NASA NTRS1998

Metastable Demixing of Supercooled Cu-Co and Cu-Fe Alloys in an Oxide Flux

A systematic study on the liquid separation in supercooled Cu-Co and Cu-Fe alloys was performed using a melt fluxing which permits high supercooling to be achieved. Moreover, this method renders it possible to directly measure binodal temperatures and establish metastable liquid miscibility gap (LMG). All phase-separated samples at compositions ranging from 10 to 80 wt pct Co or to 83 wt pct Fe were found to exhibit droplet-shaped morphologies, in spite of various droplet distributions. Uniformly dispersed microstructures were obtained as the minority component was less than 20 vol.%; while beyond this percentage, serious coarsening was brought about. Calculations of the miscibility gap in the Cu-Co system and Stokes movement velocity of Co and Fe droplets in Cu matrix were made to analyze the experimental results.

Li, D.↗

NASA NTRS1998

Liquidus Temperatures and Solidification Behavior in the Copper-Niobium System

The copper-niobium phase diagram has been under active debate; thus, a corroboratory experimental study is needed. In this investigation, the melts of Cu-Nb alloys at compositions ranging from 5 lo 86 wt% Nb were processed in different environments and solidified at relatively low rates of 50-75 C/s to determine liquidus temperatures and to study solidification behavior. For all samples processed under very clean conditions, only Nb dendrites in a Cu matrix were observed; while in the presents of oxygen impurities, the alloys containing 5-35 wt% Nb exhibited microstructure of Nb-rich spheroids and Nb dendrites in the Cu matrix. The results obtained from clean conditions are in fair agreement with the Cu-Nb phase diagram having an S-shaped, near-horizontal appearances of the liquidus. The formation of Nb-rich droplets at slow cooling rates is discussed in terms of a stable liquid miscibility gap induced by oxygen.

Li, D.↗

NASA NTRS1998

Liquidus Temperatures and Solidification Behavior in the Copper-Niobium System

The copper-niobium phase diagram has been under active debate; thus, a corroboratory experimental study is needed. In this investigation, the melts of Cu-Nb alloys at compositions ranging from 5 to 86 wt pct Nb were processed in different environments and solidified at relatively low cooling rates of 50 to 75 C/s to determine liquidus temperatures and to study solidification behavior. For all samples processed under very clean conditions, only Nb dendrites in a Cu matrix were observed; while in the presence of oxygen impurities the alloys containing 5 to 35 wt pct Nb exhibited microstructure of Nb-rich spheroids and Nb dendrites in the Cu matrix. The results obtained from clean conditions are in fair agreement with the Cu-Nb phase diagram having an S-shaped, near-horizontal appearance of the liquidus. The formation of Nb- rich droplets at slow cooling rates is discussed in terms of a stable liquid miscibility gap induced by oxygen.

Li, D.↗

NASA NTRS1998

On the Cu-Nb Phase Diagram and Solidified Microstructures

Container and containerless processing was employed to determine liquidus temperatures and to examine microstructural development in the Cu-Nb system. The Cu-Nb phase diagram of an S-shaped, near-horizontal liquidus, has been confirmed by both the temperature-time profiles and resultant microstructures with only Nb dendrites in a Cu matrix, which were obtained from crucible experiments under clean conditions. However, the microstructural pathways of Cu-Nb alloys are particularly sensitive to processing variables. By the addition of oxygen impurities or rapid solidification, droplet-shaped morphology was observed for some compositions, implying occurrence of a liquid-phase separation. The effects of impurities and cooling rates are analyzed in connection with a stable and metastable liquid miscibility gap, respectively.

Li, D.↗

NASA NTRS1998

Undercooling, Liquid Separation and Solidification of Cu-Co Alloys

Large undercooling can induce not only various solidification pathways, but also a precursor reaction, or liquid separation. This paper deals with the latter effect of undercooling using examples of the Cu-Co system which has a flattened liquidus. Bulk Cu-Co alloys (about 7mm diameter) at compositions ranging from 10 to 90 wt pct Co were highly undercooled using a fluxing technique. Except for Cu-90 wt pct Co, liquid separation was directly observed as undercooling exceeded a critical value depending on the composition. It was also confirmed by a microstructural transition from dendrites to droplets above the critical undercooling. Finally, theoretical calculations regarding the metastable miscibility boundary and maximum droplet radius were made to analyze the experimental results.

Robinson, M. B.↗