Reduction of Methane Leaks through Corrosion Mitigation Pre-treatments for Pipelines with Field Applied Coatings
Corrosion of buried, coated steel pipelines transporting natural gas is a significant source of methane emissions, from pipeline venting required for maintenance and repairs and from pipeline leaks and incidents. Corrosion of steel under field applied coatings is an important safety concern for the pipeline industry. This project investigates the application of a field applied alloy over girth welds to mitigate external corrosion of buried coated steel pipelines. Various metallic coating options were considered, which were required to meet several criteria: (1) it must resist corrosion under open-circuit or mild cathodic protection conditions, (2) it must protect the substrate steel, and (3) it must not negatively affect the adhesion of the field coating. Finite element models and lab testing were performed of alloy coating compositions to identify promising alloy types underneath disbonded coatings. Polarization curves of coating alloys were generated to provide the boundary conditions for the COMSOL model to compute potential and current distributions around coated areas. Sacrificial and corrosion-resistant metal alloy coatings were evaluated and optimized using corrosion modeling and laboratory electrochemical testing, where aluminum alloy 5356 (5% Mg) and steel alloy B9 (9% Cr) were selected. Corrosion test coupons were designed and fabricated using thermal spray aluminum 5356 and welded B9 steel overlays on API 5L grade X42 line pipe steel. The corrosion test coupons, with simulated pipe coating damage, were tested in a laboratory soil box and a field pipeline site in Texas for 3-months. Corrosion test coupons were then tested for 6-months at field pipeline sites in Texas and Tennessee to quantify corrosion rates and performance of the aluminum and steel alloys under polyethylene tape and 2-part epoxy coatings, various coating holidays, and with and without cathodic protection.