Engineering topics
Publications and source records attributed to Lieberman, S. L..
Potting compounds include series of modified silicone RTV polymers and series of coreacted epoxy urethanes. Special properties are obtained by including Br, P, and N in polymeric structure.
Based upon extensive contacts with vendors, a broad array of non-flammable polymeric specie, and additives generally noted to have flame retarding properties, were considered. The following polymeric matrices were examined: modified silicone and fluorosilicone RTV's polyesters, epoxies, urethanes, and epoxy-urethanes. Optimization of formulations to obtain a suitable balance between the various properties and flammability resistance led to the final selection of a silicone RTV/additive-loaded compound which meets almost all program requirements. The very low valued properties found are within a realistic level of design toleration. Complete formulation, processing, and test data is provided for this compound, EPOCAST 87517-A/B, and the other formulations prepared by the project. Details of those test methods are presented along with procedures utilized in the program. In addition, a description of the special flammability facility previously designed and then modified for this program is also presented.
Tables are presented which include: material properties; elemental analysis; silicone RTV formulations; polyester systems and processing; epoxy preblends and processing; urethane materials and processing; epoxy-urethanes elemental analysis; flammability test results, and vacuum effects.
Appendices are presented which include: statement of work; material vendor contacts; formulation/processing data sheet; upward propagation test; flammability test conditions/results sheet; odor test; vacuum stability requirements; flammability test facility; determination of offgassing products and carbon monoxide test; and pneumatic and mechanical impact test guidelines.
The necessity of having nonflammable versions of potting and encapsulating compounds and conformal coatings for space vehicles is discussed. The formulation, EPOCAST 87517 A/B, was found to have the best balance of thermal, electrical, mechanical, physical, and chemical properties of those evaluated. The requirements which this formulation did not meet are listed, and other formulations which were evaluated are summarized. Recommendations for improving EPOCAST 87517 A/B are included.
Two fluorosilicone rubber formulations have been produced which are nonflammable or self-extinguishing. Extensive report was prepared which includes information on testing and describes many alternate formulations.
The overall program objective was to develop a flexible compound which not only functioned in a manned aerospace environment as an effective electrical insulation, but whose flammability characteristics in 16.5 psia, 60% oxygen/40% nitrogen were evidenced by rapid self-extinguishment and minimal thermal (pyrolysis) degradation. The following polymeric matrices were examined in depth: fluoroelastomers, modified fluoroelastomers, silicone RTV's, and modified silicone and fluorosilicone RTV's. Almost none of these systems burned in air, but all burned in 6.2 psia oxygen. Inorganic, organic, and inorganic/organic additives were evaluated in conjunction with these polymers in order to achieve the required survival in the 16.5 psia 60/40 environment. Depending upon formulations, it was possible to achieve nonflammable products when tested in the 1/4 in. x 1/4 in. x 1 in. configuration, even up to and including 16.5 psia oxygen. However, in order to assure this level of flame resistance, it was found necessary to heavily load the matrix with the additives. This resulted in a significant reduction in mechanical properties and large increases in viscosities. Optimization of formulations to obtain a suitable balance between these properties and flammability resistance led to the final selection of Formulation 387 as the primary system.