Lightweight, deployable antennas for a variety of outer-space and terrestrial applications would be designed and fabricated according to the concept of cold hibernated elastic memory (CHEM) structures, according to a proposal. Mechanically deployable antennas now in use are heavy, complex, and unreliable, and they utilize packaging volume inefficiently. The proposed CHEM antenna structures would be simple and would deploy themselves without need for any mechanisms and, therefore, would be more reliable. The proposed CHEM antenna structures would also weigh less, could be packaged in smaller volumes, and would cost less, relative to mechanically deployable antennas. The CHEM concept was described in two prior NASA Tech Briefs articles: "Cold Hibernated Elastic Memory (CHEM) Expandable Structures" (NPO-20394), Vol. 23, No. 2 (February 1999), page 56; and "Solar Heating for Deployment of Foam Structures" (NPO-20961), Vol. 25, No. 10 (October 2001), page 36. To recapitulate from the cited prior articles: The CHEM concept is one of utilizing opencell foams of shape-memory polymers (SMPs) to make lightweight, reliable, simple, and inexpensive structures that can be alternately (1) compressed and stowed compactly or (2) expanded, then rigidified for use. A CHEM structure is fabricated at full size from a block of SMP foam in its glassy state [at a temperature below the glass-transition temperature (Tg) of the SMP]. The structure is heated to the rubbery state of the SMP (that is, to a temperature above Tg) and compacted to a small volume. After compaction, the structure is cooled to the glassy state of the SMP. The compacting force can then be released and the structure remains compact as long as the temperature is kept below Tg. Upon subsequent heating of the structure above Tg, the simultaneous elastic recovery of the foam and its shape-memory effect cause the structure to expand to its original size and shape. Once thus deployed, the structure can be rigidified by cooling below Tg. Once deployed and rigidified, the structure could be heated and recompacted. In principle, there should be no limit on the achievable number of compaction/deployment/ rigidification cycles. Thus far, several different designs of a 3.5-m-long CHEM conical corrugated horn antenna have been analyzed (see figure). A small CHEM structural antenna model was fabricated and a thin, electrically conductive layer of aluminum was deposited on the inner surface of the model. This structural model was then subjected to the compaction and deployment treatments described above to demonstrate the feasibility of a CHEM corrugated horn antenna.

Sokolowski, Witold↗

NASA NTRS2003

Noninvasive, near infrared spectroscopic-measured muscle pH and PO2 indicate tissue perfusion for cardiac surgical patients undergoing cardiopulmonary bypass

OBJECTIVE: To determine whether near infrared spectroscopic measurement of tissue pH and Po2 has sufficient accuracy to assess variation in tissue perfusion resulting from changes in blood pressure and metabolic demand during cardiopulmonary bypass. DESIGN: Prospective clinical study. SETTING: Academic medical center. SUBJECTS: Eighteen elective cardiac surgical patients. INTERVENTION: Cardiac surgery under cardiopulmonary bypass. MEASUREMENTS AND MAIN RESULTS: A near infrared spectroscopic fiber optic probe was placed over the hypothenar eminence. Reference Po2 and pH sensors were inserted in the abductor digiti minimi (V). Data were collected every 30 secs during surgery and for 6 hrs following cardiopulmonary bypass. Calibration equations developed from one third of the data were used with the remaining data to investigate sensitivity of the near infrared spectroscopic measurement to physiologic changes resulting from cardiopulmonary bypass. Near infrared spectroscopic and reference pH and Po2 measurements were compared for each subject using standard error of prediction. Near infrared spectroscopic pH and Po2 at baseline were compared with values during cardiopulmonary bypass just before rewarming commenced (hypotensive, hypothermic), after rewarming (hypotensive, normothermic) just before discontinuation of cardiopulmonary bypass, and at 6 hrs following cardiopulmonary bypass (normotensive, normothermic) using mixed-model analysis of variance. Near infrared spectroscopic pH and Po2 were well correlated with the invasive measurement of pH (R2 =.84) and Po2 (R 2 =.66) with an average standard error of prediction of 0.022 +/- 0.008 pH units and 6 +/- 3 mm Hg, respectively. The average difference between the invasive and near infrared spectroscopic measurement was near zero for both the pH and Po2 measurements. Near infrared spectroscopic Po2 significantly decreased 50% on initiation of cardiopulmonary bypass and remained depressed throughout the bypass and monitored intensive care period. Near infrared spectroscopic pH decreased significantly during cardiopulmonary bypass, decreased significantly during rewarming, and remained depressed 6 hrs after cardiopulmonary bypass. Diabetic patients responded differently than nondiabetic subjects to cardiopulmonary bypass, with lower muscle pH values (p =.02). CONCLUSIONS: Near infrared spectroscopic-measured muscle pH and Po2 are sensitive to changes in tissue perfusion during cardiopulmonary bypass.

Non-NASA Center↗

NASA NTRS2001

A New, Simple Technique to Prevent Water Condensation on Intraocular Lenses during Vitrectomy

Explore the source record for details and available documents.

water condensation, intraocular lenses, vitrectomy↗