Assessment of multi-stage telescopic control rods in a pebble bed reactor. Part II: corrosion and wear performance
To support High-Temperature Gas-Cooled Reactor designs, the effects of corrosion and wear on a SS316L telescopic control rod prototype were investigated in helium at 775 °C with up to 5 ppm oxygen for durations up to 500 h. Three deployment conditions were tested to assess their impact on wear and oxide formation: severe cycles, daily cycles, and gravity-driven deployments. Here, a chromium-rich oxide layer developed on regions exposed to the helium flow, reaching up to 2 µm in the most affected areas. No carburization or decarburization was observed. Oxide breakthrough occurred mainly at grooves and contact points during severe cycling of the telescopic rod, while in the other tests it was limited to contact points. Friction forces increased due to oxide growth and thermal expansion, the latter being the dominant factor, but never enough to hinder rod deployment significantly. Coaxial misalignment of stages was identified as the main potential risk to reliable operation under normal conditions.