DOE OSTI2023

Synthesis and exceptional operational durability of polyaniline-inspired conductive ladder polymers

Ladder-type structures can impart exceptional stability to polymeric electronic materials. This article introduces a new class of conductive polymers featuring a fully ladder-type backbone. A judicious molecular design strategy enables the synthesis of a low-defect ladder polymer, which can be efficiently oxidized and acid-doped to achieve its conductive state. The structural elucidation of this polymer and the characterization of its open-shell nature are facilitated with the assistance of studies on small molecular models. An autonomous robotic system is used to optimize the conductivity of the polymer thin film, achieving over 7 mS cm −1 . Impressively, this polymer demonstrates unparalleled stability in strong acid and under harsh UV-irradiation, significantly surpassing commercial benchmarks like PEDOT:PSS and polyaniline. Moreover, it displays superior durability across numerous redox cycles as the active material in an electrochromic device and as the pseudocapacitive material in a supercapacitor device. This work provides structural design guidance for durable conductive polymers for long-term device operation.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Robust chain aggregation of low-entropy rigid ladder polymers in solution

Conjugated polymers have been widely investigated where ladder-type conjugated polymers receive more attention due to their rigid backbones and extraordinary properties. However, the understanding of how the rigid conformation of ladder polymers translates to material properties is still limited. Here, we systematically investigated the solution aggregation properties of a carbazole-derived conjugated ladder polymer (LP) and its analogous non-ladder control polymer (CP) via light scattering, neutron scattering, and UV-vis absorption spectroscopy characterization techniques, revealing a highly robust, temperature-insensitive aggregation behavior of the LP. The experimental findings were further validated by computational molecular dynamics simulations. Here we found that the peak positions and intensities of the UV spectra of the LP remained constant between 20 °C and 120 °C in chlorobenzene solution. The polymer also showed a stable hydrodynamic radius measured by dynamic light scattering from 20 °C to 70 °C in the chlorobenzene solution. Using small-angle neutron scattering, no Guinier region was reached in the measured q range down to 0.008 Å –1 , even at elevated temperature. In contrast, the non-ladder control polymer CP was fully soluble in the chlorobenzene solvent without the observation of any notable aggregates. The Brownian dynamics simulation showed that during polymer aggregation, the entropy change of the LP was significantly less negative than that of the non-ladder control polymer. These findings revealed the low entropy nature of rigid conjugated ladder polymers and the low entropy penalty for their aggregation, which is promising for highly robust intermolecular interactions at high temperatures. Such a unique thermodynamic feature of rigid ladder polymers can be leveraged in the design and application of next-generation electronic and optoelectronic devices that function under unconventional high temperature conditions.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Variable-Temperature Scattering and Spectroscopy Characterizations for Temperature-Dependent Solution Assembly of PffBT4T-Based Conjugated Polymers

The solution structure of conjugated polymers (CPs) from which the films are cast is critical for tailoring the thin-film morphology thus device performance. Here, we used multimodal variable-temperature scattering and spectroscopy tools to fully quantify the solution assembly of poly[(5,6-difluoro-2,1,3-benzothiadiazol-4,7-diyl)-alt-(3,3'''-dialkyl-2,2';5',2'';5'',2'''-quaterthiophen-5,5'''-diyl)] (PffBT4T) polymers with varying side-chain lengths at different assembly temperatures. The conformational and aggregation behaviors for PffBT4T-based CPs were found to be very sensitive to both temperature and side chain length using ultraviolet–visible (UV–vis) spectroscopy, nuclear magnetic resonance (NMR) spectroscopy, dynamic light scattering (DLS), and small-angle neutron scattering (SANS). We found that with slightly increasing side chain length from 2-octyldodecyl (C8C12) to 2-nonyltridecyl (C9C13), PffBT4T-based CPs show a significant decrease in aggregation-to-dissolved chain transition temperature (10 °C), degree of aggregation, enthalpy change of aggregation, and size of the aggregates in solution. At room temperature, PffBT4T polymer strongly aggregated to form fabric structure with the film thickness of a few nanometers in thickness and hundreds of nanometers in length, as probed by atomic force microscopy (AFM), transmission electronic microscopy (TEM), and dynamic light scattering (DLS). At the elevated temperature above the aggregation-to-dissolved chain transition temperature, PffBT4T is fully dissolved and adopts a semiflexible coil conformation with the persistence length of 3.1 nm for PffBT4T-C8C12 and a slightly increased persistence length of 3.4 nm for PffBT4T-C9C13, according to temperature-dependent SANS measurements. Longer side chains of PffBT4T-C9C13 also lead to less aggregation enthalpy gain compared with PffBT4T-C8C12. This work provides a solution structure manipulating strategy of CPs and thus will inspire the molecular design and processing protocols of CPs toward higher performance electronic devices.

36 MATERIALS SCIENCE↗