Engineering topics
Publications and source records attributed to Leduc, H. G..
The development of SIS tunnel junctions based on NbN for mixer applications in the submillimeter range is reported. The unique technological challenges inherent in the development of all refractory-compound superconductor-based tunnel junctions are highlighted. Current deposition and fabrication techniques are discussed, and the current status of all-NbN tunnel junctions is reported.
The deposition of stoichiometric B1-crystal-structure (111) NbN films on glass or sapphire substrates by reactive dc magnetron sputtering is reported. High-purity Ar-N2 mixtures are used in the apparatus described by Thakoor et al. (1985), and typical deposition parameters are given as background pressure about 10 ntorr, voltage -325 V, current 1 A, deposition rate 1.35 nm/s, film thickness 500 nm, P(Ar) 5-17 mtorr, initial P(N2) 2-6 mtorr, and room temperature. The N2 consumption-injection characteristics are studied and found to control NbN formation using well-conditioned Nb targets. Films with transition temperatures 15-16 K are obtained at P(Ar) = 12.9 + or - 0.2 mtorr and P(N2) = 3.7 + or - 0.1 mtorr. SIS junctions of area about 0.001 sq cm fabricated using the NbN films are shown to have I-V characteristics with nonlinearity parameter about 110 and NbN superconducting-gap parameter Delta = about 2.8 meV.
Detector for trace chemicals senses as few as 10 to the 12th power molecules of given material on surface. Contains no moving parts, amenable to large-scale integration, and operates at room temperature. Potential applications in industrial process control and in environmental analysis. Characteristic signals indicate presence of certain chemicals.
The physical mechanisms underlying a novel chemical sensor based on electron tunneling in metal-insulator-metal (MIM) tunnel junctions were studied. Chemical sensors based on electron tunneling were shown to be sensitive to a variety of substances that include iodine, mercury, bismuth, ethylenedibromide, and ethylenedichloride. A sensitivity of 13 parts per billion of iodine dissolved in hexane was demonstrated. The physical mechanisms involved in the chemical sensitivity of these devices were determined to be the chemical alteration of the surface electronic structure of the top metal electrode in the MIM structure. In addition, electroreflectance spectroscopy (ERS) was studied as a complementary surface-sensitive technique. ERS was shown to be sensitive to both iodine and mercury. Electrolyte electroreflectance and solid-state MIM electroreflectance revealed qualitatively the same chemical response. A modified thin-film structure was also studied in which a chemically active layer was introduced at the top Metal-Insulator interface of the MIM devices. Cobalt phthalocyanine was used for the chemically active layer in this study. Devices modified in this way were shown to be sensitive to iodine and nitrogen dioxide. The chemical sensitivity of the modified structure was due to conductance changes in the active layer.
Electronic structure induced by adsorbates at the interface of Al/AlOx/Au tunnel junctions has been observed by elastic electron tunneling spectroscopy. Strong structures appearing in the tunneling spectra above approximately 1 eV after exposure to I, Hg, Bi, and organohalides, have been interpreted in terms of adsorbate-induced surface states. The spectroscopic capabilities of elastic electron tunneling spectroscopy may be useful in the area of chemical detection. In the broader sense, the observation of adsorbate-induced unoccupied electronic states below the vacuum energy, makes elastic electron tunneling spectroscopy a potentially useful technique for the study of surfaces.