Lee, S. Y.

Publications and source records attributed to Lee, S. Y..

At least 19 records

Crew/Robot Coordinated Planetary EVA Operations at a Lunar Base Analog Site

Under the direction of NASA's Exploration Technology Development Program, robots and space suited subjects from several NASA centers recently completed a very successful demonstration of coordinated activities indicative of base camp operations on the lunar surface. For these activities, NASA chose a site near Meteor Crater, Arizona close to where Apollo Astronauts previously trained. The main scenario demonstrated crew returning from a planetary EVA (extra-vehicular activity) to a temporary base camp and entering a pressurized rover compartment while robots performed tasks in preparation for the next EVA. Scenario tasks included: rover operations under direct human control and autonomous modes, crew ingress and egress activities, autonomous robotic payload removal and stowage operations under both local control and remote control from Houston, and autonomous robotic navigation and inspection. In addition to the main scenario, participants had an opportunity to explore additional robotic operations: hill climbing, maneuvering heaving loads, gathering geo-logical samples, drilling, and tether operations. In this analog environment, the suited subjects and robots experienced high levels of dust, rough terrain, and harsh lighting.

Diftler, M. A.

Thin film diamond microstructure applications

Selective deposition and abrasion, as well as etching in atomic oxygen or reduced-pressure air, have been used to prepare patterned polycrystalline diamond films which, on further processing by anisotropic Si etching, yield the microstructures of such devices as flow sensors and accelerometers. Both types of sensor have been experimentally tested in the respective functions of hot-wire anemometer and both single- and double-hinged accelerometer.

Roppel, T.

Manufacturing stresses and strains in filament wound cylinders

Tests were performed to verify a previously developed model for simulating the manufacturing process of filament wound cylinders. The axial and hoop strains were measured during cure inside a filament wound Fiberite T300/976 graphite-epoxy cylinder. The measured strains were compared to those computed by the model. Good agreements were found between the data and the model, indicating that the model is a useful representation of the process. For the conditions of the test, the manufacturing stresses inside the cylinder were also calculated using the model.

Calius, E. P.

Method of neutralizing the corrosive surface of amine-cured epoxy resins

The corrosive alkaline surface layer of an epoxy resin product formed by the curing of the epoxy with an aliphatic amine is eliminated by first applying a non-solvent to remove most or all of the free unreacted amine and then applying a layer of a chemical reagent to neutralize the unused amine or amine functional groups by forming a substituted urea. The surface then may be rinsed with acetone and then with alcohol. The non-solvent may be an alcohol. The neutralizing chemical reagent is a mono-isocyanate or a mono-isothiocyanate. Preferred is an aromatic mono-isocyanate such as phenyl isocyanate, nitrophenyl isocyanate and naplthyl isocyanate.

Lee, S. Y.

Neutralizing Amine-Cured Epoxy Surfaces

New surface treatment is a rapid, convenient, and effective method for converting unused amines and amine functional groups into neutral, noncorrosive substituted urea. Reaction proceeds at room temperature, takes only a few minutes, and leaves no corrosive residue. Surface should first be washed with alcohol to remove as much as possible of unreacted amine. Then it should be dried, since residual moisture or alcohol may consume some of treatment reagent and neutralization may then be incomplete.

Lee, S. Y.

Evaluation of present thermal barrier coatings for potential service in electric utility gas turbines

The resistance of present-day thermal barrier coatings to combustion gases found in electric utility turbines was assessed. The plasma sprayed coatings, both duplex and graded types, were primarily zirconia-based, although a calcium silicate was also evaluated. Both atmospheric burner rig tests and high pressure tests (135 psig) showed that several present-day thermal barrier coatings have a high potential for service in gas turbines burning the relatively clean GT No. 2 fuel. However, coating improvements are needed for use in turbines burning lower grade fuel such as residual oil. The duplex ZrO2.8Y2O3/NiCrA1Y coating was ranked highest and selected for near-term field testing, with Ca2SiO4/NiCrA1Y ranked second. Graded coatings show potential for corrosive turbine operating conditions and warrant further development. The coating degradation mechanisms for each coating system subjected to the various environmental conditions are also described.

Bratton, R. J.

Ceramic thermal barrier coatings for gas turbine engines

The results of studies concerning the high temperature corrosion resistance of ZrO2-Y2O3, ZrO2-MgO, and Ca2SiO4 plasma-sprayed coatings, which may be used as gas turbine engine thermal barriers, are reported. The coatings were evaluated in atmospheric burner rig and pressurized passage tests, using GT No. 2 fuel in pure form and with sodium, sulfur and vanadium corrosive impurities doping. It is found that, while the coatings performed well in both pressurized passage and burner rig tests with pure fuel chemical reactions between the ceramic coatings and combustion gases/condensates resulted in coating degradation with impure fuels. Chemical reactions between the ceramic coatings and vanadium compounds played a critical role in coating degradation.

Bratton, R. J.

Advanced ceramic coating development for industrial/utility gas turbine applications

The effects of ceramic coatings on the lifetimes of metal turbine components and on the performance of a utility turbine, as well as of the turbine operational cycle on the ceramic coatings were determined. When operating the turbine under conditions of constant cooling flow, the first row blades run 55K cooler, and as a result, have 10 times the creep rupture life, 10 times the low cycle fatigue life and twice the corrosion life with only slight decreases in both specific power and efficiency. When operating the turbine at constant metal temperature and reduced cooling flow, both specific power and efficiency increases, with no change in component lifetime. The most severe thermal transient of the turbine causes the coating bond stresses to approach 60% of the bond strengths. Ceramic coating failures was studied. Analytic models based on fracture mechanics theories, combined with measured properties quantitatively assessed both single and multiple thermal cycle failures which allowed the prediction of coating lifetime. Qualitative models for corrosion failures are also presented.

Andersson, C. A.

Thermal stability and aging of some new anaerobic adhesives for structural binding

Polyurethane-modified high impact anaerobic adhesives have been chosen for a bonding application where impact cushion is critical. These adhesives meet all the requirements for high rate production and automatic assembly techniques. With aluminum adherends, one selected adhesive cured at room temperature with the recommended activator retained sixty percent of its original impact strength after twenty-six week aging at 100 C. The impact strength aging, the thermogravimetric analysis results, the outgassing data, and other observations made in this work indicate that the adhesives cured by simple heating give a more durable bond than that cured with an activator at room temperature.

Lee, S. Y.

Evaluation of present-day thermal barrier coatings for industrial/utility applications

Atmospheric burner rig tests have been conducted to evaluate the corrosion resistance of present-day thermal barrier coatings. The coatings are primarily plasma-sprayed and zirconia-based. Both duplex and graded coating systems were tested at a gas temperature of 2100 F and metal temperatures that range from 1475 F to 1650 F. The fuels ranged from clean GT No. 2 to that doped with impurity levels which simulate water-washed residual fuels. Results to date suggest that liquid sulfate condensates play an important role in the coating degradation mechanisms, whereas the role of vanadium and its salts is less clear.

Bratton, R. J.

Physical correction filter for improving the optical quality of an image

A family of physical correction filters is described. Each filter is designed to correct image content of a photographed scene of limited resolution and includes a first filter element with a pinhole through which light passes to a differential amplifier. A second filter element through which light passes through one or more openings, whose geometric configuration is a function of the cause of the resolution loss included. The light, passing through the second filter element, is also supplied to the differential amplifier whose output is used to activate an optical display or recorder to reproduce a photograph or display of the scene in the original photograph or display of the scene in the original photograph with resolution which is significantly greater than that characterizing the original photograph.

Lee, S. Y.