Engineering topics
Publications and source records attributed to Lee, Dongsoo.
Removing cobalt lowers the electronic conductivity of high-nickel cathodes. A mismatch between electronic and ionic conductivities in the cathode composite leads to reaction inhomogeneity and peculiar cycling behavior in all-solid-state batteries.
Abstract Single‐crystalline layered oxide (LiNi 1‐ x ‐ y Mn x Co y O 2 ) cathodes have been found to exhibit exceptional electrochemical properties when coupled with various inorganic solid electrolytes (ISEs) in all‐solid‐state batteries (ASSBs). Their advantages stem from the robust morphological integrity with the absence of grain boundaries and the high electrochemical oxidative stability. Here, ASSBs featuring single‐crystalline LiNiO 2 (LNO) with the highest Ni content are reported, offering a high theoretical specific capacity of 275 mAh g ‐1 alongside a high average discharge voltage (3.7 V vs Li + /Li). Through a careful investigation, it is demonstrated that micron‐sized single‐crystalline LNO (µSC‐LNO) composite cathodes with a halide ISE exhibit a high initial discharge capacity of 205 mAh g ‐1 with an outstanding cycle performance over 200 cycles in room‐temperature ASSBs. The significance of engineering parameters is emphasized, such as particle size and specific density, in promoting a homogeneous and fast Li + transport within the composite cathodes. Furthermore, the formation of undesirable interphase between the halide ISE in the cathode and sulfide ISE separator is elucidated, which may be a critical factor impeding long‐term cyclability of ASSBs. This work provides insights into the design of composite cathodes for high‐energy‐density ASSBs.
Abstract Lithium‐sulfur (Li‐S) batteries, with their high energy density, nontoxicity, and the natural abundance of sulfur, hold immense potential as the next‐generation energy storage technology. To maximize the actual energy density of the Li‐S batteries for practical applications, it is crucial to escalate the areal capacity of the sulfur cathode by fabricating an electrode with high sulfur loading. Herein, ultra‐high sulfur loading (up to 12 mg cm −2 ) cathodes are fabricated through an industrially viable and sustainable solvent‐free dry‐processing method that utilizes a polytetrafluoroethylene binder fibrillation. Due to its low porosity cathode architecture formed by the binder fibrillation process, the dry‐processed electrodes exhibit a relatively lower initial capacity compared to the slurry‐processed electrode. However, its mechanical stability is well maintained throughout the cycling without the formation of electrode cracking, demonstrating significantly superior cycling stability. Additionally, through the optimization of the dry‐processing, a single‐layer pouch cell with a loading of 9 mg cm −2 and a novel multi‐layer pouch cell that uses an aluminum mesh as its current collector with a total loading of 14 mg cm −2 are introduced. To address the reduced initial capacity of dry‐processed electrodes, strategies such as incorporating electrocatalysts or employing prelithiated active materials are suggested.
A functionalized dry electrode (FDE) incorporating solvate-ionic-liquid-infiltrated ethyl cellulose demonstrates the criticality of the role of the conductive binder for achieving improved electrochemical performance in all-solid-state batteries.
Employing high voltage cobalt-free spinel LiNi 0.5 Mn 1.5 O 4 (LNMO) as a cathode is promising for high energy density and cost-effectiveness, but it has challenges in all-solid-state batteries (ASSBs). Here, it is revealed that the limitation of lithium argyrodite sulfide solid electrolyte (Li 6 PS 5 Cl) with the LNMO cathode is due to the intrinsic chemical incompatibility and poor oxidative stability. Through a careful analysis of the interphase of LNMO, it is elucidated that even the halide solid electrolyte (Li 3 InCl 6 ) with high oxidative stability can be decomposed to form resistive interphase layers with LNMO in ASSBs. Interestingly, with Fe-doping and a Li 3 PO 4 protective layer coating, LNMO with Li 3 InCl 6 displays stable cycle performance with a stabilized interphase at a high voltage (≈4.7 V) in ASSBs. The enhanced interfacial stability with the extended electrochemical stability window through doping and coating enables high electrochemical stability with LNMO in ASSBs. Furthermore, this work provides guidance for employing high-voltage cathodes in ASSBs and highlights the importance of stable interphases to enable stable cycling in ASSBs.
All-solid-state batteries (ASSBs) employing Li-metal anodes and inorganic solid electrolytes are attracting great attention due to high safety and energy density for next-generation energy storage devices. However, the volume change of cathode active materials can cause contact loss, resulting in charge carrier isolation, heterogeneous current distribution, and poor electrochemical properties in ASSBs. Here, a simple, yet effective, solvent-free electrode engineering approach with polytetrafluoroethylene (PTFE) as a binder for ASSBs is reported, enabling intimate contact and stable interfaces with the cathode. It is substantiated that the crystallinity of PTFE can be controlled depending on the heat history, and highly crystalline PTFE displays robust mechanical properties. High-nickel LiNi 0.8 Mn 0.1 Co 0.1 O 2 cathode prepared with crystalline PTFE show improved cycle and rate performances in ASSBs. In addition, it is revealed that the intimate contact between cathode particles with a stable cathode electrolyte layer is maintained during cycling by postmortem studies. Furthermore, this simple engineering method can be applied to prepare cathodes with a variety of active materials and solid electrolytes in ASSBs.