Lee, Bongjoon | Engineering Papers

DOE OSTI2023

Polyethylene Blends for Improved Oxygen Barrier: Processing-Dependent Microstructure and Gas Permeability

Here this work demonstrates a greater than expected enhancement of oxygen barrier properties in linear low-density polyethylene (LLDPE)-based materials by blending LLDPE with high-density polyethylene (HDPE). The films made by melt pressing the LLDPE/HDPE blends had a greater reduction in oxygen permeability coefficients (PO 2 ) than predicted using common permeability reduction models, i.e., the harmonic average model and zero-permeability nanofiller model. The reduction of PO 2 was attributed to the presence of spherulite crystal structures, as revealed by atomic force microscopy combined with infrared spectroscopy (AFM-IR). The LLDPE matrix exhibited significant spherulite formation even at a relatively low addition of HDPEs, which likely formed tortuous pathways for diffusing oxygen molecules. Transport results from melt-pressed films contrast with the results from films with similar compositions prepared by film blowing, which did not show barrier enhancement beyond expectation. AFM-IR revealed that the blown films lacked spherulite crystals likely due to stretching in the machine direction followed by rapid cooling. These findings demonstrate the role of processing in controlling microstructures and thus the oxygen barrier performance. This work offers the possibility of achieving easily recyclable LLDPE-based packaging materials by simple blending of polyethylenes with different crystalline content.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Improved Polypropylene Thermoformability through Polyethylene Layering

Due to its low cost, stiffness, and recyclability, isotactic polypropylene (iPP) is an excellent candidate for packaging applications. However, iPP is notoriously difficult to thermoform due to its low melt strength. The addition of just 10 thin layers of high-molecular-weight, linear low-density polyethylene (LLDPE) into iPP sheets by coextrusion significantly increased extensional viscosity and reduced sag. Both LLDPE and iPP were metallocene-catalyzed with excellent adhesion as measured in our previous work. Here, we performed a series of hot tensile tests and sheet sag measurements to determine the properties of the iPP sheet and the multilayer sheet between 130 and 180 °C. To evaluate the thermoformability of these multilayer sheets, truncated conical cups were positive vacuum formed at different temperatures and heating times, and the crush strength was measured. Cups that released easily from the mold with good shape retention and a crush strength within 80% of the maximum value were used to define a temperature–time thermoformability window. We estimated the maximum stress that occurred during the thermoforming process to be 5 MPa. Layer thicknesses before and after thermoforming were used to estimate an average strain of 0.78. The thin LLDPE layers decreased the yield stress below 5 MPa. This enabled thermoforming at sheet temperatures as low as 150 °C. The immiscible LLDPE interfaces increased extensional viscosity, which decreased sag in the multilayer sheets compared to iPP. This broadened the thermoforming range to temperatures as high as 180 °C and allowed longer heating times. These highly thermoformable, layered sheets may be recycled as iPP since they contain only 8% of LLDPE.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗