved extraordinary peak power densities in the fuel cell mode (0.52 and 1.57 W cm −2 at 450 and 600 °C, respectively), a current density of 2.62 A cm −2 at 1.3 V and 600 °C in the electrolysis mode while demonstrating exceptional durability for over 1000‐h when exposed to 50% H 2 O. This research underscores the transformative potential of high‐throughput computational techniques in advancing the field of proton‐conducting oxides for sustainable power generation and hydrogen production.

08 HYDROGEN↗
DOE OSTI2023

Protonic ceramic materials for clean and sustainable energy: advantages and challenges

In recent years, the hydrogen economy has been strongly favoured by governmental and industrial bodies worldwide. A tremendous number of papers are published every year on different aspects of protonic ceramic electrochemical cells (PCECs) due to their lower operation temperature, easier reversible operation, and brighter prospects for further development. While new progress is being made continuously, many critical challenges remain. The effort on PCEC investigation could be more aligned for greater collective impact, e.g. the academic community could devote more effort to overdue critical problems but less to incremental improvements. This review aims to provide some insightful perspectives on critical challenges facing the development of PCECs, to sort out priorities in future effort, and to suggest promising directions to pursue. In this way, it is hoped that the technical readiness level of PCECs might advance more quickly, toward field demonstrations and commercialization for a clean and sustainable energy era.

36 MATERIALS SCIENCE↗
DOE OSTI2023

A reversible perovskite air electrode for active and durable oxygen reduction and evolution reactions via the A-site entropy engineering

The performance of reversible solid oxide electrochemical cells (R-SOECs) is largely hindered by the insufficient electroactivity and poor durability of the bifunctional air electrodes, where the oxygen reduction and evolution reactions (ORR and OER) occur. Here, we report our findings in boosting the electrochemical activity and durability of an air electrode with Pr 0.2 Ba 0.2 Sr 0.2 La 0.2 Ca 0.2 CoO 3-δ (PBSLCC) via an A-site entropy engineering. The PBSLCC electrode shows enhanced oxygen reaction activity and excellent durability compared to binary and ternary double perovskites (PrBaCo 2 O 5+δ and Pr 0.8 Ba 0.8 Ca 0.4 Co 2 O 5+δ , respectively). A low and nearly unchanged area-specific resistance of 0.042Ωcm 2 is achieved at 750 °C during the 225-h stability test. La 0.9 Sr 0.1 Ga 0.8 Mg 0.2 O 3-δ electrolyte-supported cells with the PBSLCC air electrode show remarkable performance at 800 °C, demonstrating a peak power density of 1.2Wcm -2 in the fuel cell mode, and a current density of -1.1 Acm -2 at 1.3 V in the electrolysis mode while maintaining the excellent cycling durability of 228 h at ±0.5 Acm -2 under humidified H 2 (10% H 2 O). A bulk oxygen p-band center model is applied to verify that tailoring of the A-site entropy strongly influences the surface exchange coefficients (k* chem ), leading to higher oxygen reaction activity of PBSLCC than the binary and ternary perovskites. Finally, this study opens a new class of high-entropy perovskites for the rational design of air electrodes for R-SOECs with high activity and durability.

30 DIRECT ENERGY CONVERSION↗
DOE OSTI2023

A New Class of Proton Conductors with Dramatically Enhanced Stability and High Conductivity for Reversible Solid Oxide Cells

Reversible solid oxide cells based on proton conductors (P-ReSOCs) have potential to be the most efficient and low-cost option for large-scale energy storage and power generation, holding promise as an enabler for the implementation of intermittent renewable energy technologies and the widespread utilization of hydrogen. Here, the rational design of a new class of hexavalent Mo/W-doped proton-conducting electrolytes with excellent durability while maintaining high conductivity is reported. Specifically, BaMo(W) 0.03 Ce 0.71 Yb 0.26 O 3-δ exhibits dramatically enhanced chemical stability against high concentrations of steam and carbon dioxide than the state-of-the-art electrolyte materials while retaining similar ionic conductivity. In addition, P-ReSOCs based on BaW 0.03 Ce 0.71 Yb 0.26 O 3-δ demonstrate high peak power densities of 1.54, 1.03, 0.72, and 0.48 W cm –2 at 650, 600, 550, and 500 °C, respectively, in the fuel cell mode. During steam electrolysis, a high current density of 2.28 A cm –2 is achieved at a cell voltage of 1.3 V at 600 °C, and the electrolysis cell can operate stably with no noticeable degradation when exposed to high humidity of 30% H 2 O at –0.5 A cm –2 and 600 °C for over 300 h. Altogether, this work demonstrates the promise of donor doping for obtaining proton conductors with both high conductivity and chemical stability for P-ReSOCs.

25 ENERGY STORAGE↗
DOE OSTI2022

Durable, High-Performance Unitized Reversible Fuel Cells Based on Proton Conductors

The main objective of this project was to develop robust, highly efficient, and economically viable H + -conducting membrane-based, unitized reversible fuel cell (H-URFC) technology for large-scale co-located energy storage and power generation. Another objective of this project is to gain a profound understanding of the degradation mechanisms of key stack materials and interfaces using various in situ, ex situ, and operando measurements guided by theoretical analysis. Nanostructured components will be integrated into cell design and the interfaces between electrodes and electrolyte will be modified with active bi-functional catalysts and protective coatings in order to achieve >70% roundtrip efficiency at 1 A/cm2 in both the fuel cell and the electrolysis modes. The end goal of the project is to advance the technology to the point that a university-industry collaboration can be established to scale up the technology for early adoption, and eventually enabling a pathway to large-scale energy storage that utilizes chemical storage and conversion for electrical grid balancing.

08 HYDROGEN↗
DOE OSTI2022

Critical role of acceptor dopants in designing highly stable and compatible proton-conducting electrolytes for reversible solid oxide cells

Proton-conducting electrolytes are receiving increasing attention due to their high ionic conductivity at intermediate temperatures, enabling the operation of solid oxide cells with high energy efficiency at low cost. However, the effect of B-site dopants on the properties of doped barium hafnate-cerate electrolyte materials, especially in single cells under operating conditions, has not been systematically studied. Here we report our findings in the development of a series of proton-conducting electrolytes with a general formula of BaHf 0.1 Ce 0.7 R 0.2 O 3–δ (BHCR172, R = Yb, Er, Y, Gd, Sm). Here, the results reveal that electrical conductivity, ionic transference number, chemical stability against steam and CO 2 , and compatibility with NiO during sintering are all closely correlated with the dopant size. In particular, the reaction with NiO is found to strongly affect the properties of the electrolytes and hence cell performance. Among all tested compositions, BaHf 0.1 Ce 0.7 Yb 0.2 O 3–δ (BHCYb172) shows excellent chemical stability and minimal reactivity towards NiO, as predicted from density functional theory (DFT)-based calculations and confirmed by experimental results. In addition, proton-conducting reversible solid oxide cells (P-ReSOCs) based on the optimized electrolyte composition, BHCYb172, demonstrate exceptional performance and stability, achieving a remarkable peak power density of 1.74 W cm –2 (O 2 as the oxidant) at 600 °C in the fuel cell mode and a high current density of 2.0 A cm –2 at 1.3 V and 600 °C in the steam electrolysis mode while maintaining excellent durability for over 1000 h.

25 ENERGY STORAGE↗
DOE OSTI2022

Surface Regulating of a Double–Perovskite Electrode for Protonic Ceramic Fuel Cells to Enhance Oxygen Reduction Activity and Contaminants Poisoning Tolerance

Protonic ceramic fuel cells (PCFCs) are one of the most efficient energy conversion devices. However, the performance of current PCFCs is greatly limited by the sluggish oxygen reduction reaction (ORR) kinetics and the fast degradation of cathode due to contaminants poisoning (such as Cr species and steam). In this work, we report a surface regulating of a double perovskite PrBa 0.5 Sr 0.5 Co 1.5 Fe 0.5 O 5+δ (PBSCF) cathode by a Pr 0.9 Fe 0.7 Co 0.3 O 3 (PFC) catalyst coating to enhance the ORR activity and stability. When tested in direct contact with Cr in the air with 3% H 2 O at 650 °C, the polarization resistance (Rp) of the PFC-PBSCF electrode increases from $\approx$0.39 to 0.45 Ω cm 2 after 100 h operation; in contrast, the R p of a PBSCF electrode increases from 0.63 to 0.82 Ω cm 2 . Further, a PCFC with the PFC-PBSCF cathode demonstrates an excellent peak power density ($\approx$1.08 W cm -2 at 650 °C) and significantly enhanced durability (degradation rate of 0.03 % h -1 ), much better than those of the cells with a PBSCF cathode ($\approx$0.75 W cm -2 and degradation rate of 0.12 % h -1 ). Raman spectroscopy and density functional theory calculations indicate that the PFC catalyst coating diminishes the formation of Cr species, such as (Ba 1-x Sr x )CrO 4 , on the cathode surface.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Surface restructuring of a perovskite-type air electrode for reversible protonic ceramic electrochemical cells

Reversible protonic ceramic electrochemical cells (R-PCECs) are ideally suited for efficient energy storage and conversion; however, one of the limiting factors to high performance is the poor stability and insufficient electrocatalytic activity for oxygen reduction and evolution of the air electrode exposed to the high concentration of steam. Here we report our findings in enhancing the electrochemical activity and durability of a perovskite-type air electrode, Ba 0.9 Co 0.7 Fe 0.2 Nb 0.1 O 3-δ (BCFN), via a water-promoted surface restructuring process. Under properly-controlled operating conditions, the BCFN electrode is naturally restructured to an Nb-rich BCFN electrode covered with Nb-deficient BCFN nanoparticles. When used as the air electrode for a fuel-electrode-supported R-PCEC, good performances are demonstrated at 650 °C, achieving a peak power density of 1.70 W cm –2 in the fuel cell mode and a current density of 2.8 A cm –2 at 1.3 V in the electrolysis mode while maintaining reasonable Faradaic efficiencies and promising durability.

30 DIRECT ENERGY CONVERSION↗
DOE OSTI2022

Precision surface modification of solid oxide fuel cells via layer-by-layer surface sol–gel deposition

While solid oxide fuel cells (SOFCs) are a promising technology for a clean and sustainable future, their commercialization is hindered by limited durability and performance. Here, we report our findings on the application of a layer-by-layer surface sol–gel (SSG) coating of catalysts to dramatically enhance the electro-catalytic activity and durability of SOFC cathodes. The SSG process is capable of penetrating and preserving complex backbone microstructures of porous electrodes, creating highly conformal coatings of controlled morphology, while tailoring the composition of the surface to improve catalytic properties and durability. For example, the application of an SSG coating of PrO x to a La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3–δ (LSCF) cathode has reduced the polarization resistance from 1.136 to 0.117 Ω cm 2 at 600 °C and the degradation rate from 1.13 × 10 –3 to 2.67 × 10 –4 Ω cm 2 h –1 at 650 °C. In addition, a continuous improvement in electrode performance is demonstrated as the thickness of the coating is increased, corresponding to the linear addition of catalyst. Furthermore, this first application of the SSG technique to SOFC systems opens the door for the controlled surface modification of porous components in electrochemical systems.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Highly Active and Durable Air Electrodes for Reversible Protonic Ceramic Electrochemical Cells Enabled by an Efficient Bifunctional Catalyst

The commercialization of reversible protonic ceramic electrochemical cells is hindered by the lack of highly active and durable air electrodes exposed to high concentration of steam under operating conditions. We report findings that dramatically enhance the electrocatalytic activity and stability of a conventional (La 0.6 Sr 0.4 ) 0.95 Co 0.2 Fe 0.8 O 3-δ (LSCF) air electrode by a multiphase catalyst coating composed of a conformal Pr 1-x Ba x CoO 3-δ thin film and exsolved BaCoO 3-δ nanoparticles, are reported. At 600 °C, the catalyst coating decreases the polarization resistance of the LSCF air electrode by a factor of 25 (from 1.09 to 0.043 Ω cm 2 ) in air and the degradation rate by two orders of magnitude (from 1.0 × 10 -2 to 1.8 × 10 -4 Ω cm2 h -1 in humidified air with 30 vol% H2O). Further, a single cell with the catalyst-coated LSCF air electrode at 600 °C demonstrates a high peak power density of 1.04 W cm -2 in the fuel cell mode and a high current density of 1.82 A cm -2 at 1.3 V in the electrolysis mode. The significantly enhanced performance of the LSCF air electrode is attributed mainly to the high rate of surface oxygen exchange, fast surface proton diffusion, and the rapid H 2 O and O 2 dissociation on the catalysts.

36 MATERIALS SCIENCE↗
DOE OSTI2022

A high-performance and durable direct NH 3 tubular protonic ceramic fuel cell integrated with an internal catalyst layer

Nickel-based cermet anode-supported protonic ceramic fuel cells (PCFCs) show great potential for direct utilization of ammonia. However, the insufficient activity of anode and the deterioration of anode activity/durability caused by the undesired interaction between nickel and ammonia greatly limit the application. Here, we report tubular PCFCs embedded with a catalytic iron layer. Such cells show peak power densities of 1.507 W cm -2 and 1.078 W cm -2 at 700 °C when using H 2 and NH 3 as fuel, respectively, which are the highest tubular PCFC performance so far ever reported. In addition, the stability of cells with the catalyst layer has been dramatically enhanced when compared with that of cells without the catalyst layer. As a result, the enhancement of activity and durability is attributed to the catalytic activity of iron for ammonia decomposition, through which the direct contact between nickel and ammonia has been minimized and the anode structure has therefore been protected.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Surface enhanced performance of La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3-δ cathodes by infiltration Pr-Ni-Mn-O progress

Herein the present study reports the enhancement of electrochemical oxygen reduction activity of porous La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3–δ (LSCF) cathodes by coating a thin film of Pr-Ni-Mn oxide (PNM5) using a multi-step infiltration process. XRD examination reveals that PNM5 mainly contains a multiphase mixture of Pr 6 O 11 , PrNiO 3 , MnO and NiO. SEM morphology shows a thin PNM5 film and small particles are formed on the surface of LSCF backbone particles. Impedance spectrum analysis indicates that PNM5 infiltrated LSCF exhibits dramatically reduced polarization resistance (R p ), reaching R p of 0.244 Ω cm 2 at 973 K, which is one-half of the baseline LSCF cathode. The activation energy of LSCF cathodes infiltrated with PNM5 is 1.45 eV, slightly lower than the baseline LSCF cathode (1.77 eV). Distribution of relaxation time (DRT) function analysis shows PNM5 infiltration layer significantly promotes the oxygen reduction reaction (ORR) of cathode surface. With the increase in firing temperature, the total resistance increases and R p changes from ion transport to oxygen reduction reaction. Degradation rate of the PNM5-infiltrated LSCF is also lower, 0.02168% vs 0.07093% for the baseline LSCF over a 200-h period. A single cell testing indicated that the peak power density of the PNM5-infiltrated cell was increased by 140.66%. Overall, PNM5 could be a potential catalyst for boosting the performance of a commercial LSCF cathode for solid oxide fuel cells (SOFC).

36 MATERIALS SCIENCE↗